Abstract: This study examined the structural reliability of the Nigerian grown Opepe timber as bridge beam material. The strength of a particular specie of timber depends so much on some factors such as soil and environment in which it is grown. The steps involved are collection of the Opepe timber samples, seasoning/preparation of the test specimens, determination of the strength properties/statistical analysis, development of a computer programme in FORTRAN language and finally structural reliability analysis using FORM 5 software. The result revealed that the Nigerian grown Opepe is a reliable and durable structural bridge beam material for span of 5000mm, depth of 400mm, breadth of 250mm and end bearing length of 150mm. The probabilities of failure in bending parallel to the grain, compression perpendicular to the grain, shear parallel to the grain and deflection are 1.61 x 10-7, 1.43 x 10-8, 1.93 x 10-4 and 1.51 x 10-15 respectively. The paper recommends establishment of Opepe plantation in various Local Government Areas in Nigeria for structural applications such as in bridges, railway sleepers, generation of income to the nation as well as creating employment for the numerous unemployed youths.
Abstract: The properties of hollow sandcrete blocks produced in
Minna, Nigeria are presented. Sandcrete block is made of cement,
water and sand binded together in certain mix proportions. For the
purpose of this work, fifty (50) commercial sandcrete block industries
were visited in Minna, Nigeria to obtain block samples and
aggregates used for the manufacture, and to take inventory of the mix
composition and the production process. Sieve analysis tests were
conduction on the soil sample from various block industries to
ascertain their quality to be used for block making. The mix ratios
were also investigated. Five (5) nine inches (9’’ or 225mm) blocks
were obtained from each block industry and tested for dimensional
compliance and compressive strength. The results of the soil test
shows that the grading fall within the limit for natural aggregate and
can easily are used to obtain workable mix. Physical examinations of
the block sizes show slight deviation from the standard requirement
in NIS 87:2000. Compressive strength of hollow sandcrete blocks in
range of 0.12 N/mm2 to 0.54 N/mm2 was obtained which is below the
recommendable value of 3.45 N/mm2 for load bearing hollow
sandcrete blocks. This indicates that these blocks are below the
standard for load-bearing sandcrete blocks and cannot be used as load
bearing walling units. The mix composition also indicated low
cement content resulting in low compressive strength. Most of the
commercial block industries visited does not take curing very serious.
Water were only sprinkled ones or twice before the blocks were
stacked and made readily available for sale. It is recommended that a
mix ratio of 1:4 to 1:6 should be used for the production of sandcrete
blocks and proper curing practice should be adhered. Blocks should
also be cured for 14 days before making them available for
consumers.