Abstract: Hard coatings are widely used in cutting and forming
tool industries. Titanium Nitride (TiN) possesses good hardness,
strength, and corrosion resistance. The coating properties are
influenced by many process parameters. The coatings were deposited
on steel substrate by changing the process parameters such as
substrate temperature, nitrogen flow rate and target power in a D.C
planer magnetron sputtering. The structure of coatings were analysed
using XRD. The hardness of coatings was found using Micro
hardness tester. From the experimental data, a regression model was
developed and the optimum response was determined using Response
Surface Methodology (RSM).
Abstract: The use of magnesium alloys is limited due to their
susceptibility to corrosion although they have many attractive
physical and mechanical properties. To increase mechanical and
corrosion properties of these alloys, many deposition method and
coating types are used. Electroless Ni–B coatings have received
considerable interest recently due to its unique properties such as
cost-effectiveness, thickness uniformity, good wear resistance,
lubricity, good ductility and corrosion resistance, excellent
solderability and electrical properties and antibacterial property. In
this study, electroless Ni-B coating could been deposited on AZ91
magnesium alloy. The obtained coating exhibited a harder and
rougher structure than the substrate.
Abstract: Pure nickel coatings have been successfully
electrodeposited on copper substrates by the pulse plating technique.
The influence of current density, duty cycle and pulse frequency on
the surface morphology, crystal orientation, and microhardness was
determined. It was found that the crystallite size of the deposit
increases with increasing current density and duty cycle. The crystal
orientation progressively changed from a random texture at 1 A/dm2
to (200) texture at 10 A/dm2. Increasing pulse frequency resulted in
increased texture coefficient and peak intensity of (111) reflection.
An increase in duty cycle resulted in considerable increase in texture
coefficient and peak intensity of (311) reflection. Coatings obtained
at high current densities and duty cycle present a mixed morphology
of small and large grains. Maximum microhardness of 193 Hv was
achieved at 4 A/dm2, 10 Hz and duty cycle of 50%. Nickel coatings
with (200) texture are ductile while (111) texture improves the
microhardness of the coatings.
Abstract: Parboiled rice was developed to produce rice, which
has a low glycemic index for diabetics. However, diabetics also have
a chromium (Cr) deficiency. Thus, it is important to fortify rice with
Cr to increase the Cr content. Moreover, parboiled rice becomes
rancid easily and has a musty odor, rendering the rice unfavorable.
Natural herbs such as pandan leaves (Pandanus amaryllifolius
Roxb.), bay leaves (Syzygium polyanthum [Wigh] Walp) and
cinnamon bark powder (Cinnamomon cassia) are commonly added to
food as aroma enhancers. Previous research has shown that these
herbs could improve insulin sensitivity. The purpose of this study
was to evaluate the effect of herbal extract coatings on the cooking
quality and the preference level of chromium fortified - parboiled rice
(CFPR). The rice grain variety used for this experiment was Ciherang
and the fortificant was CrCl3. The three herbal extracts used for
coating the CFPR were cinnamon, pandan and bay leaf, with
concentration variations of 3%, 6%, and 9% (w/w) for each of the
extracts. The samples were analyzed for their alkali spreading value,
cooking time, elongation, water uptake ratio, solid loss, colour and
lightness; and their sensory properties were determined by means of
an organoleptic test. The research showed that coating the CFPR with
pandan and cinnamon extracts at a concentration of 3% each
produced a preferred CFPR. When coated with those herbal extracts
the CFPR had the following cooking quality properties: alkali
spreading value 5 (intermediate gelatinization temperature), cooking
time, 26-27 min, color value, 14.95-15.00, lightness, 42.30 – 44.06,
elongation, 1.53 – 1.54, water uptake ratio , 4.05-4.06, and solid loss,
0.09/100 g – 0.13 g/100 g.
Abstract: The present study deals with the characterization of
CrSiN coatings obtained by PVD magnetron sputtering systems.
CrSiN films were deposited with different Si contents, in order to
check the effect of at.% variation on the different properties of the
Cr–N system. Coatings were characterized by scanning electron
microscopy (SEM) for thickness measurements, X-ray diffraction.
Surface morphology and the roughness characteristics were explored
using AFM, Mechanicals properties, elastic and plastic deformation
resistance of thin films were investigated using nanoindentation test. We observed that the Si addition improved the hardness and the
Young’s modulus of the Cr–N system. Indeed, the hardness value is
18,56 GPa for CrSiN coatings. Besides, the Young’s modulus value
is 224,22 GPa for CrSiN coatings for Si content of 1.2 at.%.
