Abstract: This paper reports the tensile fracture location
characterizations of dissimilar friction stir welds between 5754
aluminium alloy and C11000 copper. The welds were produced using
three shoulder diameter tools; namely, 15, 18 and 25 mm by varying
the process parameters. The rotational speeds considered were 600,
950 and 1200 rpm while the feed rates employed were 50, 150 and
300 mm/min to represent the low, medium and high settings
respectively. The tensile fracture locations were evaluated using the
optical microscope to identify the fracture locations and were
characterized. It was observed that 70% of the tensile samples failed
in the Thermo Mechanically Affected Zone (TMAZ) of copper at the
weld joints. Further evaluation of the fracture surfaces of the pulled
tensile samples revealed that welds with low Ultimate Tensile
Strength either have defects or intermetallics present at their joint
interfaces.
Abstract: This paper presents a experiment to estimate the
influences of cutting conditions in microstructure changes of
machining austenitic 304 stainless steel, especially for wear insert. The
wear insert were prefabricated with a width of 0.5 mm. And the forces,
temperature distribution, RS, and microstructure changes were
measured by force dynamometer, infrared thermal camera, X-ray
diffraction, XRD, SEM, respectively. The results told that the different
combinations of machining condition have a significant influence on
machined surface microstructure changes. In addition to that, the
ANOVA and AOMwere used to tell the different influences of cutting
speed, feed rate, and wear insert.
Abstract: The machining of Carbon Fiber Reinforced Plastics
has come to constitute a significant challenge for many fields of
industry. The resulting surface finish of machined parts is of primary
concern for several reasons, including contact quality and impact on
the assembly. Therefore, the characterization and prediction of
roughness based on machining parameters are crucial for costeffective
operations. In this study, a PCD tool comprised of two
straight flutes was used to trim 32-ply carbon fiber laminates in a bid
to analyze the effects of the feed rate and the cutting speed on the
surface roughness. The results show that while the speed has but a
slight impact on the surface finish, the feed rate for its part affects it
strongly. A detailed study was also conducted on the effect of fiber
orientation on surface roughness, for quasi-isotropic laminates used
in aerospace. The resulting roughness profiles for the four-ply
orientation lay-up were compared, and it was found that fiber angle is
a critical parameter relating to surface roughness. One of the four
orientations studied led to very poor surface finishes, and
characteristic roughness profiles were identified and found to only
relate to the ply orientations of multilayer carbon fiber laminates.