Abstract: This study shows the effect of carbon towards
molybdenum carbide alloy when exposed to Microwave. This
technique is also known as Microwave Induced Alloying (MIA) for
the preparation of molybdenum carbide. In this study ammonium
heptamolybdate solution and carbon black powder were
heterogeneously mixed and exposed to microwave irradiation for 2
minutes. The effect on amount of carbon towards the produced alloy
on morphological and oxidation states changes during microwave is
presented. In this experiment, it is expected carbon act as a reducing
agent with the ratio 2:7 molybdenum to carbon as the optimum for
the production of molybdenum carbide alloy. All the morphological
transformations and changes in this experiment were followed and
characterized using X-Ray Diffraction and FESEM.
Abstract: Highly ordered TiO2 nanotube (TNT) arrays were
fabricated onto a pre-treated titanium foil by anodic oxidation with a
voltage of 20V in phosphoric acid/sodium fluoride electrolyte. A pretreatment
of titanium foil involved washing with acetone,
isopropanol, ethanol and deionized water. Carbon doped TiO2
nanotubes (C-TNT) was fabricated 'in-situ' with the same method in
the presence of polyvinyl alcohol and urea as carbon sources. The
affects of polyvinyl alcohol concentration and oxidation time on the
composition, morphology and structure of the C-TN were studied by
FE-SEM, EDX and XRD techniques. FESEM images of the
nanotubes showed uniform arrays of C-TNTs. The density and
microstructures of the nanotubes were greatly affected by the content
of PVA. The introduction of the polyvinyl alcohol into the electrolyte
increases the amount of C content inside TiO2 nanotube arrays
uniformly. The influence of carbon content on the photo-current of
C-TNT was investigated and the I-V profiles of the nanotubes were
established. The preliminary results indicated that the 'in-situ'
doping technique produced a superior quality nanotubes compared to
post doping techniques.