Abstract: (Bi0.5Na0.5)TiO3 doped with 8 mol % BaTiO3 powder
(BNT-BT0.08), prepared by sol-gel method was compacted and
sintered by Spark Plasma Sintering (SPS) process. The influence of
SPS temperature on the densification of BNT-BT0.08 ceramic was
investigated. Starting from sol-gel nanopowder of BNT-BT
containing 8 mol % BaTiO3 with an average particles size of about
30 nm, were obtained ceramics with density around 98 % of the
theoretical density value when the SPS temperature used was about
850 °C. The average grain size of the resulting ceramics was 80 nm.
The BNT-BT0.08 ceramic sample obtained by SPS method has shown
good electric properties at various frequencies.
Abstract: Nanowire arrays of copper with uniform diameters have
been synthesized by potentiostatic electrochemical metal deposition
(EMD) of copper sulphate and potassium chloride solution within
the nano-channels of porous Indium-Tin Oxide (ITO), also known as
Tin doped Indium Oxide templates. The nanowires developed were
fairly continuous with diameters ranging from 110-140 nm along
the entire length. Single as well as poly-crystalline copper wires
have been prepared by application of appropriate potential during the
EMD process. Scanning electron microscopy (SEM), high resolution
transmission electron microscopy (HRTEM), small angle electron
diffraction (SAED) and atomic force microscopy (AFM) were used
to characterize the synthesized nano wires at room temperature. The
electrochemical response of synthesized products was evaluated by
cyclic voltammetry while surface energy analysis was carried out
using a Goniometer.
Abstract: An ordered porous antimony-doped tin oxide (ATO) film was successfully prepared using a simple coating process with colloidal templates. The facile production was effective when a combination of 16-nm ATO (as a model of an inorganic nanoparticle) and polystyrene (PS) spheres (as a model of the template) weresimply coated to produce a composite ATO/PS film. Heat treatment was then used to remove the PS and produce the porous film. The porous film with a spherical pore shape and a highly ordered porous structure could be obtained. A potential way for the control of pore size could be also achieved by changing initial template size. The theoretical explanation and mechanism of porous formation were also added, which would be important for the scaling-up prediction and estimation.
Abstract: Titanium oxide films with different morphologies have for the first time been fabricated through hydrothermal reactions between a titanium substrate and iodine powder in water or ethanol. SEM revealed that iodine supported titanium (Ti-I2) surface shows different morphologies with variable treatment conditions. The mean surface roughness (Ra) was increased in the different groups. Use of surfactant has a role to increase the roughness of the film. The surface roughness was in the range of 0.15 μm-0.42 μm. Furthermore, the electrochemical examinations showed that the Ti-I2 surface fabricated in alcoholic medium has high corrosion resistance than in aqueous medium.
Abstract: In this paper, a fibre laser at 546 nm has been studied
for a signal power of -30 dB. Er3+-doped ZBLAN fibre has been used
by upconversion pumping of a 980 nm laser diode. Gain saturation
effect has been investigated in detail. Laser performance has also been
discussed. An efficiency of 35% has been calculated with a length of 5
mm fibre laser. Results show that Er3+-doped ZBLAN is a promising
candidate for optical amplification at 546 nm.
Abstract: In metal cutting industries, mathematical/statistical
models are typically used to predict tool replacement time. These
off-line methods usually result in less than optimum replacement
time thereby either wasting resources or causing quality problems.
The few online real-time methods proposed use indirect measurement
techniques and are prone to similar errors. Our idea is based on
identifying the optimal replacement time using an electronic nose to
detect the airborne compounds released when the tool wear reaches
to a chemical substrate doped into tool material during the
fabrication. The study investigates the feasibility of the idea, possible
doping materials and methods along with data stream mining
techniques for detection and monitoring different phases of tool
wear.
Abstract: A study concerning the photocatalytic decolourization
of Congo red (CR) dye, over artificial UV irradiation is presented.
