Abstract: In this paper, the effect of WC-12Co particle
temperature in HVOF thermal spraying process on the coating
thickness has been studied. The statistical results show that the spray
distance and oxygen-to-fuel ratio are effective factors on particle
characterization and thickness of HVOF thermal spraying coatings.
Spray Watch diagnostic system, scanning electron microscopy
(SEM), X-ray diffraction and thickness measuring system were used
for this purpose.
Abstract: Calcium phosphate coating (CaP) has been employed
for protein delivery, but the typical direct protein adsorption on the
coating led to low incorporation content and fast release of the
protein from the coating. By using bovine serum albumin (BSA) as a
model protein, rapid biomimetic co-precipitation between calcium
phosphate and BSA was employed to control the distribution of BSA
within calcium phosphate coating during biomimetic formation on
titanium surface for only 6 h at 50oC in an accelerated calcium
phosphate solution. As a result, the amount of BSA incorporation and
release duration could be increased by using a rapid biomimetic coprecipitation
technique. Up to 43 fold increases in the BSA
incorporation content and the increase from 6 h to more than 360 h in
release duration compared to typical direct adsorption technique were
observed depending on the initial BSA concentration used during coprecipitation
(1, 10 and 100 μg.ml-1). From x-ray diffraction and
Fourier transform infrared spectroscopy studies, the coating
composition was not altered with the incorporation of BSA by this
rapid biomimetic co-precipitation and mainly comprised octacalcium
phosphate and hydroxyapatite. However, the microstructure of
calcium phosphate crystals changed from straight, plate-like units to
curved, plate-like units with increasing BSA content.
Abstract: Concerns on corrosion and effective coating
protection of double hull tankers and bulk carriers in service have
been raised especially in water ballast tanks (WBTs). Test
protocols/methodologies specifically that which is incorporated in the
International Maritime Organisation (IMO), Performance Standard
for Protective Coatings for Dedicated Sea Water ballast tanks (PSPC)
are being used to assess and evaluate the performance of the coatings
for type approval prior to their application in WBTs. However, some
of the type approved coatings may be applied as very thick films to
less than ideally prepared steel substrates in the WBT. As such films
experience hygrothermal cycling from operating and environmental
conditions, they become embrittled which may ultimately result in
cracking. This embrittlement of the coatings is identified as an
undesirable feature in the PSPC but is not mentioned in the test
protocols within it. There is therefore renewed industrial research
aimed at understanding this issue in order to eliminate cracking and
achieve the intended coating lifespan of 15 years in good condition.
This paper will critically review test protocols currently used for
assessing and evaluating coating performance, particularly the IMO
PSPC.
Abstract: This research studies the electroplating of zinc coating
in the zinc chloride bath mixed with supercritical CO2. The sodium
fluoride (NaF) was used as the bath additive to change the structure
and property of the coating, and therefore the roughness and corrosion
resistance of the zinc coating was investigated. The surface
characterization was performed using optical microscope (OM), X-ray
diffractometer (XRD), and α-step profilometer. Moreover, the
potentiodynamic polarization measurement in 3% NaCl solution was
employed in the corrosion resistance evaluation. Because of the
emulsification of the electrolyte mixed in Sc-CO2, the electroplated
zinc produced the coating with smoother surface, smaller grain, better
throwing power and higher corrosion resistance. The main role played
by the NaF was to reduce the coating’s roughness and grain size. In
other words, the CO2 mixed with the electrolyte under the supercritical
condition performed the similar function as brighter and leveler in zinc
electroplating to enhance the throwing power and corrosion resistance
of the coating.
Abstract: This work investigates the wear of a steam turbine blade coated with titanium nitride (TiN), and compares to the wear of uncoated blades. The coating is deposited on by physical vapor deposition (PVD) method. The working conditions of the blade were simulated and surface temperature and pressure values as well as flow velocity and flow direction were obtained. This data was used in the finite element wear model developed here in order to predict the wear of the blade. The wear mechanisms considered are erosive wear due to particle impingement and fluid jet, and fatigue wear due to repeated impingement of particles and fluid jet. Results show that the life of the TiN-coated blade is approximately 1.76 times longer than the life of the uncoated one.
