Abstract: Freezing and thawing are considered to be one of the major causes of concrete deterioration in the cold regions. This study aimed at assessing the freezing and thawing of concrete within the cover zone by monitoring the formation of ice and melting at different temperatures using electrical measurement technique. A multi-electrode array system was used to obtain the resistivity of ice formation and melting at discrete depths within the cover zone of the concrete. A total number of four concrete specimens (250 mm x 250 mm x 150 mm) made of ordinary Portland cement concrete and ordinary Portland cement replaced by 65% ground granulated blast furnace slag (GGBS) is investigated. Water/binder ratios of 0.35 and 0.65 were produced and ponded with water to ensure full saturation and then subjected to freezing and thawing process in a refrigerator within a temperature range of -30 0C and 20 0C over a period of time 24 hours. The data were collected and analysed. The obtained results show that the addition of GGBS changed the pore structure of the concrete which resulted in the decrease in conductance. It was recommended among others that, the surface of the concrete structure should be protected as this will help to prevent the instantaneous propagation of ice trough the rebar and to avoid corrosion and subsequent damage.
Abstract: In this paper, the effect of grades 32.4 and 42.5
Portland-limestone cements generally used for concrete production in
Nigeria on concrete compressive strength is investigated.
Investigation revealed that the compressive strength of concrete
produced with Portland-limestone cement grade 42.5 is generally
higher than that produced with cement grade 32.5. The percentage
difference between the compressive strengths of the concrete cubes
produced with Portland-limestone cement grades 42.5 and 32.5 is
inversely proportional to the richness of the concrete with the highest
and the least percentage difference associated with the 1:2:4 and
1:1:2 mix ratios respectively. It is recommended that cement grade
42.5 be preferred for construction in Nigeria as this will lead to the
construction of stronger concrete structures, which will reduce the
incidence of failure of building and other concrete structures at no
additional cost since the cost of both cement grades are the same.
Abstract: Due to growing environmental concerns of the cement
industry, alternative cement technologies have become an area of
increasing interest. It is now believed that new binders are
indispensable for enhanced environmental and durability
performance. Self-compacting Geopolymer concrete is an innovative
method and improved way of concreting operation that does not
require vibration for placing it and is produced by complete
elimination of ordinary Portland cement.
This paper documents the assessment of the compressive strength
and workability characteristics of low-calcium fly ash based selfcompacting
geopolymer concrete. The essential workability
properties of the freshly prepared Self-compacting Geopolymer
concrete such as filling ability, passing ability and segregation
resistance were evaluated by using Slump flow, V-funnel, L-box and
J-ring test methods. The fundamental requirements of high
flowability and segregation resistance as specified by guidelines on
Self Compacting Concrete by EFNARC were satisfied. In addition,
compressive strength was determined and the test results are included
here. This paper also reports the effect of extra water, curing time and
curing temperature on the compressive strength of self-compacting
geopolymer concrete. The test results show that extra water in the
concrete mix plays a significant role. Also, longer curing time and
curing the concrete specimens at higher temperatures will result in
higher compressive strength.