Photocatalysts based on a commercial titanium dioxide (TiO2)
modified with transition metals (Ni, Cu and Zn) were used. The
dopage method used was wet impregnation. A TiO2 sample without
salt was subjected to the same hydrothermal treatment to be used as
reference. Congo red solutions to several pH conditions (natural and
basic) were used to evaluate photocatalytic performance of each
doped catalysts. Photodecolourization percentage was measured
spectrofotrometically after 3 h of treatment to 499 nm as response
variable. Kinetics investigations of photodegradation indicated that
reactions obey to Langmuir-Hinshelwood model and pseudo–first
order law. The rate constant studies of photocatalytic decolourization
reactions for Zn–TiO2 and Cu–TiO2 photocatalysts indicated that in
all cases the rate constant of the reaction was higher than that of TiO2
undoped. These results show that nature of the metal modifying the
TiO2 influence on the efficiency of the photocatalyst evaluated in
process. Ni does not present an additional effect compared with TiO2,
while Zn enhances the photoactivity due to its electronic properties.
Abstract: High Pressure Raman scattering measurements of KDP:Mn were performed at room temperatures. The X-ray powder diffraction patterns taken at room temperature by Rietveld refinement showed that doped samples of KDP-Mn have the same tetragonal structure of a pure KDP crystal, but with a contraction of the crystalline cell. The behavior of the Raman spectra, in particular the emergence of a new modes at 330 cm-1, indicates that KDP:Mn undergoes a structural phase transition with onset at around 4 GP. First principle density-functional theory (DFT) calculations indicate that tetrahedral rotation with pressure is predominantly around the c crystalline direction. Theoretical results indicates that pressure induced tetrahedral rotations leads to change tetrahedral neighborhood, activating librations/bending modes observed for high pressure phase of KDP:Mn with stronger Raman activity.
Abstract: Antimosy-doped tin oxide (ATO) particles were
prepared via chemical coprecipitation and reverse emulsion. The size
and size distribution of ATO particles were obviously decreased via
reverse microemulsion method. At the relatively high yield the ATO
particles were nearly spherical in shape, meanwhile the crystalline
structure and excellent conductivity were reserved, which could satisfy
the requirement as composite fillers, such as dielectric filler of
polyimide film.
Abstract: Titanium gels doped with water-soluble cationic porphyrin were synthesized by the sol–gel polymerization of Ti (OC4H9)4. In this work we investigate the spectroscopic properties along with SEM images of tetra carboxyl phenyl porphyrin when incorporated into porous matrix produced by the sol–gel technique.
Abstract: Three sulphonic acid-doped polyanilines were
synthesized through chemical oxidation at low temperature (0-5 oC)
and potential of these polymers as sensing agent for O2 gas detection
in terms of fluorescence quenching was studied. Sulphuric acid,
dodecylbenzene sulphonic acid (DBSA) and camphor sulphonic acid
(CSA) were used as doping agents. All polymers obtained were dark
green powder. Polymers obtained were characterized by Fourier
transform infrared spectroscopy, ultraviolet-visible absorption
spectroscopy, thermogravimetry analysis, elemental analysis,
differential scanning calorimeter and gel permeation
chromatography. Characterizations carried out showed that polymers
were successfully synthesized with mass recovery for sulphuric aciddoped
polyaniline (SPAN), DBSA-doped polyaniline (DBSA-doped
PANI) and CSA-doped polyaniline (CSA-doped PANI) of 71.40%,
75.00% and 39.96%, respectively. Doping level of SPAN, DBSAdoped
PANI and CSA-doped PANI were 32.86%, 33.13% and
53.96%, respectively as determined based on elemental analysis.
Sensing test was carried out on polymer sample in the form of
solution and film by using fluorescence spectrophotometer. Samples
of polymer solution and polymer film showed positive response
towards O2 exposure. All polymer solutions and films were fully
regenerated by using N2 gas within 1 hour period. Photostability
study showed that all samples of polymer solutions and films were
stable towards light when continuously exposed to xenon lamp for 9
hours. The relative standard deviation (RSD) values for SPAN
solution, DBSA-doped PANI solution and CSA-doped PANI
solution for repeatability were 0.23%, 0.64% and 0.76%,
respectively. Meanwhile RSD values for reproducibility were 2.36%,
6.98% and 1.27%, respectively. Results for SPAN film, DBSAdoped
PANI film and CSA-doped PANI film showed the same
pattern with RSD values for repeatability of 0.52%, 4.05% and
0.90%, respectively. Meanwhile RSD values for reproducibility were
2.91%, 10.05% and 7.42%, respectively. The study on effect of the
flow rate on response time was carried out using 3 different rates
which were 0.25 mL/s, 1.00 mL/s and 2.00 mL/s. Results obtained
showed that the higher the flow rate, the shorter the response time.