Abstract: The application of cold Radio-Frequency (RF) plasma
in the conservation of cultural heritage became important in the last
decades due to the positive results obtained in decontamination
treatments. This paper presents an equipment especially designed for cold RF
plasma application on paper documents, developed within a research
project. The equipment consists in two modules: the first one is
designed for decontamination and cleaning treatments of any type of
paper supports, while the second one can be used for coating friable
papers with adequate polymers, for protection purposes. All these
operations are carried out in cold radio-frequency plasma, working in
gaseous nitrogen, at low pressure. In order to optimize the equipment parameters ancient paper
samples infested with microorganisms have been treated in nitrogen
plasma and the decontamination effects, as well as changes in surface
properties (color, pH) were assessed. The microbiological analysis
revealed complete decontamination at 6 minutes treatment duration;
only minor modifications of the surface pH were found and the
colorimetric analysis showed a slight yellowing of the support.
Abstract: Expansive soils are often encountered in many parts
of the world, especially in arid and semi-arid fields. Such kind of
soils, generally including active clay minerals in low water content,
enlarge in volume by absorbing the water through the surface and
cause a great harm to the light structures such as channel coating,
roads and airports. The expansive soils were encountered on the path
of Apa-Hotamış conveyance channel belonging to the State
Hydraulic Works in the region of Konya. In the research done in this
area, it is predicted that the soil has a swollen nature and the soil
should be filled with proper granular equipments by digging the
ground to 50-60 cm. In this study, for purpose of helping the other
research to be done in the same area, it is thought that instead of
replacing swollen soil with the granular soil, by stabilizing it with
polypropylene fiber and using it its original place decreases effect of
swelling percent, in this way the cost will be decreased. Therefore,
laboratory tests were conducted to study the effects of polypropylene
fiber on swelling characteristics of expansive soil. Test results
indicated that inclusion of fiber reduced swell percent of expansive
soil. As the fiber content increased, the unconfined compressive
strength was increased. Finally, it can be said that stabilization of
expansive soils with polypropylene fiber is an effective method.
Abstract: This paper presents the influences on the entrainment
of serpentines by grinding and reagents during copper–nickel sulfide
flotation. The previous bench flotation tests were performed to extract
the metallic values from the ore in Yunnan Mine, China and the
relatively satisfied results with recoveries of 86.92% Cu, 54.92% Ni,
and 74.73% Pt+Pd in the concentrate were harvested at their grades of
4.02%, 3.24% and 76.61 g/t, respectively. However, the content of
MgO in the concentrate was still more than 19%. Micro-flotation tests
were conducted with the objective of figuring out the influences on the
entrainment of serpentines into the concentrate by particle size,
flocculants or depressants and collectors, as well as visual
observations in suspension by OLYMPUS camera. All the tests results
pointed to the presences of both “entrapped-in” serpentines and its
coating on the hydrophobic flocs resulted from strong collectors
(combination of butyl xanthate, butyl ammonium dithophosphate,
even after adding carboxymethyl cellulose as effective depressant.
And fine grinding may escalate the entrainment of serpentines in the
concentrate.
Abstract: The nickel-manganese (Ni-Mn) alloy coating prepared
from DC electrodeposition process in sulphamate bath was studied.
The effects of process parameters, such as current density and
electrolyte composition, on the cathodic current efficiency,
microstructure, internal stress and mechanical properties were
investigated. Because of its crucial effect on the application to the
electroforming of microelectronic components, the development of
low internal stress coating with high leveling power was emphasized.
It was found that both the coating’s manganese content and the
cathodic current efficiency increased with the raise in current density.
In addition, the internal stress of the deposited coating showed
compressive nature at low current densities while changed to tensile
one at higher current densities. Moreover, the metallographic
observation, X-ray diffraction measurement, and polarization curve
measurement were conducted. It was found that the Ni-Mn coating
consisted of nano-sized columnar grains and the maximum hardness of
the coating was associated with (111) preferred orientation in the
microstructure. The grain size was refined along with the increase in
the manganese content of the coating, which accordingly, raised its
hardness and resistance to annealing softening. In summary, the
Ni-Mn coating prepared at lower current density of 1-2 A/dm2 had low
internal stress, high leveling power, and better corrosion resistance.
Abstract: A solar dish collector has been designed, fabricated
and tested for its performance on 10-03-2015 in Salem, Tamilnadu,
India. The experiments on cooking vessels of coated and un-coated
with 5 Liters capacity have been used for cooking Rice. The results
are shown in graphs. The solar cooker is always capable of cooking
food within the expected length of time and based on the solar
radiation levels. With minimum cooking power, the coated pressure
cooker of 5 Liters capacity cooks the food at faster manner. This is
due to the conductivity of the coating material provided in the cooker.
