Abstract: Inelastic deformation of the brace in Special Concentrically Braced Frame (SCBF) creates inelastic damages on gusset plate connections such as buckling at edges. In this study, to improve the seismic performance of SCBFs connections, an analytical study was undertaken. To improve the gusset plate connection, this study proposes using edge’s stiffeners in both sides of gusset plate. For this purpose, in order to examine edge’s stiffeners effect on gusset plate connections, two groups of modeling with and without considering edge’s stiffener and different types of braces were modeled using ABAQUS software. The results show that considering the edge’s stiffener reduces the equivalent plastic strain values at a connection region of gusset plate with beam and column, which can improve the seismic performance of gusset plate. Furthermore, considering the edge’s stiffeners significantly decreases the strain concentration at regions where gusset plates have been connected to beam and column. Moreover, considering 2tpl distance causes reduction in the plastic strain.
Abstract: Inelastic deformation of the brace in Special Concentrically Braced Frame (SCBF) creates inelastic damages on gusset plate connections such as buckling at edges. In this study, to improve the seismic performance of SCBFs connections, an analytical study was undertaken. Using edge’s stiffeners is one of the main solutions of this study to improve the gusset plate connections' behavior. For this purpose, in order to examine edge’s stiffeners effect on gusset plate connections, two groups of modeling with and without considering edge’s stiffener and different types of braces were modeled using ABAQUS software. The results show that considering the edge’s stiffener reduces the equivalent plastic strain values at a connection region of gusset plate with beam and column, which can improve the seismic performance of gusset plate. Furthermore, considering the edge’s stiffeners significantly decreases the strain concentration at regions where gusset plates have been connected to beam and column. Moreover, considering 2tpl distance causes reduction in the plastic strain.
Abstract: Induction assisted single point incremental forming
(IASPIF) is a flexible method and can be simply utilized to
form a high strength alloys. Due to the interaction between the
mechanical and thermal properties during IASPIF an evaluation for
the process is necessary to be performed analytically. Therefore, a
numerical simulation was carried out in this paper. The numerical
analysis was operated at both room and elevated temperatures
then compared with experimental results. Fully coupled dynamic
temperature displacement explicit analysis was used to simulated the
hot single point incremental forming. The numerical analysis was
indicating that during hot single point incremental forming were a
combination between complicated compression, tension and shear
stresses. As a result, the equivalent plastic strain was increased
excessively by rising both the formed part depth and the heating
temperature during forming. Whereas, the forming forces were
decreased from 5 kN at room temperature to 0.95 kN at elevated
temperature. The simulation shows that the maximum true strain was
occurred in the stretching zone which was the same as in experiment.
Abstract: In present work, prediction the effect of nose radius, rz (mm) on the equivalent strain (PEEQ) and surface finish during the machining of titanium alloy (Ti-6Al-4V) through orthogonal cutting process. The results were performed at several of the nose radiuses, rz (mm) while the cutting speed, vc (m/min), feed rate, f (mm/tooth) and depth of cut, d (mm) were remained constant. The equivalent plastic strain (PEEQ) was estimated by using finite element modeling (FEM) and applied through ABAQUS/EXPLICIT software. The simulation results led to conclude that the equivalent plastic strain (PEEQ) was increased and surface roughness (Ra) decreased when increasing nose radius, rz (mm) during the machining of titanium alloy (Ti–6Al–4V) in dry cutting conditions.
Abstract: The sand production problem has led researchers into making various attempts to understand the phenomenon. The generally accepted concept is that the occurrence of sanding is due to the in-situ stress conditions and the induced changes in stress that results in the failure of the reservoir sandstone during hydrocarbon production from wellbores. By using a hypothetical cased (perforated) well, an approach to the problem is presented here by using Finite Element numerical modelling techniques. In addition to the examination of the erosion problem, the influence of certain key parameters is studied in order to ascertain their effect on the failure and subsequent erosion process. The major variables investigated include: drawdown, perforation depth, and the erosion criterion. Also included is the determination of the optimal mud pressure for given operational and reservoir conditions. The improved understanding between parameters enables the choice of optimal values to minimize sanding during oil production.
Abstract: Aluminum alloy sheets have several advantages such
as the lightweight, high-specific strength and recycling efficiency.
Therefore, aluminum alloy sheets in sheet forming have been used in various areas as automotive components and so forth. During the
process of sheet forming, wrinkling which is caused by compression stress might occur and the formability of sheets was affected by
occurrence of wrinkling. A few studies of uniaxial compressive test by
using square tubes, pipes and sheets were carried out to clarify the each wrinkling behavior. However, on uniaxial compressive test,
deformation behavior of the sheets hasn-t be cleared. Then, it is necessary to clarify the relationship between the buckling behavior
and the forming conditions. In this study, the effect of dimension of the sheet in the buckling behavior on compression test of aluminum alloy sheet was cleared by experiment and FEA. As the results, the buckling
deformation was classified by three modes in terms of the distribution of equivalent plastic strain.