Abstract: An ordered porous antimony-doped tin oxide (ATO) film was successfully prepared using a simple coating process with colloidal templates. The facile production was effective when a combination of 16-nm ATO (as a model of an inorganic nanoparticle) and polystyrene (PS) spheres (as a model of the template) weresimply coated to produce a composite ATO/PS film. Heat treatment was then used to remove the PS and produce the porous film. The porous film with a spherical pore shape and a highly ordered porous structure could be obtained. A potential way for the control of pore size could be also achieved by changing initial template size. The theoretical explanation and mechanism of porous formation were also added, which would be important for the scaling-up prediction and estimation.
Abstract: spherical porous carbon particles with
controllable porosity with a mean size of 2.5m have been
prepared using a spray drying method with organic particle
colloidal template. As a precursor, a mixing solution of carbon
nanopowder and polystyrene (PS) particles as a template was
used. The result showed that the particles with a good porous
structure could be obtained. The pore size and shape (spherical)
were identical to the initial template, giving a potential way for
further developments. The control of particle porosity was also
possible and reported in this paper, in which this control could
be achieved by means of PS concentration.