Abstract: Performance of a cobalt doped sol-gel derived silica (Co/SiO2) catalyst for Fischer–Tropsch synthesis (FTS) in slurryphase reactor was studied using paraffin wax as initial liquid media. The reactive mixed gas, hydrogen (H2) and carbon monoxide (CO) in a molar ratio of 2:1, was flowed at 50 ml/min. Braunauer-Emmett- Teller (BET) surface area and X-ray diffraction (XRD) techniques were employed to characterize both the specific surface area and crystallinity of the catalyst, respectively. The reduction behavior of Co/SiO2 catalyst was investigated using the Temperature Programmmed Reduction (TPR) method. Operating temperatures were varied from 493 to 533K to find the optimum conditions to maximize liquid fuels production, gasoline and diesel.
Abstract: Characteristics and sonocatalytic activity of zeolite
Y catalysts loaded with TiO2 using impregnation and ion exchange
methods for the degradation of amaranth dye were investigated.
The Ion-exchange method was used to encapsulate the TiO2 into
the internal pores of the zeolite while the incorporation of TiO2
mostly on the external surface of zeolite was carried out using the
impregnation method. Different characterization techniques were
used to elucidate the physicochemical properties of the produced
catalysts. The framework of zeolite Y remained virtually
unchanged after the encapsulation of TiO2 while the crystallinity of
zeolite decreased significantly after the incorporation of 15 wt% of
TiO2. The sonocatalytic activity was enhanced by TiO2
incorporation with maximum degradation efficiencies of 50% and
68% for the encapsulated titanium and titanium loaded onto the
zeolite, respectively after 120min of reaction. Catalysts
characteristics and sonocatalytic behaviors were significantly
affected by the preparation method and the location of TiO2
introduced with zeolite structure. Behaviors in the sonocatalytic
process were successfully correlated with the characteristics of the
catalysts used.