Abstract: This investigation examines the effect of the sintering
temperature curve in manufactured nickel powder capillary structure
(wick) for a loop heat pipe (LHP). The sintering temperature curve is
composed of a region of increasing temperature; a region of constant
temperature and a region of declining temperature. The most important
region is that in which the temperature increases, as an index in the
stage in which the temperature increases. The wick of nickel powder is
manufactured in the stage of fixed sintering temperature and the time
between the stage of constant temperature and the stage of falling
temperature. When the slope of the curve in the region of increasing
temperature is unity (equivalent to 10 °C/min), the structure of the
wick is complete and the heat transfer performance is optimal. The
result of experiment test demonstrates that the heat transfer
performance is optimal at 320W; the minimal total thermal resistance
is approximately 0.18°C/W, and the heat flux is 17W/cm2; the internal
parameters of the wick are an effective pore radius of 3.1 μm, a
permeability of 3.25×10-13m2 and a porosity of 71%.