Abstract: Non-water based fixed abrasive polishing was adopted
to manufacture LBO crystal for nano precision surface quality because
of its deliquescent. Ethyl alcohol was selected as the non-water based
slurry solvent and ethanediamine, lactic acid, hydrogen peroxide was
added in the slurry as a chemical additive, respectively. Effect of
different additives with non-water based slurry on material removal
rate, surface topography, microscopic appearances, and surface
roughness were investigated in fixed abrasive polishing of LBO
crystal. The results show the best surface quality of LBO crystal with
surface roughness Sa 8.2 nm and small damages was obtained by
non-water based slurry with lactic acid. Non-water based fixed
abrasive polishing can achieve nano precision surface quality of LBO
crystal with high material removal.
Abstract: Experimental study on slicing of sapphire with fixed
abrasive diamond wire saw was conducted in this paper. The process
parameters were optimized through orthogonal experiment of three
factors and four levels. The effects of wire speed, feed speed and
tension pressure on the surface roughness were analyzed. Surface
roughness in cutting direction and feed direction were both detected.
The results show that feed speed plays the most significant role on the
surface roughness of sliced sapphire followed by wire speed and
tension pressure. The optimized process parameters are as follows:
wire speed 1.9 m/s, feed speed 0.187 mm/min and tension pressure
0.18 MPa. In the end, the results were verified by analysis of variance.