Abstract: Lanthanide-doped upconversion nanoparticles which can convert near-infrared lights to visible lights have attracted growing interest because of their great potentials in fluorescence imaging. Upconversion fluorescence imaging technique with excitation in the near-infrared (NIR) region has been used for imaging of biological cells and tissues. However, improving the detection sensitivity and decreasing the absorption and scattering in biological tissues are as yet unresolved problems. In this present study, a novel NIR-reflected multispectral imaging system was developed for upconversion fluorescent imaging in small animals. Based on this system, we have obtained the high contrast images without the autofluorescence when biocompatible UCPs were injected near the body surface or deeply into the tissue. Furthermore, we have extracted respective spectra of the upconversion fluorescence and relatively quantify the fluorescence intensity with the multispectral analysis. To our knowledge, this is the first time to analyze and quantify the upconversion fluorescence in the small animal imaging.
Abstract: The conventional production of biodiesel from crude
palm oil which contains large amounts of free fatty acids in the
presence of a homogeneous base catalyst confronts the problems of
soap formation and very low yield of biodiesel. To overcome these
problems, free fatty acids must be esterified to their esters in the
presence of an acid catalyst prior to alkaline-catalyzed
transesterification. Sulfated metal oxides are a promising group of
catalysts due to their very high acidity. In this research, aluminadoped
sulfated tin oxide (SO4
2-/Al2O3-SnO2) catalysts were prepared
and used for esterification of free fatty acids in crude palm oil in a
batch reactor. The SO4
2-/Al2O3-SnO2 catalysts were prepared from
different Al precursors. The results showed that different Al
precursors gave different activities of the SO4
2-/Al2O3-SnO2 catalysts.
The esterification of free fatty acids in crude palm oil with methanol
in the presence of SO4
2-/Al2O3-SnO2 catalysts followed first-order
kinetics.
Abstract: In this work, an organic compound 5,10,15,20-
Tetrakis(3,5-di-tertbutylphenyl)porphyrinatocopper(II) (TDTBPPCu)
is studied as an active material for thin film electronic devices. To
investigate the electrical properties of TDTBPPCu, junction of
TDTBPPCu with heavily doped n-Si and Al is fabricated.
TDTBPPCu film was sandwiched between Al and n-Si electrodes.
Various electrical parameters of TDTBPPCu are determined. The
current-voltage characteristics of the junction are nonlinear,
asymmetric and show rectification behavior, which gives the clue of
formation of depletion region. This behavior indicates the potential
of TDTBPPCu for electronics applications. The current-voltage and
capacitance-voltage techniques are used to find the different
electronic parameters.
Abstract: The technical realization of data transmission using
glass fiber began after the development of diode laser in year 1962.
The erbium doped fiber amplifiers (EDFA's) in high speed networks
allow information to be transmitted over longer distances without
using of signal amplification repeaters. These kinds of fibers are
doped with erbium atoms which have energy levels in its atomic
structure for amplifying light at 1550nm. When a carried signal wave
at 1550nm enters the erbium fiber, the light stimulates the excited
erbium atoms which pumped with laser beam at 980nm as additional
light. The wavelength and intensity of the semiconductor lasers
depend on the temperature of active zone and the injection current.
The present paper shows the effect of the diode lasers temperature
and injection current on the optical amplification. From the results of
in- and output power one may calculate the max. optical gain by
erbium doped fiber amplifier.
Abstract: Based on a theoretical erbium-doped fiber amplifier
(EDFA) model, we have proposed an application of disturbance
observer(DOB) with proportional/integral/differential(PID) controller
to EDFA for minimizing gain-transient time of wavelength
-division-multiplexing (WDM) multi channels in optical amplifier in
channel add/drop networks. We have dramatically reduced the
gain-transient time to less than 30μsec by applying DOB with PID
controller to the control of amplifier gain. The proposed DOB-based
gain control algorithm for EDFA was implemented as a digital control
system using TI's DSP(TMS320C28346) chip and experimental
results of the system verify the excellent performance of the proposed
gain control methodology.
