Abstract: The three-dimensional incompressible flow past a
rectangular open cavity is investigated, where the aspect ratio of the
cavity is considered as 4. The principle objective is to use large-eddy
simulation to resolve and control the large-scale structures, which are
largely responsible for flow oscillations in a cavity. The flow past an
open cavity is very common in aerospace applications and can be a
cause of acoustic source due to hydrodynamic instability of the shear
layer and its interactions with the downstream edge. The unsteady
Navier-stokes equations have been solved on a staggered mesh using
a symmetry-preserving central difference scheme. Synthetic jet has
been used as an active control to suppress the cavity oscillations in
wake mode for a Reynolds number of ReD = 3360. The effect of
synthetic jet has been studied by varying the jet amplitude and
frequency, which is placed at the upstream wall of the cavity. The
study indicates that there exits a frequency band, which is larger than
a critical value, is effective in attenuating cavity oscillations when
blowing ratio is more than 1.0.
Abstract: The present paper reports results of an experimental
program conducted to study performance of fly ash based
geopolymer pastes at elevated temperature. Three series of
geopolymer pastes differing in Na2O content (8.5%, 10% and 11.5%)
were manufactured by activating low calcium fly ash with a mixture
of sodium hydroxide and sodium silicate solution. The paste
specimens were subjected to temperatures as high as 900oC and the
behaviour at elevated temperatures were investigated on the basis of
physical appearance, weight losses, residual strength, shrinkage
measurements and sorptivity tests at different temperatures. Scanning
electron microscopy along with EDX and XRD tests were also
conducted to examine microstructure and mineralogical changes
during the thermal exposure. Specimens which were initially grey
turned reddish accompanied by appearance of small cracks as the
temperature increased to 900oC. Loss of weight was more in
specimens manufactured with highest Na2O content. Geopolymer
paste specimen containing minimum Na2O performed better than
those with higher Na2O content in terms of residual compressive
strength.