Abstract: The aim of this study is to evaluate the influence of raw material composition on the microstructure, mechanical and fatigue properties and micromechanisms of failure of nodular cast iron. In order to evaluate the influence of charge composition, the structural analysis, mechanical and fatigue tests and microfractographic analysis were carried out on specimens of ten melts with different charge compositions. The basic charge of individual melts was formed by different ratio of pig iron and steel scrap and by different additive for regulation of chemical composition (silicon carbide or ferrosilicon). The results show differences in mechanical and fatigue properties, which are connected with the microstructure. SiC additive positively influences microstructure. Consequently, mechanical and fatigue properties of nodular cast iron are improved, especially in the melts with higher ratio of steel scrap in the charge.
Abstract: High pressure turbine (HPT) blades of DV – 2 jet
engines are made from Ni – based superalloy. This alloy was
originally manufactured in the Soviet Union and referred as ŽS6K.
For improving alloy’s high temperature resistance are blades coated
with Al – Si diffusion layer. A regular operation temperature of HPT
blades vary from 705°C to 750°C depending on jet engine regime.
An overcrossing working temperature range causes degradation of
the protective coating as well as base material which microstructure
is formed by the gamma matrix and strengthening phase gamma
prime (forming small particles in the microstructure). Diffusion
processes inside the material during exposition of the material to high
temperatures causes mainly coarsening of the gamma prime particles,
thus decreasing its strengthening effect. Degradation of the Al – Si
coating caused its thickness growth. All the microstructure changes
and coating layer thickness growth results in decreasing of the turbine
blade operation lifetime.