Abstract: The effect of dry milling on the carbothermic
reduction of celestite was investigated. Mixtures of celestite
concentrate (98% SrSO4) and activated carbon (99% carbon) was
milled for 1 and 24 hours in a planetary ball mill. Un-milled and
milled mixtures and their products after carbothermic reduction were
studied by a combination of XRD and TGA/DTA experiments. The
thermogravimetric analyses and XRD results showed that by milling
celestite-carbon mixtures for one hour, the formation temperature of
strontium sulfide decreased from about 720°C (in un-milled sample)
to about 600°C, after 24 hours milling it decreased to 530°C. It was
concluded that milling induces increasingly thorough mixing of the
reactants to reduction occurring at lower temperatures