Abstract: Excessive fretting wear at the taper-trunnion junction
(trunnionosis) apparently contributes to the high failure rates of hip
implants. Implant wear and corrosion lead to the release of metal
particulate debris and subsequent release of metal ions at the tapertrunnion
surface. This results in a type of metal poisoning referred to
as metallosis. The consequences of metal poisoning include;
osteolysis (bone loss), osteoarthritis (pain), aseptic loosening of the
prosthesis and revision surgery. Follow up after revision surgery,
metal debris particles are commonly found in numerous locations. Background: A stable connection between the femoral ball head
(taper) and stem (trunnion) is necessary to prevent relative motions
and corrosion at the taper junction. Hence, the importance of
component assembly cannot be over-emphasized. Therefore, the aim
of this study is to determine the influence of head-stem junction
assembly by press fitting and the subsequent
disengagement/disassembly on the connection strength between the
taper ball head and stem. Methods: CoCr femoral heads were assembled with High stainless
hydrogen steel stem (trunnion) by Push-in i.e. press fit; and
disengaged by pull-out test. The strength and stability of the two
connections were evaluated by measuring the head pull-out forces
according to ISO 7206-10 standards. Findings: The head-stem junction strength linearly increases with
assembly forces.