Abstract: This paper investigates the effectiveness of two
natural zeolites in reducing expansion of concrete due to alkali-silica
reaction. These natural zeolites have different reactive silica content.
Three aggregates; two natural sands and one crushed stone aggregate
were used while preparing mortar bars in accordance with accelerated
mortar bar test method, ASTM C1260. Performances of natural
zeolites are compared by examining the expansions due to alkali
silica reaction. Natural zeolites added to the mixtures at 10% and
20% replacement levels by weight of cement. Natural zeolite with
high reactive silica content had better performance on reducing
expansions due to ASR. In this research, using high reactive zeolite at
20% replacement levels was effective in mitigating expansions.
Abstract: Oilsands bitumen is an extremely important source of
energy for North America. However, due to the presence of large
molecules such as asphaltenes, the density and viscosity of the
bitumen recovered from these sands are much higher than those of
conventional crude oil. As a result the extracted bitumen has to be
diluted with expensive solvents, or thermochemically upgraded in
large, capital-intensive conventional upgrading facilities prior to
pipeline transport. This study demonstrates that globally abundant
natural zeolites such as clinoptilolite from Saint Clouds, New Mexico
and Ca-chabazite from Bowie, Arizona can be used as very effective
reagents for cracking and visbreaking of oilsands bitumen. Natural
zeolite cracked oilsands bitumen products are highly recoverable (up
to ~ 83%) using light hydrocarbons such as pentane, which indicates
substantial conversion of heavier fractions to lighter components.
The resultant liquid products are much less viscous, and have lighter
product distribution compared to those produced from pure thermal
treatment. These natural minerals impart similar effect on industrially
extracted Athabasca bitumen.
Abstract: Mechanical and water transport properties of high
performance concrete (HPC) containing natural zeolite as partial
replacement of Portland cement are studied. Experimental results
show that in the investigated mixes the use of natural zeolite leads to
an increase of porosity, decrease of compressive strength and
increase of moisture diffusivity and water vapor diffusion coefficient,
as compared with the reference HPC. However, for the replacement
level up to 20% of the mass of Portland cement the concretes still
maintain their high performance character and exhibit acceptable
water transport properties. Therefore, natural zeolite can be
considered an environmental friendly binder with a potential to
replace a part of Portland cement in concrete in building industry.
Abstract: For more than 120 years, gold mining formed the
backbone the South Africa-s economy. The consequence of mine
closure was observed in large-scale land degradation and widespread
pollution of surface water and groundwater. This paper investigates
the feasibility of using natural zeolite in removing heavy metals
contaminating the Wonderfonteinspruit Catchment Area (WCA), a
water stream with high levels of heavy metals and radionuclide
pollution. Batch experiments were conducted to study the adsorption
behavior of natural zeolite with respect to Fe2+, Mn2+, Ni2+, and Zn2+.
The data was analysed using the Langmuir and Freudlich isotherms.
Langmuir was found to correlate the adsorption of Fe2+, Mn2+, Ni2+,
and Zn2+ better, with the adsorption capacity of 11.9 mg/g, 1.2 mg/g,
1.3 mg/g, and 14.7 mg/g, respectively. Two kinetic models namely,
pseudo-first order and pseudo second order were also tested to fit the
data. Pseudo-second order equation was found to be the best fit for
the adsorption of heavy metals by natural zeolite. Zeolite
functionalization with humic acid increased its uptake ability.