Abstract: Samples of CoFe2-xCrxO4 where x varies from 0.0 to 0.5 were prepared by co-precipitation route. These samples were sintered at 750°C for 2 hours. These particles were characterized by X-ray diffraction (XRD) at room temperature. The FCC spinel structure was confirmed by XRD patterns of the samples. The crystallite sizes of these particles were calculated from the most intense peak by Scherrer formula. The crystallite sizes lie in the range of 37-60 nm. The lattice parameter was found decreasing upon substitution of Cr. DC electrical resistivity was measured as a function of temperature. The room temperature thermoelectric power was measured for the prepared samples. The magnitude of Seebeck coefficient depends on the composition and resistivity of the samples.
Abstract: Films of pure tin oxide SnO2 and in presence of
antimony atoms (SnO2-Sb) deposited onto glass substrates have
shown a sufficiently high energy gap to be transparent in the visible
region, a high electrical mobility and a carrier concentration which
displays a good electrical conductivity [1]. In this work, the effects of
polycrystalline silicon substrate on the optical properties of pure and
Sb doped tin oxide is investigated.
We used the APCVD (atmospheric pressure chemical vapour
deposition) technique, which is a low-cost and simple technique,
under nitrogen ambient, for growing this material. A series of SnO2
and SnO2-Sb have been deposited onto polycrystalline silicon
substrates with different contents of antimony atoms at the same
conditions of deposition (substrate temperature, flow oxygen,
duration and nitrogen atmosphere of the reactor). The effect of the
substrate in terms of morphology and nonlinear optical properties,
mainly the reflectance, was studied. The reflectance intensity of the
device, compared to the reflectance of tin oxide films deposited
directly on glass substrate, is clearly reduced on the overall
wavelength range. It is obvious that the roughness of the poly-c
silicon plays an important role by improving the reflectance and
hence the optical parameters.
A clear shift in the minimum of the reflectance upon doping level
is observed. This minimum corresponds to strong free carrier
absorption, resulting in different plasma frequency. This effect is
followed by an increase in the reflectance depending of the antimony
doping. Applying the extended Drude theory to the combining
optical and electrical obtained results these effects are discussed.
Abstract: A diamond-like carbon (DLC) based solid-lubricant
film was designed and DLC films were successfully prepared using a
microwave plasma enhanced magnetron sputtering deposition
technology. Post-test characterizations including Raman
spectrometry, X-ray diffraction, nano-indentation test, adhesion test,
friction coefficient test were performed to study the influence of
substrate bias voltage on the mechanical properties of the W- and
S-doped DLC films. The results indicated that the W- and S-doped
DLC films also had the typical structure of DLC films and a better
mechanical performance achieved by the application of a substrate
bias of -200V.
Abstract: Un-doped GaN film of thickness 1.90 mm, grown on
sapphire substrate were uniformly implanted with 325 keV Mn+ ions
for various fluences varying from 1.75 x 1015 - 2.0 x 1016 ions cm-2 at
3500 C substrate temperature. The structural, morphological and
magnetic properties of Mn ion implanted gallium nitride samples
were studied using XRD, AFM and SQUID techniques. XRD of the
sample implanted with various ion fluences showed the presence of
different magnetic phases of Ga3Mn, Ga0.6Mn0.4 and Mn4N.
However, the compositions of these phases were found to be
depended on the ion fluence. AFM images of non-implanted sample
showed micrograph with rms surface roughness 2.17 nm. Whereas
samples implanted with the various fluences showed the presence of
nano clusters on the surface of GaN. The shape, size and density of
the clusters were found to vary with respect to ion fluence. Magnetic
moment versus applied field curves of the samples implanted with
various fluences exhibit the hysteresis loops. The Curie temperature
estimated from zero field cooled and field cooled curves for the
samples implanted with the fluence of 1.75 x 1015, 1.5 x 1016 and 2.0
x 1016 ions cm-2 was found to be 309 K, 342 K and 350 K
respectively.