Abstract: Rare earths containing complex metal oxides have drawn much attention due to physical, chemical and optical properties which make them feasible in so many areas such as non-linear optical materials and ion exchanger. We have researched a systematic study to obtain rare earth containing zirconium molybdate compound, characterization, investigation of crystal system and calculation of unit cell parameters. After a successful synthesis of Nd2Zr3(MoO4)9 which is a member of rare earth metal containing complex oxides family, X-ray diffraction (XRD), High Score Plus/Rietveld refinement analysis, and Fourier Transform Infrared Spectroscopy (FTIR) were completed to determine the crystal structure. Morphological properties and elemental composition were determined by scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) analysis. Thermal properties were observed via Thermogravimetric-differential thermal analysis (TG/DTA).
Abstract: This article presents summary on preparation and
characterization of zinc, copper, cadmium and cobalt chromite
nanocrystals, embedded in an amorphous silica matrix. The
ZnCr2O4/SiO2, CuCr2O4/SiO2, CdCr2O4/SiO2 and CoCr2O4/SiO2
nanocomposites were prepared by a conventional sol-gel method
under acid catalysis. Final heat treatment of the samples was carried
out at temperatures in the range of 900−1200 ◦C to adjust the
phase composition and the crystallite size, respectively. The resulting
samples were characterized by Powder X-ray diffraction (PXRD),
High Resolution Transmission Electron Microscopy (HRTEM),
Raman/FTIR spectroscopy and magnetic measurements. Formation
of the spinel phase was confirmed in all samples. The average size of
the nanocrystals was determined from the PXRD data and by direct
particle size observation on HRTEM; both results were correlated.
The mean particle size (reviewed by HRTEM) was in the range from
∼4 to 46 nm. The results showed that the sol-gel method can be
effectively used for preparation of the spinel chromite nanoparticles
embedded in the silica matrix and the particle size is driven by the
type of the cation A2+ in the spinel structure and the temperature
of the final heat treatment. Magnetic properties of the nanocrystals
were found to be just moderately modified in comparison to the bulk
phases.
Abstract: High Pressure Raman scattering measurements of KDP:Mn were performed at room temperatures. The X-ray powder diffraction patterns taken at room temperature by Rietveld refinement showed that doped samples of KDP-Mn have the same tetragonal structure of a pure KDP crystal, but with a contraction of the crystalline cell. The behavior of the Raman spectra, in particular the emergence of a new modes at 330 cm-1, indicates that KDP:Mn undergoes a structural phase transition with onset at around 4 GP. First principle density-functional theory (DFT) calculations indicate that tetrahedral rotation with pressure is predominantly around the c crystalline direction. Theoretical results indicates that pressure induced tetrahedral rotations leads to change tetrahedral neighborhood, activating librations/bending modes observed for high pressure phase of KDP:Mn with stronger Raman activity.