Abstract: Adhesively bonded joints are preferred over the
conventional methods of joining such as riveting, welding, bolting
and soldering. Some of the main advantages of adhesive joints
compared to conventional joints are the ability to join dissimilar
materials and damage-sensitive materials, better stress distribution,
weight reduction, fabrication of complicated shapes, excellent
thermal and insulation properties, vibration response and enhanced
damping control, smoother aerodynamic surfaces and an
improvement in corrosion and fatigue resistance. This paper presents
the behavior of adhesively bonded joints subjected to combined
thermal loadings, using the numerical methods. The joint
configuration considers aluminum as central adherend with six
different outer adherends including aluminum, steel, titanium, boronepoxy,
unidirectional graphite-epoxy and cross-ply graphite-epoxy
and epoxy-based adhesives. Free expansion of the joint in x
direction was permitted and stresses in adhesive layer and interfaces
calculated for different adherends.
Abstract: In the present work, a study has been made on the combination of the electrical discharge machining (EDM) with ultrasonic vibrations to improve the machining efficiency. In experiments the graphite used as tool electrode and material of workpiece was AISIH13 tool steel. The parameters such as discharge peak current and pulse duration were changed to explore their effect on the material removal rate (MRR), relative tool wear ratio (TWR) and surface roughness. From the experimental result it can be seen that ultrasonic vibration of the workpiece can significantly reduces the inactive pulses and improves the stability of process. It was found that ultrasonic assisted EDM (US-EDM) is effective in attaining a high material removal rate (MRR) in finishing regime.
Abstract: The presence of heavy metals in the environment
could constitute a hazard to food security and public health. These
can be accumulated in aquatic animals such as fish. Samples of four
popular brands of canned fish in the Iranian market (yellowfin tuna,
common Kilka, Kawakawa and longtail tuna) were analyzed for level
of Cr after wet digestion with acids using graphite furnace atomic
absorption spectrophotometry. The mean concentrations for Cr in the
different brands were: 2.57, 3.24, 3.16 and 1.65 μg/g for brands A, B,
C and D respectively. Significant differences were observed in the Cr
levels between all of the different brands of canned fish evaluated in
this study. The Cr concentrations for the varieties of canned fishes
were generally within the FAO/WHO, U.S. FDA and U.S. EPA
recommended limits for fish.
Abstract: We fabricated multi-walled carbon nanotube (MCNT)
emitters by an electroporetic deposition (EPD) method using a
MCNT-sodium dodecyl sulfate (SDS) suspension. MCNT films were
prepared on graphite tip using EPD. We observe field emission
properties of MCNT film after heat treatment. Consequently, The
MCNT film on graphite tip exhibit good electron emission current.
Abstract: In the first part of the research work, an electrolyzer (10.16 cm dia and 24.13 cm height) to produce hydrogen and oxygen was constructed for single slice O2/H2 fuel cell using cation exchange membrane. The electrolyzer performance was tested with 23% NaOH, 30% NaOH, 30% KOH and 35% KOH electrolyte solution with current input 4 amp and 2.84 V from the rectifier. Rates of volume of hydrogen produced were 0.159 cm3/sec, 0.155 cm3/sec, 0.169 cm3/sec and 0.163 cm3/sec respectively from 23% NaOH, 30% NaOH, 30% KOH and 35% KOH solution. Rates of volume of oxygen produced were 0.212 cm3/sec, 0.201 cm3/sec, 0.227 cm3/sec and 0.219 cm3/sec respectively from 23% NaOH, 30% NaOH, 30% KOH and 35% KOH solution (1.5 L). In spite of being tested the increased concentration of electrolyte solution, the gas rate does not change significantly. Therefore, inexpensive 23% NaOH electrolyte solution was chosen to use as the electrolyte in the electrolyzer. In the second part of the research work, graphite serpentine flow plates, fiberglass end plates, stainless steel screen electrodes, silicone rubbers were made to assemble the single slice O2/H2 polymer electrolyte membrane fuel cell (PEMFC).
Abstract: The peculiarities of the nanoscale structure-phase
states formed after electroexplosive carburizing and subsequent
electron-beam treatment of technically pure titanium surface in different regimes are established by methods of transmission electron
diffraction microscopy and physical mechanisms are discussed. Electroexplosive carburizing leads to surface layer formation
(40 m thickness) with increased (in 3.5 times) microhardness. It consists of β-titanium, graphite (monocrystals 100-150 nm,
polycrystals 5-10 nm, amorphous particles 3-5nm), TiC (5-10 nm), β-Ti02 (2-20nm). After electron-beam treatment additionally increasing the microhardness the surface layer consists of TiC.