Abstract: Ceramic Waste Aggregates (CWAs) were made from
electric porcelain insulator wastes supplied from an electric power
company, which were crushed and ground to fine aggregate sizes. In
this study, to develop the CWA mortar as an eco–efficient, ground
granulated blast–furnace slag (GGBS) as a Supplementary
Cementitious Material (SCM) was incorporated. The water–to–binder
ratio (W/B) of the CWA mortars was varied at 0.4, 0.5, and 0.6. The
cement of the CWA mortar was replaced by GGBS at 20 and 40% by
volume (at about 18 and 37% by weight). Mechanical properties of
compressive and splitting tensile strengths, and elastic modulus were
evaluated at the age of 7, 28, and 91 days. Moreover, the chloride
ingress test was carried out on the CWA mortars in a 5.0% NaCl
solution for 48 weeks. The chloride diffusion was assessed by using an
electron probe microanalysis (EPMA). To consider the relation of the
apparent chloride diffusion coefficient and the pore size, the pore size
distribution test was also performed using a mercury intrusion
porosimetry at the same time with the EPMA. The compressive
strength of the CWA mortars with the GGBS was higher than that
without the GGBS at the age of 28 and 91 days. The resistance to the
chloride ingress of the CWA mortar was effective in proportion to the
GGBS replacement level.
Abstract: Deoxygenation of beef fat for the production of hydrogenated biodiesel is investigated in a high pressure continuous flow fixed bed reactor over palladium-supported mesoporous titania catalyst synthesized via a combined single-step sol-gel process with surfactant-assisted templating method (SATM). The catalyst possessed a mesoporous charactheristic with high surface area and narrow pore size distribution. The main products of all Pd/TiO2 catalysts are n-heptadecane (n-C17) and n-pentadecane (n-C15) resulting from decarbonylation reaction. Pd/TiO2 catalyst synthesized via a combined single-step sol-gel process with SATM (SSSG) gave higher activity and selectivity to the desired products when compared to IWI/SG-TiO2 and IWI/P25-TiO2, respectively. SSSG catalyst gave the average conversion up to 80-90 % and 80 % for the selectivity in diesel range hydrocarbons. This result may cause by the higher surface area and the ability in dispersion of palladium ion in mesoporous of TiO2 during sol-gel process.