Abstract: In this paper, the absorption and fluorescence
emission spectra of Yb:Y3Al5O12 (YAG)(25 at%) crystal as a disk
laser medium are measured at high temperature (300-450K). The
absorption and emission cross sections of Yb:YAG crystal are
determined using Reciprocity method. Temperature dependence of
941nm absorption cross section and 1031nm emission cross section
is extracted in the range of 300-450K. According to our experimental
results, an exponential temperature dependence between 300K and
450K is acquired for the 1031nm peak emission cross section and
also for 941nm peak absorption cross section of Yb:YAG crystal.
These results could be used for simulation and design of high power
highly doped Yb:YAG thin disk lasers.
Abstract: Series of tellurite glass of the system 78TeO2-10PbO-
10Li2O-(2-x)Nd2O3-xEr2O3, where x = 0.5, 1.0, 1.5 and 2.0 was
successfully been made. A study of upconversion luminescence of
the Nd3+/Er3+ co-doped tellurite glass has been carried out. From
Judd-Ofelt analysis, the experimental lifetime, exp. τ of the glass
serie are found higher in the visible region as they varies from
65.17ms to 114.63ms, whereas in the near infrared region (NIR) the
lifetime are varies from 2.133ms to 2.270ms. Meanwhile, the
emission cross section,σ results are found varies from 0.004 x 1020
cm2 to 1.007 x 1020 cm2 with respect to composition. The emission
spectra of the glass are found been contributed from Nd3+ and Er3+
ions by which nine significant transition peaks are observed. The
upconversion mechanism of the co-doped tellurite glass has been
shown in the schematic energy diagrams. In this works, it is found
that the excited state-absorption (ESA) is still dominant in the
upconversion excitation process as the upconversion excitation
mechanism of the Nd3+ excited-state levels is accomplished through a
stepwise multiphonon process. An efficient excitation energy transfer
(ET) has been observed between Nd3+ as a donor and Er3+ as the
acceptor. As a result, respective emission spectra had been observed.