Abstract: Microstructural and electrical properties of
Cu-chromium alloy (Cu-Cr) dispersed with vapor-grown carbon fiber
(VGCF) prepared by powder metallurgy (P/M) process have been
investigated. Cu-0.7 mass% Cr pre-alloyed powder (Cu-Cr) made by
water atomization process was used as raw materials, which contained
solid solute Cr elements in Cu matrix. The alloy powder coated with
un-bundled VGCF by using oil coating process was consolidated at
1223 K in vacuum by spark plasma sintering, and then extruded at
1073 K. The extruded Cu-Cr alloy (monolithic alloy) had 209.3 MPa
YS and 80.4 IACS% conductivity. The extruded Cu-Cr with 0.1
mass% VGCF composites revealed a small decrease of YS compared
to the monolithic Cu-Cr alloy. On the other hand, the composite had a
higher electrical conductivity than that of the monolithic alloy. For
example, Cu-Cr with 0.1 mass% VGCF composite sintered for 5 h
showed 182.7 MPa YS and 89.7 IACS% conductivity. In the case of
Cu-Cr with VGCFs composites, the Cr concentration was observed
around VGCF by SEM-EDS analysis, where Cr23C6 compounds were
detected by TEM observation. The amount of Cr solid solution in the
matrix of the Cu-Cr composites alloy was about 50% compared to the
monolithic Cu-Cr sintered alloy, and resulted in the remarkable
increment of the electrical conductivity.
Abstract: The aim of this study is to investigate formability of
Al based closed cell metallic foams at high temperature. The foam
specimens with rectangular section were produced from
AlMg1Si0.6TiH20.8 alloy preform material. Bending and free
bending tests based on gravity effect were applied to foam specimens
at high temperatures. During the tests, the time-angular deformation
relationships with various temperatures were determined.
Deformation types formed in cell walls were investigated by means
of Scanning Electron Microscopy (SEM) and optical microscopy.
Bending deformation about 90° was achieved without any defect at
high temperatures. The importance of a critical temperature and
deformation rate was emphasized in maintaining the deformation.
Significant slip lines on surface of cell walls at tensile zones of
bending specimen were observed. At high strain rates, the microcrack
formation in boundaries of elongated grains was determined.
Abstract: The article presents a plasma chemical technology for
processing solid fuels, using examples of bituminous and brown
coals. Thermodynamic and experimental investigation of the
technology was made. The technology allows producing synthesis
gas from the coal organic mass and valuable components (technical
silicon, ferrosilicon, aluminum, and carbon silicon, as well as
microelements of rare metals, such as uranium, molybdenum,
vanadium, etc.) from the mineral mass. The thusly produced highcalorific
synthesis gas can be used for synthesis of methanol, as a
high-calorific reducing gas instead of blast-furnace coke as well as
power gas for thermal power plants.
Abstract: Many industrial materials like magnets need to be
tested for the radiation environment expected at linear colliders (LC)
where the accelerator and detectors will be subjected to large
influences of beta, neutron and gamma’s over their life Gamma
irradiation of the permanent sample magnets using a 60Co source was
investigated up to an absorbed dose of 700Mrad shows a negligible
effect on some magnetic properties of Nd-Fe-B. In this work it has
been tried to investigate the change of some important properties of
Barium hexa ferrite. Results showed little decreases of magnetic
properties at doses rang of 0.5 to 2.5 Mrad. But at the gamma
irradiation dose up to 10 Mrad it is showed a few increase of
properties. Also study of gamma irradiation of Nd-Fe-B showed
considerably increase of magnetic properties.