Abstract: In this study, the Mo-electrode thin films were deposited using two-stepped process and the high purity copper indium selenide-based powder (CuInSe2, CIS) was fabricated by using hydrothermal process by Nanowin Technology Co. Ltd. Because the CIS powder was aggregated into microscale particles, the CIS power was ground into nano-scale particles. 6 wt% CIS particles were mixed and dispersed into isopropyl alcohol (IPA). A new non-vacuum thin-film deposition process, spray coating method (SPM), was investigated to deposit the high-densified CIS absorber layers. 0.1 ml CIS solution was sprayed on the 20 mm×10 mm Mo/glass substrates and then the CuInSe2 thin films were annealed in a selenization furnace using N2 as atmosphere. The annealing temperature and time were set at 550oC and 5 min, and 0.0g~0.6g extra Se content was added in the furnace. The influences of extra Se content on the densification, crystallization, resistivity (ρ), hall mobility (μ), and carrier concentration of the CIS absorber layers were well investigated in this study.
Abstract: Polymeric materials have become an integral part of every aspect of today's industry. They have wide applications, inter alia, in areas such as medicine, food industry and agriculture. In agriculture, for example, they are used for the production of pots, irrigation systems and for soil mulching. The aim of this study was the attempt to produce a biodecomposable agricultural mat, by coating cotton fabric with a blend of carboxylated styrene-butadiene latex (LBSK) containing the enzymatic hydrolyzate of keratin from cattle hair, which would serve as a material for mulching.
The production of such material allows the beneficial management of burdensome tannery waste constituted by keratin from cattle hair and at the same time, the production of agricultural mats that much faster undergo decomposition than commonly used polyethylene mats.
Abstract: This work details the generation of thin films of
structured zeolite catalysts (ZSM–5 and Y) onto the surface of a
metal substrate (FeCrAlloy) using in-situ hydrothermal synthesis. In
addition, the zeolite Y is post-synthetically modified by acidified
ammonium ion exchange to generate US-Y. Finally the catalytic
activity of the structured ZSM-5 catalyst films (Si/Al = 11, thickness
146 0m) and structured US–Y catalyst film (Si/Al = 8, thickness
230m) were compared with the pelleted powder form of ZSM–5 and
USY catalysts of similar Si/Al ratios.
The structured catalyst films have been characterised using a range
of techniques, including X-ray diffraction (XRD), Electron
microscopy (SEM), Energy Dispersive X–ray analysis (EDX) and
Thermogravimetric Analysis (TGA). The transition from oxide-onalloy
wires to hydrothermally synthesised uniformly zeolite coated
surfaces was followed using SEM and XRD. In addition, the
robustness of the prepared coating was confirmed by subjecting these
to thermal cycling (ambient to 550oC).
The cracking of n–heptane over the pellets and structured catalysts
for both ZSM–5 and Y zeolite showed very similar product
selectivities for similar amounts of catalyst with an apparent
activation energy of around 60 kJ mol-1. This paper demonstrates that
structured catalysts can be manufactured with excellent zeolite
adherence and when suitably activated/modified give comparable
cracking results to the pelleted powder forms. These structured
catalysts will improve temperature distribution in highly exothermic
and endothermic catalysed processes.
Abstract: The problem of magnetohydrodynamics boundary layer flow and heat transfer on a permeable stretching surface in a second grade nanofluid under the effect of heat generation and partial slip is studied theoretically. The Brownian motion and thermophoresis effects are also considered. The boundary layer equations governed by the PDE’s are transformed into a set of ODE’s with the help of local similarity transformations. The differential equations are solved by variational finite element method. The effects of different controlling parameters on the flow field and heat transfer characteristics are examined. The numerical results for the dimensionless velocity, temperature and nanoparticle volume fraction as well as the reduced Nusselt and Sherwood number have been presented graphically. The comparison confirmed excellent agreement. The present study is of great interest in coating and suspensions, cooling of metallic plate, oils and grease, paper production, coal water or coal-oil slurries, heat exchangers technology, materials processing exploiting.
Abstract: Aluminum Matrix Composites reinforced with
nanocrystalline Ni3Al carbon-coated intermetallic particles, were
synthesized by powder metallurgy. Powder mixture of aluminum
with 0.5-volume fraction of reinforcement particles was compacted
by spark plasma sintering (SPS) technique and the compared with
conventional sintering process. The better results for SPS technique
were obtained in 520ºC-5kN-3min.The hardness (70.5±8 HV) and the
elastic modulus (95 GPa) were evaluated in function of sintering
conditions for SPS technique; it was found that the incorporation of
these kind of reinforcement particles in aluminum matrix improve its
mechanical properties. The densities were about 94% and 97% of the
theoretical density. The carbon coating avoided the interfacial
reaction between matrix-particle at high temperature (520°C) without
show composition change either intermetallic dissolution.
