Abstract: The cellulose was extracted from pomelo peel and an
etherification reaction used for converting cellulose to carboxymethyl
cellulose (CMC). The pomelo peel was refluxed with 0.5 M HCl and 1
M NaOH solution at 90°C for 1 h and 2 h, respectively. The cellulose
was bleached with calcium hypochlorite and used as precursor. The
precursor was soaked in mixed solution between isopropyl alcohol and
40%w/v NaOH for 12 h. After that, chloroacetic acid was added and
reacted at 55°C for 6 h. The optimum condition was 5 g of cellulose:
0.25 mole of NaOH : 0.07 mole of ClCH2COOH with 78.00% of yield.
Moreover, the product had 0.54 of degree of substitution (DS).
Abstract: The ability of pomelo peel, a natural biosorbent, to remove Cd(II) ions from aqueous solution by biosorption was investigated. The experiments were carried out by batch method at 25 °C. The influence of solution pH, initial cadmium ion concentrations and contact times were evaluated. Cadmium ion removal increased significantly as the pH of the solution increased from pH 1 to pH 5. At pH 5, the cadmium ion removal reached a maximum value. The equilibrium process was described well by the Langmuir isotherm model, with a maximum biosorption capacity of 21.83 mg/g. The biosorption was relatively quick, (approx. 20 min). Biosorption kinetics followed a pseudo-second-order model. The result showed that pomelo peel was effective as a biosorbent for removing cadmium ions from aqueous solution. It is a low cost material that shows potential to be applied in wastewater technology for remediation of heavy metal contamination.