Abstract: This study investigates the use of centrifugal casting method to fabricate functionally graded aluminium A356 Alloy and A356-10%SiCp composite for hydro turbine bucket application. The study includes the design and fabrication of a permanent mould. The mould was put into use and the buckets of A356 Alloy and A356-10%SiCp composite were cast, cut and machined into specimens. Some specimens were given T6 heat treatment and the specimens were prepared for different examinations accordingly. The SiCp particles were found to be more at inner periphery of the bucket. The maximum hardness of As-Cast A356 and A356-10%SiCp composite was recorded at the inner periphery to be 60 BRN and 95BRN, respectively. And these values were appreciated to 98BRN and 122BRN for A356 alloy and A356-10%SiCp composite, respectively. It was observed that the ultimate tensile stress and yield tensile stress prediction curves show the same trend.
Abstract: In the present work, a comparative study on the
microstructure and mechanical properties of as cast, cast aged and
forged aged A356 alloy has been investigated. The study reveals that
mechanical properties of A356 alloy are highly influenced by melt
treatment and solid state processing. Cast aged alloys achieve highest
strength and hardness compared to as cast and forge aged ones. Ones
treated with combined addition of grain refiners and modifiers
achieve maximum strength and hardness. Cast aged A356 alloy
possesses higher wear resistance compared to as cast and forge aged
ones. Forging improves both strength and ductility of alloys over as
cast ones. However, the improvement in ductility is perceptible only
for properly grain refined and modified alloys. Ones refined with
0.65% Al-3Ti shows highest improvement in ductility while ones
treated with 0.20% Al-10Sr exhibits less improvement in ductility.