Abstract: Cement stabilization has been widely used for
improving the strength and stiffness of soft clayey soils. Cement
treated soil specimens used to investigate the stress-strain behaviour in
the laboratory study are usually cured for 7 days. This paper examines
the effects of curing time on the strength and stress strain behaviour of
cement treated marine clay under triaxial loading condition.
Laboratory-prepared cement treated Singapore marine clay with
different mix proportion S-C-W (soil solid-cement solid-water) and
curing time (7 days to 180 days) was investigated through conducting
unconfined compressive strength test and triaxial test. The results
show that the curing time has a significant effect on the unconfined
compressive strength u q , isotropic compression behaviour and stress
strain behaviour. Although the primary yield loci of the cement treated
soil specimens with the same mix proportion expand with curing time,
they are very narrowly banded and have nearly the same shape after
being normalized by isotropic compression primary stress '
py p . The
isotropic compression primary yield stress '
py p was shown to be
linearly related to unconfined compressive strength u q for specimens
with different curing time and mix proportion. The effect of curing
time on the hardening behaviour will diminish with consolidation
stress higher than isotropic compression primary yield stress but its
damping rate is dependent on the cement content.
Abstract: The development of shape and size of a crack in a
pressure vessel under uniaxial and biaxial loadings is important in
fitness-for-service evaluations such as leak-before-break. In this
work finite element modelling was used to evaluate the mean stress
and the J-integral around a front of a surface-breaking crack. A
procedure on the basis of ductile tearing resistance curves of high and
low constrained fracture mechanics geometries was developed to
estimate the amount of ductile crack extension for surface-breaking
cracks and to show the evolution of the initial crack shape. The
results showed non-uniform constraint levels and crack driving forces
around the crack front at large deformation levels. It was also shown
that initially semi-elliptical surface cracks under biaxial load
developed higher constraint levels around the crack front than in
uniaxial tension. However similar crack shapes were observed with
more extensions associated with cracks under biaxial loading.
Abstract: Two-dimensional finite element model was created in this work to investigate the stresses distribution within rock-like samples with offset open non-persistent joints under biaxial loading. The results of this study have explained the fracture mechanisms observed in tests on rock-like material with open non-persistent offset joints [1]. Finite element code SAP2000 was used to study the stresses distribution within the specimens. Four-nodded isoperimetric plain strain element with two degree of freedom per node, and the three-nodded constant strain triangular element with two degree of freedom per node were used in the present study.The results of the present study explained the formation of wing cracks at the tip of the joints for low confining stress as well as the formation of wing cracks at the middle of the joint for the higher confining stress. High shear stresses found in the numerical study at the tip of the joints explained the formation of secondary cracks at the tip of the joints in the experimental study. The study results coincide with the experimental observations which showed that for bridge inclination of 0o, the coalescence occurred due to shear failure and for bridge inclination of 90o the coalescence occurred due to tensile failure while for the other bridge inclinations coalescence occurred due to mixed tensile and shear failure.