Abstract: Reinforced concrete has good durability and excellent structural performance. But there are cases of early deterioration due to a number of factors, one prominent factor being corrosion of steel reinforcement. The process of corrosion sets in due to ingress of moisture, oxygen and other ingredients into the body of concrete, which is unsound, permeable and absorbent. Cracks due to structural and other causes such as creep, shrinkage, etc also allow ingress of moisture and other harmful ingredients and thus accelerate the rate of corrosion. There are several interactive factors both external and internal, which lead to corrosion of reinforcement and ultimately failure of structures. Suitable addition of mineral admixture like silica fume (SF) in concrete improves the strength and durability of concrete due to considerable improvement in the microstructure of concrete composites, especially at the transition zone. Secondary reinforcement in the form of fibre is added to concrete, which provides three dimensional random reinforcement in the entire mass of concrete. Reinforced concrete beams of size 0.1 m X 0.15 m and length 1m have been cast using M 35 grade of concrete. The beams after curing process were subjected to corrosion process by impressing an external Direct Current (Galvanostatic Method) for a period of 15 days under stressed and unstressed conditions. The corroded beams were tested by applying two point loads to determine the ultimate load carrying capacity and cracking pattern and the results of specimens were compared with that of the companion specimens. Gravimetric method is used to quantify corrosion that has occurred.
Abstract: Repairing of the cracks by fiber metal laminates
(FMLs) was first done by some aeronautical laboratories in early
1970s. In this study, experimental investigations were done on the
effect of repairing the center-cracked aluminum plates using the FML
patches. The repairing processes were conducted to characterize the
response of the repaired structures to tensile tests. The composite
patches were made of one aluminum layer and two woven glassepoxy
composite layers. Three different crack lengths in three crack
angles and different patch lay-ups were examined. It was observed
for the lengthen cracks, the effect of increasing the crack angle on
ultimate tensile load in the structure was increase. It was indicated
that the situation of metal layer in the FML patches had an important
effect on the tensile response of the tested specimens. It was found
when the aluminum layer is farther, the ultimate tensile load has the
highest amount.
Abstract: Analytical procedure was carried out in this paper to
calculate the ultimate load capacity of reinforced concrete corbels
strengthened or repaired externally with CFRP sheets. Strut and tie
method and shear friction method proposed earlier for analyzing
reinforced concrete corbels were modified to incorporate the effect of
external CFRP sheets bonded to the corbel. The points of weakness
of any method that lead to an inaccuracy, especially when
overestimating test results were checked and discussed. Comparison
of prediction with the test data indicates that the ratio of test /
calculated ultimate load is 0.82 and 1.17 using strut and tie method
and shear friction method, respectively. If the limits of maximum
shear stress is followed, the calculated ultimate load capacity using
shear friction method was found to underestimates test data
considerably.
Abstract: When the foundations of structures under cyclic
loading with amplitudes less than their permissible load, the concern exists often for the amount of uniform and non-uniform settlement of
such structures. Storage tank foundations with numerous filling and discharging and railways ballast course under repeating
transportation loads are examples of such conditions. This paper
deals with the effects of using the new generation of reinforcements,
Grid-Anchor, for the purpose of reducing the permanent settlement
of these foundations under the influence of different proportions of
the ultimate load. Other items such as the type and the number of
reinforcements as well as the number of loading cycles are studied numerically. Numerical models were made using the Plaxis3D
Tunnel finite element code. The results show that by using gridanchor
and increasing the number of their layers in the same
proportion as that of the cyclic load being applied, the amount of
permanent settlement decreases up to 42% relative to unreinforced
condition depends on the number of reinforcement layers and percent
of applied load and the number of loading cycles to reach a constant
value of dimensionless settlement decreases up to 20% relative to
unreinforced condition.