Abstract: In this study, fiberless reactive powder concrete (RPC) was produced with high pressure and flexural strength. C30/37 concrete was chosen as the control sample. In this study, 9 different cure types were applied to fiberless RPC. the most suitable combined cure type was selected according to the pressure and flexure strength. Pressure and flexural strength tests were applied to these samples after curing. As a result of the study, the combined cure type with the highest pressure resistance was obtained. The highest pressure resistance was achieved with consecutive standard water cure at 20 °C for 7 days – hot water cure at 90 °C for 2 days - drying oven cure at 180 °C for 2 days. As a result of the study, the highest pressure resistance of fiberless RPC was found as 123 MPa with water cure at 20 °C for 7 days - hot water cure at 90 °C for 2 days - drying oven cure at 180 °C for 2 days; and the highest flexural resistance was found as 8.37 MPa for the same combined cure type.
Abstract: This paper in essence presents comparative
experimental data on the mechanical performance of steel and
synthetic fibre-reinforced concrete under compression, tensile split
and flexure. URW1050 steel fibre and HPP45 synthetic fibre, both
with the same concrete design mix, have been used to make cube
specimens for a compression test, cylinders for a tensile split test and
beam specimens for a flexural test. The experimental data
demonstrated steel fibre reinforced concrete to be stronger in flexure
at early stages, whilst both fibre reinforced concrete types displayed
comparatively the same performance in compression, tensile splitting
and 28-day flexural strength. In terms of post-crack controlHPP45
was preferable.