Abstract: The process of post-supercritical CO2 electroplating uses the electrolyte solution after being mixed with supercritical CO2 and released to atmospheric pressure. It utilizes the microbubbles that form when oversaturated CO2 in the electrolyte returns to gaseous state, which gives the similar effect of pulsed electroplating. Under atmospheric pressure, the CO2 bubbles gradually diffuse. Therefore, the introduction of ultrasound and/or other agitation can potentially excite the CO2 microbubbles to achieve an electroplated surface of even higher quality. In this study, during the electroplating process, three different modes of agitation: magnetic stirrer agitation, ultrasonic agitation and a combined mode (magnetic + ultrasonic) were applied, respectively, in order to obtain an optimal surface morphology and mechanical properties for the electroplated Ni coating. It is found that the combined agitation mode at a current density of 40 A/dm2 achieved the smallest grain size, lower surface roughness, and produced an electroplated Ni layer that achieved hardness of 320 HV, much higher when compared with conventional method, which were usually in the range of 160 to 300 HV. However, at the same time, the electroplating with combined agitation developed a higher internal stress of 320 MPa due to the lower current efficiency of the process and finer grain in the coating. Moreover, a new control methodology for tailoring the coating’s mechanical property through its thickness was demonstrated by the timely introduction of ultrasonic agitation during the electroplating process with post supercritical CO2 mixed electrolyte.
Abstract: The nickel-manganese (Ni-Mn) alloy coating prepared
from DC electrodeposition process in sulphamate bath was studied.
The effects of process parameters, such as current density and
electrolyte composition, on the cathodic current efficiency,
microstructure, internal stress and mechanical properties were
investigated. Because of its crucial effect on the application to the
electroforming of microelectronic components, the development of
low internal stress coating with high leveling power was emphasized.
It was found that both the coating’s manganese content and the
cathodic current efficiency increased with the raise in current density.
In addition, the internal stress of the deposited coating showed
compressive nature at low current densities while changed to tensile
one at higher current densities. Moreover, the metallographic
observation, X-ray diffraction measurement, and polarization curve
measurement were conducted. It was found that the Ni-Mn coating
consisted of nano-sized columnar grains and the maximum hardness of
the coating was associated with (111) preferred orientation in the
microstructure. The grain size was refined along with the increase in
the manganese content of the coating, which accordingly, raised its
hardness and resistance to annealing softening. In summary, the
Ni-Mn coating prepared at lower current density of 1-2 A/dm2 had low
internal stress, high leveling power, and better corrosion resistance.
Abstract: This research studies the electroplating of zinc coating
in the zinc chloride bath mixed with supercritical CO2. The sodium
fluoride (NaF) was used as the bath additive to change the structure
and property of the coating, and therefore the roughness and corrosion
resistance of the zinc coating was investigated. The surface
characterization was performed using optical microscope (OM), X-ray
diffractometer (XRD), and α-step profilometer. Moreover, the
potentiodynamic polarization measurement in 3% NaCl solution was
employed in the corrosion resistance evaluation. Because of the
emulsification of the electrolyte mixed in Sc-CO2, the electroplated
zinc produced the coating with smoother surface, smaller grain, better
throwing power and higher corrosion resistance. The main role played
by the NaF was to reduce the coating’s roughness and grain size. In
other words, the CO2 mixed with the electrolyte under the supercritical
condition performed the similar function as brighter and leveler in zinc
electroplating to enhance the throwing power and corrosion resistance
of the coating.
Abstract: This paper aims to present the design, fabrication and test of a novel piezoelectric actuated, check-valves embedded micropump having the advantages of miniature size, light weight and low power consumption. This device is designed to pump gases and liquids with the capability of performing the self-priming and bubble-tolerant work mode by maximizing the stroke volume of the membrane as well as the compression ratio via minimization of the dead volume of the micropump chamber and channel. By experiment apparatus setup, we can get the real-time values of the flow rate of micropump, the displacement of the piezoelectric actuator and the deformation of the check valve, simultaneously. The micropump with check valve 0.4 mm in thickness obtained higher output performance under the sinusoidal waveform of 120 Vpp. The micropump achieved the maximum pumping rates of 42.2 ml/min and back pressure of 14.0 kPa at the corresponding frequency of 28 and 20 Hz. The presented micropump is able to pump gases with a pumping rate of 196 ml/min at operating frequencies of 280 Hz under the sinusoidal waveform of 120 Vpp.
Abstract: The main objective of this article is to present the semi-active vibration control using an electro-rheological fluid embedded sandwich structure for a cantilever beam. ER fluid is a smart material, which cause the suspended particles polarize and connect each other to form chain. The stiffness and damping coefficients of the ER fluid can be changed in 10 micro seconds; therefore, ERF is suitable to become the material embedded in the tunable vibration absorber to become a smart absorber. For the ERF smart material embedded structure, the fuzzy control law depends on the experimental expert database and the proposed self-tuning strategy. The electric field is controlled by a CRIO embedded system to implement the real application. This study investigates the different performances using the Type-1 fuzzy and interval Type-2 fuzzy controllers. The Interval type-2 fuzzy control is used to improve the modeling uncertainties for this ERF embedded shock absorber. The self-tuning vibration controllers using Type-1 and Interval Type-2 fuzzy law are implemented to the shock absorber system. Based on the resulting performance, Internal Type-2 fuzzy is better than the traditional Type-1 fuzzy control for this vibration control system.
Abstract: This paper investigates experimental studies on
vibration suppression for a cantilever beam using an
Electro-Rheological (ER) sandwich shock absorber. ER fluid (ERF) is a
class of smart materials that can undergo significant reversible changes
immediately in its rheological and mechanical properties under the
influence of an applied electric field. Firstly, an ER sandwich beam is
fabricated by inserting a starch-based ERF into a hollow composite
beam. At the same time, experimental investigations are focused on the
frequency response of the ERF sandwich beam. Second, the ERF
sandwich beam is attached to a cantilever beam to become as a shock
absorber. Finally, a fuzzy semi-active vibration control is designed to
suppress the vibration of the cantilever beam via the ERF sandwich
shock absorber. To check the consistency of the proposed fuzzy
controller, the real-time implementation validated the performance of
the controller.
Abstract: In this study, a nickel film with nano-crystalline grains,
high hardness and smooth surface was electrodeposited using a post
supercritical carbon dioxide (CO2) mixed Watts electrolyte. Although
the hardness was not as high as its Sc-CO2 counterpart, the thin coating
contained significantly less number of nano-sized pinholes. By
measuring the escape concentration of the dissolved CO2 in post
Sc-CO2 mixed electrolyte with the elapsed time, it was believed that
the residue of dissolved CO2 bubbles should closely relate to the
improvement in hardness and surface roughness over its conventional
plating counterpart. Therefore, shortening the duration of
electroplating with the raise of current density up to 0.5 A/cm2 could
effectively retain more post Sc-CO2 mixing effect. This study not only
confirms the roles of dissolved CO2 bubbles in electrolyte but also
provides a potential process to overcome most issues associated with
the cost in building high-pressure chamber for large size products and
continuous plating using supercritical method.