Volume:8, Issue: 10, 2014 Page No: 1105 - 1108
ISSN: 2415-6620
High temperature deformation behavior of cast
Fe-20Cr-5Al alloy has been investigated in this study by performing
tensile and compression tests at temperatures from 1100 to 1200oC.
Rectangular ingots of which the dimensions were 300×300×100 in
millimeter were cast using vacuum induction melting. Phase
equilibrium was calculated using the FactSage®, thermodynamic
software and database. Tensile strength of cast Fe-20Cr-5Al alloy was
4 MPa at 1200oC. With temperature decreased, tensile strength
increased rapidly and reached up to 13 MPa at 1100oC. Elongation
also increased from 18 to 80% with temperature decreased from
1200oC to 1100oC. Microstructure observation revealed that M23C6
carbide was precipitated along the grain boundary and within the
matrix.