Abstract: There are many kinds of metal borates found not only
in nature but also synthesized in the laboratory such as magnesium
borates. Due to its excellent properties, as remarkable ceramic
materials, they have also application areas in anti-wear and friction
reducing additives as well as electro-conductive treating agents. The
synthesis of magnesium borate powders can be fulfilled simply with
two different methods, hydrothermal and thermal synthesis.
Microwave assisted method, also another way of producing
magnesium borate, can be classified into thermal synthesis because of
using the principles of solid state synthesis. It also contributes
producing particles with small size and high purity in nano-size
material synthesize. In this study the production of magnesium
borates, are aimed using MgCl2.6H2O and H3BO3. The identification
of both starting materials and products were made by the equipments
of, X-Ray Diffraction (XRD) and Fourier Transform Infrared
Spectroscopy (FT-IR). After several synthesis steps magnesium
borates were synthesized and characterized by XRD and FT-IR, as
well.
Abstract: Turkey has 72 % of total world boron reserves on the
basis of B2O3.Borates that is a refined form of boron minerals have a
wide range of applications. Zinc borates can be used as multifunctional
synergistic additives. The most important properties are
low solubility in water and high dehydration temperature. Zinc
borates dehydrate above 290°C and anhydrous zinc borate has
thermal resistance about 400°C. Zinc borates can be synthesized
using several methods such as hydrothermal and solid-state
processes. In this study, the solid-state method was applied between
500 and 800°C using the starting materials of ZnO and H3BO3 with
1:4 mole ratio. The reaction time was determined as 4 hours after
some preliminary experiments. After the synthesis, the crystal
structure and the morphology of the products were examined by XRay
Diffraction (XRD), Fourier Transform Infrared Spectroscopy
(FT-IR) and Raman Spectrometer. As a result the form of ZnB4O7
was synthesized with the highest crystal score at 800°C.
Abstract: Borate minerals have attracted considerable attention in the past years due to their structural chemistry and mechanical properties in several industries. Recently, increasing attention has been paid to the use of; synthetically produced magnesium borates as catalysts reinforcing material for plastics, the conversion of hydrocarbons, electro-conductive treating agent, anti-wear and anti-corrosion materials. Magnesium borates can be synthesized by several methods such as; hydrothermal and solid-state (thermal) processes. In this study the hydrothermal production method was applied at the modest temperature of 80C along with convenient crystal growth. Using MgCl2.6H2O, H3BO3, and NaOH as starting materials, 30, 60, 120, 240 minutes of reaction times were studied. After all, the crystal structure and the morphology of the products were examined by X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR). As a result the forms of Admontite and Mcallisterite minerals were synthesized.
Abstract: Zinc borates can be used as multi-functional
synergistic additives with flame retardant additives in polymers. Zinc
borate is white, non-hygroscopic and powder type product. The most
important properties are low solubility in water and high dehydration
temperature. Zinc borates dehydrate above 290°C and anhydrous zinc
borate has thermal resistance about 400°C. Zinc borates can be
synthesized using several methods such as hydrothermal and solidstate
processes. In this study, the solid-state method was applied at
low temperatures of 600oC and 700oC using the starting materials of
ZnO and H3BO3 with several mole ratios. The reaction time was
determined as 4 hours after some preliminary experiments. After the
synthesis, the crystal structure and the morphology of the products
were examined by X-Ray Diffraction (XRD) and Fourier Transform
Infrared Spectroscopy (FT-IR). As a result the forms of ZnB4O7,
Zn3(BO3)2, ZnB2O4 were synthesized and obtained along with the
unreacted ZnO.
Abstract: Magnesium wastes and scraps, one of the metal wastes, are produced by many industrial activities, all over the world. Their growing size is becoming a future problem for the world. In this study, the use of magnesium wastes as a raw material in the production of the magnesium borate hydrates are aimed. The method used in the experiments is hydrothermal synthesis. The conditions are set to, waste magnesium to B2O3, 1:3 as a molar ratio. Four different reaction times are studied which are 30, 60, 120 and 240 minutes. For the identification analyses X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FT-IR) and Raman spectroscopy techniques are used. As a result at all the reaction times magnesium borate hydrates are synthesized and the most crystalline forms are obtained at a reaction time of 120 minutes. The overall yields of the production are found between the values of 65-80 %.