Abstract: The principal purpose of this paper is to find the influence of maximum fatigue load on the probabilistic aspect of fatigue crack propagation life at a specified grown crack in magnesium alloys. The experiments of fatigue crack propagation are carried out in laboratory air under different conditions of the maximum fatigue loads to obtain the fatigue crack propagation data for the statistical analysis. In order to analyze the probabilistic aspect of fatigue crack propagation life, the goodness-of fit test for probability distribution of the fatigue crack propagation life at a specified grown crack is implemented through Anderson-Darling test. The good probability distribution of the fatigue crack propagation life is also verified under the conditions of the maximum fatigue loads.
Abstract: It is necessary to predict a fatigue crack propagation
life for estimation of structural integrity. Because of an uncertainty
and a randomness of a structural behavior, it is also required to
analyze stochastic characteristics of the fatigue crack propagation life
at a specified fatigue crack size. The essential purpose of this study is to find the effect of load ratio
on probability distribution of the fatigue crack propagation life at a
specified grown crack size and to confirm the good probability
distribution in magnesium alloys under various fatigue load ratio
conditions. To investigate a stochastic crack growth behavior, fatigue
crack propagation experiments are performed in laboratory air under
several conditions of fatigue load ratio using AZ31. By Anderson-Darling test, a goodness-of-fit test for probability
distribution of the fatigue crack propagation life is performed. The
effect of load ratio on variability of fatigue crack propagation life is
also investigated.
Abstract: The fatigue crack growth is stochastic because of the fatigue behavior having an uncertainty and a randomness. Therefore, it is necessary to determine the probability distribution of a grown crack size at a specific fatigue crack propagation life for maintenance of structure as well as reliability estimation. The essential purpose of this study is to present the good probability distribution fit for the grown crack size at a specified fatigue life in a rolled magnesium alloy under different specimen thickness conditions. Fatigue crack propagation experiments are carried out in laboratory air under three conditions of specimen thickness using AZ31 to investigate a stochastic crack growth behavior. The goodness-of-fit test for probability distribution of a grown crack size under different specimen thickness conditions is performed by Anderson-Darling test. The effect of a specimen thickness on variability of a grown crack size is also investigated.