Abstract: Composite materials are one answer to the growing demand for materials with better parameters of construction and exploitation. Composite materials also permit conscious shaping of desirable properties to increase the extent of reach in the case of metals, ceramics or polymers. In recent years, composite materials have been used widely in aerospace, energy, transportation, medicine, etc. Fiber-reinforced composites including carbon fiber, glass fiber and aramid fiber have become a major structural material. The typical defect during manufacture and operation is delamination damage of layered composites. When delamination damage of the composites spreads, it may lead to a composite fracture. One of the many methods used in non-destructive testing of composites is active infrared thermography. In active thermography, it is necessary to deliver energy to the examined sample in order to obtain significant temperature differences indicating the presence of subsurface anomalies. To detect possible defects in composite materials, different methods of thermal stimulation can be applied to the tested material, these include heating lamps, lasers, eddy currents, microwaves or ultrasounds. The use of a suitable source of thermal stimulation on the test material can have a decisive influence on the detection or failure to detect defects. Samples of multilayer structure carbon composites were prepared with deliberately introduced defects for comparative purposes. Very thin defects of different sizes and shapes made of Teflon or copper having a thickness of 0.1 mm were screened. Non-destructive testing was carried out using the following sources of thermal stimulation, heating lamp, flash lamp, ultrasound and eddy currents. The results are reported in the paper.
Abstract: The goal of this paper is to examine the effects of laser
radiation on the skin wound healing using infrared thermography as
non-invasive method for the monitoring of the skin temperature
changes during laser treatment. Thirty Wistar rats were used in this
study. A skin lesion was performed at the leg on all rats. The animals
were exposed to laser radiation (λ = 670 nm, P = 15 mW, DP = 16.31
mW/cm2) for 600 s. Thermal images of wound were acquired before
and after laser irradiation. The results have demonstrated that the
tissue temperature decreases from 35.5±0.50°C in the first treatment
day to 31.3±0.42°C after the third treatment day. This value is close
to the normal value of the skin temperature and indicates the end of
the skin repair process. In conclusion, the improvements in the
wound healing following exposure to laser radiation have been
revealed by infrared thermography.
Abstract: Constant amplitude fatigue crack growth (FCG) tests
were performed on dissimilar metal welded plates of Type 316L
Stainless Steel (SS) and IS 2062 Grade A Carbon steel (CS). The
plates were welded by TIG welding using SS E309 as electrode. FCG
tests were carried on the Side Edge Notch Tension (SENT)
specimens of 5 mm thickness, with crack initiator (notch) at base
metal region (BM), weld metal region (WM) and heat affected zones
(HAZ). The tests were performed at a test frequency of 10 Hz and at
load ratios (R) of 0.1 & 0.6. FCG rate was found to increase with
stress ratio for weld metals and base metals, where as in case of
HAZ, FCG rates were almost equal at high ΔK. FCG rate of HAZ of
stainless steel was found to be lowest at low and high ΔK. At
intermediate ΔK, WM showed the lowest FCG rate. CS showed
higher crack growth rate at all ΔK. However, the scatter band of data
was found to be narrow. Fracture toughness (Kc) was found to vary
in different locations of weldments. Kc was found lowest for the
weldment and highest for HAZ of stainless steel. A novel method of
characterizing the FCG behavior using an Infrared thermography
(IRT) camera was attempted. By monitoring the temperature rise at
the fast moving crack tip region, the amount of plastic deformation
was estimated.