Abstract: Microfibrous palygorskite and tubular halloysite clay mineral combined with nanocrystalline TiO2 are incorporating in the preparation of nanocomposite films on glass substrates via sol-gel route at 450oC. The synthesis is employing nonionic surfactant molecule as pore directing agent along with acetic acid-based sol-gel route without addition of water molecules. Drying and thermal treatment of composite films ensure elimination of organic material lead to the formation of TiO2 nanoparticles homogeneously distributed on the palygorskite or halloysite surfaces. Nanocomposite films without cracks of active anatase crystal phase on palygorskite and halloysite surfaces are characterized by microscopy techniques, UV-Vis spectroscopy, and porosimetry methods in order to examine their structural properties.
The composite palygorskite-TiO2 and halloysite-TiO2 films with variable quantities of palygorskite and halloysite were tested as photocatalysts in the photo-oxidation of Basic Blue 41 azo dye in water. These nanocomposite films proved to be most promising photocatalysts and highly effective to dye’s decoloration in spite of small amount of palygorskite-TiO2 or halloysite-TiO2 catalyst immobilized onto glass substrates mainly due to the high surface area and uniform distribution of TiO2 on clay minerals avoiding aggregation.
Abstract: In this study, a plasma electrolytic oxidation (PEO) process was used to form titanium-aluminum oxide coating on aluminized steel. The present work was mainly to study the effects of treatment time of PEO process on properties of the titanium coating. A potentiodynamic polarization corrosion test was employed to investigate the corrosion resistance of the coating. The friction coefficient and wear resistance of the coating were studied by using pin-on-disc test. The thermal transfer behaviors of uncoated and PEO-coated aluminized steels were also studied. It could be seen that treatment time of PEO process significantly influenced the properties of the titanium oxide coating. Samples with a longer treatment time had a better performance for corrosion and wear protection. This paper demonstrated different treatment time could alter the surface behavior of the coating material.
Abstract: In this paper, the effect of WC-12Co particle velocity in HVOF thermal spraying process on the coating thickness has been studied. The statistical results show that the spray distance and oxygen-to-fuel ratio are more effective factors on particle characterization and thickness of HVOF thermal spraying coatings. Spray Watch diagnostic system, scanning electron microscopy (SEM), X-ray diffraction and thickness measuring system were used for this purpose.
Abstract: High velocity oxygen fuel (HVOF) spray technique is one of the leading technologies that have been proposed as an alternative to the replacement of electrolytic hard chromium plating in a number of engineering applications. In this study, WC-Co powder was coated on AISI1045 steel using high velocity oxy fuel (HVOF) method. The sin2ψ method was used to evaluate the through thickness residual stress by means of XRD after mechanical layer removal process (only grinding). The average of through thickness residual stress using X-Ray diffraction was -400 MPa.
Abstract: This article is focused on the thermal spray coating machining issue. Those are irreplaceable in many areas of nowadays industrial branches such as aerospace industry, mostly thanks to their excellent qualities in production and also in renovation of machinery parts. The principals of thermal spraying and elementary diversification are described in introduction. Plasma coating method of composite materials – cermets – is described more thoroughly. The second part describes thermal spray coating machining and grinding in detail. This part contains suggestion of appropriate grinding tool and assessment of cutting conditions used for grinding a given part. Conclusion describes a problem which occurred while grinding a cermet thermal spray coating with a specially designed grindstone and a way to solve this problem.
Abstract: Polymer nanocomposites represent a new class of materials in which nanomaterials act as the reinforcing material in composites, wherein small additions of nanomaterials lead to large enhancements in thermal, optical and mechanical properties. A boost in these properties is due to the large interfacial area per unit volume or weight of the nanoparticles and the interactions between the particle and the polymer. Micro sized particles used as reinforcing agents scatter light, thus reducing light transmittance and optical clarity. Efficient nanoparticle dispersion combined with good polymer–particle interfacial adhesion eliminates scattering and allows the exciting possibility of developing strong yet transparent films, coatings and membranes. This paper aims at synthesising zinc oxide nanoparticles which are reinforced in poly vinyl alcohol (PVA) polymer. The mechanical properties showed that the tensile strength of the PVA nanocomposites increases with the increase in the amount of nanoparticles.