Abstract: The use of titanium fluoride and iron fluoride
(TiF3/FeF3) catalysts in combination with polutetrafluoroethylene
(PTFE) in plain zinc- dialkyldithiophosphate (ZDDP) oil is important
for the study of engine tribocomponents and is increasingly a strategy
to improve the formation of tribofilm and provide low friction and
excellent wear protection in reduced phosphorus plain ZDDP oil. The
influence of surface roughness and the concentration of
TiF3/FeF3/PTFE were investigated using bearing steel samples
dipped in lubricant solution at 100°C for two different heating time
durations. This paper addresses the effects of water drop contact
angle using different surface; finishes after treating them with
different lubricant combination. The calculated water drop contact
angles were analyzed using Design of Experiment software (DOE)
and it was determined that a 0.05 μm Ra surface roughness would
provide an excellent TiF3/FeF3/PTFE coating for antiwear resistance
as reflected in the Scanning electron microscopy (SEM) images and
the tribological testing under extreme pressure conditions. Both
friction and wear performance depend greatly on the PTFE/and
catalysts in plain ZDDP oil with 0.05 % phosphorous and on the
surface finish of bearing steel. The friction and wear reducing effects,
which was observed in the tribological tests, indicated a better micro
lubrication effect of the 0.05 μm Ra surface roughness treated at
100°C for 24 hours when compared to the 0.1 μm Ra surface
roughness with the same treatment.
Abstract: A novel chromium-free protective coating films based
on a zeolite coating was growing onto a FeCrAlloy metal using in –
situ hydrothermal method. The zeolite film was obtained using in-situ
crystallization process that is capable of coating large surfaces with
complex shape and in confined spaces has been developed. The
zeolite coating offers an advantage of a high mechanical stability and
thermal stability. The physicochemical properties were investigated
using X-ray diffraction (XRD), Electron Microscopy (SEM), Energy
Dispersive X–ray Analysis (EDX) and Thermogravimetric Analysis
(TGA). The transition from oxide-on-alloy wires to hydrothermally
synthesised uniformly zeolite coated surfaces was followed using
SEM and XRD. In addition, the robustness of the prepared coating
was confirmed by subjecting these to thermal cycling (ambient to
550oC).
Abstract: The synthesis of CuFe2O4 spinel powders by an
optimized combustion-like process followed by calcination is
described herein. The samples were characterized using X-ray
diffraction (XRD), differential thermal analysis (TG/DTA), scanning
electron microscopy (SEM), dilatometry and 4-probe DC methods.
Different glycine to nitrate (G/N) ratios of 1 (fuel-deficient), 1.48
(stoichiometric) and 2 (fuel-rich) were employed. Calcining the asprepared
powders at 800 and 1000°C for 5 hours showed that the G/N
ratio of 2 results in the formation of the desired copper spinel single
phase at both calcination temperatures. For G/N=1, formation of
CuFe2O4 takes place in three steps. First, iron and copper nitrates
decompose to iron oxide and pure copper. Then, copper transforms to
copper oxide and finally, copper and iron oxides react with each other
to form a copper ferrite spinel phase. The electrical conductivity and
the coefficient of thermal expansion of the sintered pelletized
samples were 2 S.cm-1 (800°C) and 11×10-6 °C-1 (25-800°C),
respectively.
Abstract: Polyaniline is an indispensible component in lightemitting
devices (LEDs), televisions, cellular telephones, automotive,
corrosion-resistant coatings, actuators etc. The electrical conductivity
properties was found be increased by introduction of metal nano
particles. In the present study, an attempt has been made to utilize
platinum nano particles to achieve the improved electrical properties.
Polyaniline and Pt-polyaniline composite are synthesized by
electrochemical routes. X-ray diffractometer confirms the amorphous
nature of polyaniline. The Bragg’s diffraction peaks correspond to
platinum nanoparticles in Pt-polyaniline composite and
thermogravimetric analyzer indicates its decomposition at certain
temperature. The Scanning Electron Micrographs of colloidal
platinum nanoparticles were spherical, uniform shape in the
composite. The current-voltage (I-V) characteristics of the PANI and
composites were also studied which indicate a significant decreasing
resistivity than PANI-Platinum after introduction of pt nanoparticles
in the matrix of polyaniline (PANI).
Abstract: These Monolayer and multilayer coatings of CrN and
AlCrN deposited on 100Cr6 (AISI 52100) substrate by PVD
magnetron sputtering system. The microstructures of the coatings
were characterized using atomic force microscopy (AFM). The AFM
analysis revealed the presence of domes and craters that are
uniformly distributed over all surfaces of the various layers.
Nanoindentation measurement of CrN coating showed maximum
hardness (H) and modulus (E) of 14 GPa and 190 GPa, respectively.
