The Collapse of a Crane on Site: A Case Study

This paper discusses the causes of the structural failure in a tower crane. The structural collapse occurred at the upper joints of the extension element used to increase the height of the crane. The extension element consists of a steel lattice structure made with angular profiles and plates joined to the tower element by arc welding. Macroscopic inspection of the sections showed that the break was always observed on the angular profiles at the weld bead edge. The case study shows how, using mechanical characterization, chemical analysis of the steel and macroscopic and microscopic metallographic examinations, it was possible to obtain significant evidence that identified the mechanism causing the breakage. The analyses identified the causes of the structural failure as the use of materials that were not suitable for welding and poor performance in the welding joints.





References:
[1] Thomas, D.J., “Analyzing the Failure of Welded Steel Components in Construction Systems”, J Fail. Anal. and Preven. 18, pp. 304–314, 2018.
[2] Standard ISO 6892-1, “Metallic materials-Tensile testing - Part 1: Method of test at room temperature”, 2016
[3] Standard EN 10025-1, “Hot rolled products of structural steels - Part 1: General technical delivery conditions”, 2005.
[4] Comparison table according to standard EN ISO 18265, “Metallic materials - Conversion of hardness values”, 2013.
[5] Standard EN 6520-1, “Welding and allied processes - Classification of geometric imperfections in metallic materials - Part 1: Fusion welding”, 2008.
[6] Bhadeshia H., Honeycombe R., “Steels: Microstructure and Properties”, Butterworth-Heinemann, 2017.
[7] O’Brien A., Guzman C., “Welding-Handbook”, Vol.4, Materials and application, Part1 (9th-Edition), AWS, 2011.
[8] Şükrü T., “The assessment of carbon equivalent formulas in predicting the properties of steel weld metals”, Materials & Design (1980-2015), Volume 31, Issue 5, pp. 2649-2653, 2010.
[9] Olabi A.G., Hashmi M.S.J., “The microstructure and mechanical properties of low carbon steel welded components after the application of PWHTs”, Journal of Materials Processing Technology, Volume 56, Issues 1–4, pp. 88-97, 1996.