Abstract: Shellac is a natural polyester resin secreted by insects. Pectins are natural, non-toxic and water-soluble polysaccharides extracted from the peels of citrus fruits or the leftovers of apples. Both polymers are allowed for the use in the pharmaceutical industry and as a food additive. SSB Aquagold® is the aqueous solution of shellac and can be used for a coating process as an enteric or controlled drug release polymer. In this study, tablets containing 10 mg methylene blue as a model drug were prepared with a rotary press. Those tablets were coated with mixtures of shellac and one of the pectin different types (i.e. CU 201, CU 501, CU 701 and CU 020) mostly in a 2:1 ratio or with pure shellac in a small scale fluidized bed apparatus. A stable, simple and reproducible three-stage coating process was successfully developed. The drug contents of the coated tablets were determined using UV-VIS spectrophotometer. The characterization of the surface and the film thickness were performed with the scanning electron microscopy (SEM) and the light microscopy. Release studies were performed in a dissolution apparatus with a basket. Most of the formulations were enteric coated. The dissolution profiles showed a delayed or sustained release with a lagtime of at least 4 h. Dissolution profiles of coated tablets with pure shellac had a very long lagtime ranging from 13 to 17.9 h and the slopes were quite high. The duration of the lagtime and the slope of the dissolution profiles could be adjusted by adding the proper type of pectin to the shellac formulation and by variation of the coating amount. In order to apply a coating formulation as a colon delivery system, the prepared film should be resistant against gastric fluid for at least 2 h and against intestinal fluid for 4-6 h. The required delay time was gained with most of the shellac-pectin polymer mixtures. The release profiles were fitted with the modified model of the Korsmeyer-Peppas equation and the Hixson-Crowell model. A correlation coefficient (R²)> 0.99 was obtained by Korsmeyer-Peppas equation.
Abstract: Silicon substrates coated with multiwalled carbon nanotubes (MWCNTs) were experimentally investigated to determine spark breakdown voltages relative to uncoated surfaces, the degree of surface degradation associated with the spark discharge, and techniques to minimize the surface degradation. The results may be applicable to instruments or processes that use MWCNT as a means of increasing local electric field strength and where spark breakdown is a possibility that might affect the devices’ performance or longevity. MWCNTs were shown to reduce the breakdown voltage of a 1mm gap in air by 30-50%. The relative decrease in breakdown voltage was maintained over gap distances of 0.5 to 2mm and gauge pressures of 0 to 4 bar. Degradation of the MWCNT coated surfaces was observed. Several techniques to improve durability were investigated. These included: chromium and gold-palladium coatings, tube annealing, and embedding clusters of MWCNT in a ceramic matrix.
Abstract: The purpose of this study was to prepare time and pH dependent release tablets of Ayurvedic Churna formulation and evaluate their advantages as colon targeted drug delivery system. The Vidangadi Churna was selected for this study which contains Embelin and Gallic acid. Embelin is used in Helminthiasis as therapeutic agent. Embelin is insoluble in water and unstable in gastric environment so it was formulated in time and pH dependent tablets coated with combination of two polymers Eudragit L100 and ethyl cellulose. The 150mg of core tablet of dried extract and lactose were prepared by wet granulation method. The compression coating was used in the polymer concentration of 150mg for both the layer as upper and lower coating tablet was investigated. The results showed that no release was found in 0.1 N HCl and pH 6.8 phosphate buffers for initial 5 hours and about 98.97% of the drug was released in pH 7.4 phosphate buffer in total 17 Hours. The in vitro release profiles of drug from the formulation could be best expressed first order kinetics as highest linearity (r2= 0.9943). The results of the present study have demonstrated that the time and pH dependent tablets system is a promising vehicle for preventing rapid hydrolysis in gastric environment and improving oral bioavailability of Embelin and Gallic acid for treatment of Helminthiasis.
Abstract: The paper presents a new drugs delivery system, based on the thin film technology. As a model antitumor drug, highly toxic doxorubicin is chosen. The system is based on the technology of obtaining zinc oxide composite of doxorubicin by deposition of nanosize ZnO films on the surface of doxorubicin coating on glass substrate using DC magnetron sputtering of zinc targets in Ar:O2 medium at room temperature. For doxorubicin zinc oxide compositions in the form of coatings and gels with 180-200nm thick ZnO films, higher (by a factor 2) in vivo (ascitic Ehrlich's carcinoma) antitumor activity is observed at low doses of doxorubicin in comparison with that of the initial preparation at therapeutic doses. The vector character of the doxorubicin zinc oxide composite transport to tumor tissues ensures the increase in antitumor activity as well as decrease of toxicity in comparison with the initial drug.