The measured H and E values of AlCrN coatings were found to be 30
GPa and 382 GPa, respectively. The improved hardness in both the
coatings was attributed mainly to a reduction in crystallite size and
decrease in surface roughness. The incorporation of Al into the CrN
coatings has improved both hardness and Young’s modulus.
Abstract: In this study, to clarify the effectiveness of an
aluminum/chromium/tungsten-based-coated tool for cutting sintered
steel, tool wear was experimentally investigated. The sintered steel
was turned with the (Al60,Cr25,W15)N-, (Al60,Cr25,W15)(C,N)- and
(Al64,Cr28,W8)(C,N)-coated cemented carbide tools according to the
physical vapor deposition (PVD) method. Moreover, the tool wear of
the aluminum/chromium/tungsten-based-coated item was compared
with that of the (Al,Cr)N coated tool. Furthermore, to clarify the tool
wear mechanism of the aluminum/chromium/tungsten-coating film for
cutting sintered steel, Scanning Electron Microscope observation and
Energy Dispersive x-ray Spectroscopy mapping analysis were
conducted on the abraded surface. The following results were
obtained: (1) The wear progress of the (Al64,Cr28,W8)(C,N)-coated
tool was the slowest among that of the five coated tools. (2) Adding
carbon (C) to the aluminum/chromium/tungsten-based-coating film
was effective for improving the wear-resistance. (3) The main wear
mechanism of the (Al60,Cr25,W15)N-, the (Al60,Cr25,W15)(C,N)-
and the (Al64,Cr28,W8)(C,N)-coating films was abrasive wear.
Abstract: Zn alloy and composite coatings are widely used in
buildings and structures, automobile and fasteners industries to
protect steel component from corrosion. In this paper, Zn-Ni-Al2O3
nanocomposite coatings were electrodeposited on mild steel using a
novel sol enhanced electroplating method. In this method, transparent
Al2O3 sol was added into the acidic Zn-Ni bath to produced Zn-Ni-
Al2O3 nanocomposite coatings. The effect of alumina sol on the
electrodeposition process, and coating properties was investigated
using cyclic voltammetry, XRD, ESEM and Tafel test. Results from
XRD tests showed that the structure of all coatings was single γ-
Ni5Zn21 phase. Cyclic voltammetry results showed that the
electrodeposition overpotential was lower in the presence of alumina
sol in the bath, and caused the reduction potential of Zn-Ni to shift to
more positive values. Zn-Ni-Al2O3 nanocomposite coatings produced
more uniform and compact deposits, with fine grained microstructure
when compared to Zn-Ni coatings. The corrosion resistance of Zn-Ni
coatings was improved significantly by incorporation of alumina
nanoparticles into the coatings.
Abstract: Psyllium gum alone and in combination with
sunflower oil was investigated as a possible alternative edible coating
for improvement of quality and shelf life of fresh-cut papaya.
Different concentrations including 0.5, 1 and 1.5 percent of psyllium
gum were used for coating of fresh-cut papaya. In some samples,
refined sunflower oil was used as a lipid component to increase the
effectiveness of coating in terms of water barrier properties. Soya
lecithin was used as an emulsifier in coatings containing oil.
Pretreatment with 1% calcium chloride was given to maintain the
firmness of fresh-cut papaya cubes. 1% psyllium gum coating was
found to yield better results. Further, addition of oil helped to
maintain the quality and acted as a barrier to water vapour, therefore,
minimizing the weight loss.
Abstract: The future and the development of science is therefore
seen in interdisciplinary areas such as biomedical engineering. Selfassembled
structures, similar to stem cell niches would inhibit fast
division process and subsequently capture the stem cells from the
blood flow. By means of surface topography and the stiffness as well
as microstructure progenitor cells should be differentiated towards
the formation of endothelial cells monolayer which effectively will
inhibit activation of the coagulation cascade. The idea of the material
surface development met the interest of the clinical institutions,
which support the development of science in this area and are waiting
for scientific solutions that could contribute to the development of
heart assist systems. This would improve the efficiency of the
treatment of patients with myocardial failure, supported with artificial
heart assist systems. Innovative materials would enable the redesign,
in the post project activity, construction of ventricular heart assist.
Abstract: A dip-coating process has been used to form an
asymmetric silica membrane with improved membrane performance
and reproducibility. First, we deposited repeatedly silica on top of a
commercial alumina membrane support to improve its structural
make up. The membrane is further processed under clean room
conditions to avoid dust impurity and subsequent drying in an oven
for high thermal, chemical and physical stability. The resulting
asymmetric membrane exhibits a gradual change in the membrane
layer thickness. Compared to the support, the dual-layer process
improves the gas flow rates. For the scientific applications for natural
gas purification, CO2, CH4 and H2 gas flow rates were. In addition,
the membrane selectively separated hydrogen.