Abstract: The paper a summary of the results of concretes with
partial substitution of natural aggregates with recycled concrete is
solved. Design formulas of the concretes were characterised with 20,
40 and 60% substitution of natural 8-16mm fraction aggregates with
a selected recycled concrete of analogous coarse fractions. With the
product samples an evaluation of coarse fraction aggregates influence
on fresh concrete consistency and concrete strength in time was
carried out. The results of concretes with aggregates substitution will
be compared to reference formula containing only the fractions of
natural aggregates.
Abstract: The acid attack on cement mortars modified with rubber aggregates and EVA polymer binder was studied. Mortar specimens were prepared using a type CEM I 42.5 Portland cement and siliceous sand, as well as by substituting 25% of sand with shredded used automobile tires, and by adding EVA polymer in two percentages (5% and 10% of cement mass). Some specimens were only air cured, at laboratory conditions, and their compressive strength and water absorption were determined. The rest specimens were stored in acid solutions (HCl, H2SO4, HNO3) after 28 days of initial curing, and stored at laboratory temperature. Compressive strength tests, mass measurements and visual inspection took place for 28 days. Compressive strength and water absorption of the air-cured specimens were significantly decreased when rubber aggregates are used. The addition of EVA polymer further reduced water absorption, while had no important impact on strength. Compressive strength values were affected in a greater extent by hydrochloric acid solution, followed by sulfate and nitric acid solutions. The addition of EVA polymer decreased compressive strength loss for the specimens with rubber aggregates stored in hydrochloric and nitric acid solutions. The specimens without polymer binder showed similar mass loss, which was higher in sulfate acid solution followed by hydrochloric and nitric acid solutions. The use of EVA polymer delayed mass loss, while its content did not affect it significantly.
Abstract: Construction industry in Greece consumes annually
more than 25 million tons of natural aggregates originating mainly
from quarries. At the same time, more than 2 million tons of
construction and demolition waste are deposited every year, usually
without control, therefore increasing the environmental impact of this
sector. A potential alternative for saving natural resources and
minimize landfilling, could be the recycling and re-use of Concrete
and Demolition Waste (CDW) in concrete production. Moreover, in
order to conform to the European legislation, Greece is obliged to
recycle non-hazardous construction and demolition waste to a
minimum of 70% by 2020. In this paper characterization of recycled
materials - commercially and laboratory produced, coarse and fine,
Recycled Concrete Aggregates (RCA) - has been performed. Namely,
X-Ray Fluorescence and X-ray diffraction (XRD) analysis were used
for chemical and mineralogical analysis respectively. Physical
properties such as particle density, water absorption, sand equivalent
and resistance to fragmentation were also determined. This study,
first time made in Greece, aims at outlining the differences between
RCA and natural aggregates and evaluating their possible influence
in concrete performance. Results indicate that RCA’s chemical
composition is enriched in Si, Al, and alkali oxides compared to
natural aggregates. X-ray diffraction (XRD) analyses results
indicated the presence of calcite, quartz and minor peaks of mica and
feldspars. From all the evaluated physical properties of coarse RCA,
only water absorption and resistance to fragmentation seem to have a
direct influence on the properties of concrete. Low Sand Equivalent
and significantly high water absorption values indicate that fine
fractions of RCA cannot be used for concrete production unless
further processed. Chemical properties of RCA in terms of water
soluble ions are similar to those of natural aggregates. Four different
concrete mixtures were produced and examined, replacing natural
coarse aggregates with RCA by a ratio of 0%, 25%, 50% and 75%
respectively. Results indicate that concrete mixtures containing
recycled concrete aggregates have a minor deterioration of their
properties (3-9% lower compression strength at 28 days) compared to
conventional concrete containing the same cement quantity.
Abstract: In this study two series of self compacting concrete
mixtures were prepared with 100% coarse recycled concrete
aggregates and different percentages of 0%, 20%, 40%, 60%, 80%
and 100% fine recycled concrete aggregates. In series I and II the
water to binder ratios were 0.50 and 0.45, respectively. The cement
content was kept 350
3 m
kg for those mixtures that don't have any
Nano-Silica. To improve the compressive strength of samples, Nano-
Silica replaced with 10% of cement weight in concrete mixtures. By
doing the tests, the results showed that, adding Nano-silica to the
samples with less percentage of fine recycled concrete aggregates,
lead to more increase on the compressive strength.
Abstract: Basic ingredients of concrete are cement, fine aggregate, coarse aggregate and water. To produce a concrete of certain specific properties, optimum proportion of these ingredients are mixed. The important factors which govern the mix design are grade of concrete, type of cement and size, shape and grading of aggregates. Concrete mix design method is based on experimentally evolved empirical relationship between the factors in the choice of mix design. Basic draw backs of this method are that it does not produce desired strength, calculations are cumbersome and a number of tables are to be referred for arriving at trial mix proportion moreover, the variation in attainment of desired strength is uncertain below the target strength and may even fail. To solve this problem, a lot of cubes of standard grades were prepared and attained 28 days strength determined for different combination of cement, fine aggregate, coarse aggregate and water. An artificial neural network (ANN) was prepared using these data. The input of ANN were grade of concrete, type of cement, size, shape and grading of aggregates and output were proportions of various ingredients. With the help of these inputs and outputs, ANN was trained using feed forward back proportion model. Finally trained ANN was validated, it was seen that it gave the result with/ error of maximum 4 to 5%. Hence, specific type of concrete can be prepared from given material properties and proportions of these materials can be quickly evaluated using the proposed ANN.
Abstract: This paper tries to study the effect of geosynthetic inclusion on the improvement of the load-settlement characters of two layered soil. In addition, the effect of geogrid and geotextile in reduction of the required thickness of subbase layer in unpaved roads is studied. Considering the vast application of bearing ratio tests in road construction projects, this test is used in present investigation. Bearing ratio tests were performed on two layered soil including a granular soil layer at the top (as the subbase layer) and a weak clayey soil placed at the bottom (as the subgrade layer). These tests were performed for different conditions including unreinforced and reinforced by geogrid and geotextile and three thicknesses for top layer soil (subbase layer). In the reinforced condition the reinforcing element was placed on the interface of the top granular layer and the beneath clayey layer to study the separation effect of geosynthetics. In all tests the soils (both granular and clayey soil layers) were compacted according to optimum water content. At the end, the diagrams were plotted and were compared with each other. Furthermore, a comparison between geogrids and geotextiles behaviors on two layer soil is done in this paper. The results show an increase in compression strength of reinforced specimen in comparison with unreinforced soil sample. The effect of geosynthetic inclusion reduces by increasing the subbase thickness. In addition it was found that geogrids have more desirable behavior rather than geotextiles due to interlocking with the subbase layer aggregates.
Abstract: The mechanical properties of granular solids are
dependent on the flow of stresses from one particle to another
through inter-particle contact. Although some experimental methods
have been used to study the inter-particle contacts in the past,
preliminary work with these techniques indicated that they do not
have the necessary resolution to distinguish between those contacts
that transmit the load and those that do not, especially for systems
with a wide distribution of particle sizes. In this research, computer
simulations are used to study the nature and distribution of contacts
in a compact with wide particle size distribution, representative of
aggregate size distribution used in asphalt pavement construction.
The packing fraction, the mean number of contacts and the
distribution of contacts were studied for different scenarios. A
methodology to distinguish and compute the fraction of load-bearing
particles and the fraction of space-filling particles (particles that do
not transmit any force) is needed for further investigation.