Abstract: The complexity of lignocellulosic biomass requires
a pretreatment step to improve the yield of fermentable sugars. The
efficient pretreatment of corn cobs using microwave and potassium
hydroxide and enzymatic hydrolysis was investigated. The
objective of this work was to characterize the optimal condition of
pretreatment of corn cobs using microwave and potassium
hydroxide enhance enzymatic hydrolysis. Corn cobs were
submerged in different potassium hydroxide concentration at varies
temperature and resident time. The pretreated corn cobs were
hydrolyzed to produce the reducing sugar for analysis. The
morphology and microstructure of samples were investigated by
Thermal gravimetric analysis (TGA, scanning electron microscope
(SEM), X-ray diffraction (XRD). The results showed that lignin
and hemicellulose were removed by microwave/potassium
hydroxide pretreatment. The crystallinity of the pretreated corn
cobs was higher than the untreated. This method was compared
with autoclave and conventional heating method. The results
indicated that microwave-alkali treatment was an efficient way to
improve the enzymatic hydrolysis rate by increasing its
accessibility hydrolysis enzymes.
Abstract: This research study the application of the immobilized
TiO2 layer and Cu-TiO2 layer on graphite substrate as a negative
electrode or anode for Li-ion battery. The titania layer was produced
through chemical bath deposition method, meanwhile Cu particles
were deposited electrochemically. A material can be used as an
electrode as it has capability to intercalates Li ions into its crystal
structure. The Li intercalation into TiO2/Graphite and Cu-
TiO2/Graphite were analyzed from the changes of its XRD pattern
after it was used as electrode during discharging process. The XRD
patterns were refined by Le Bail method in order to determine the
crystal structure of the prepared materials. A specific capacity and the
cycle ability measurement were carried out to study the performance
of the prepared materials as negative electrode of the Li-ion battery.
The specific capacity was measured during discharging process from
fully charged until the cut off voltage. A 300 was used as a load.
The result shows that the specific capacity of Li-ion battery with
TiO2/Graphite as negative electrode is 230.87 ± 1.70mAh.g-1 which is
higher than the specific capacity of Li-ion battery with pure graphite
as negative electrode, i.e 140.75 ±0.46mAh.g-1. Meanwhile
deposition of Cu onto TiO2 layer does not increase the specific
capacity, and the value even lower than the battery with
TiO2/Graphite as electrode. The cycle ability of the prepared battery
is only two cycles, due to the Li ribbon which was used as cathode
became fragile and easily broken.
Abstract: Protective clothing limits heat transfer and hampers
task performance due to the increased weight. Militarism protective
clothing enables humans to operate in adverse environments. In the
selection and evaluation of militarism protective clothing attention
should be given to heat strain, ergonomic and fit issues next to the
actual protection it offers.
Fifty Male healthy subjects participated in the study. The subjects
were dressed in shorts, T-shirts, socks, sneakers and four deferent
kinds of militarism protective clothing such as CS, CSB, CS with
NBC protection and CS with NBC- protection added.
Ergonomically and psychological strains of every four cloths were
investigated on subjects by walking on a treadmill (7km/hour) with a
19.7 kg backpack. As a result of these tests were showed that, the
highest heart rate was found wearing the NBC-protection added
outfit, the highest temperatures were observed wearing NBCprotection
added, followed by respectively CS with NBC protection,
CSB and CS and the highest value for thermal comfort (implying
worst thermal comfort) was observed wearing NBC-protection
added.
Abstract: The recovery of metal values and safe disposal of
spent catalyst is gaining interest due to both its hazardous nature and
increased regulation associated with disposal methods. Prior to the
recovery of the valuable metals, removal of entrained deposits limit
the diffusion of lixiviate resulting in low recovery of metals must be
taken into consideration. Therefore, petroleum refinery spent catalyst
was subjected to acetone washing and roasting at 500oC. The treated
samples were investigated for metals bioleaching using
Acidithiobacillus ferrooxidans in batch reactors and the leaching
efficiencies were compared. It was found out that acetone washed
spent catalysts results in better metal recovery compare to roasted
spent. About 83% Ni, 20% Al, 50% Mo and 73% V were leached
using the acetone washed spent catalyst. In both the cases, Ni, V and
Mo was high compared to Al.
Abstract: Renewable energy sources have gained ultimate urgency due to the need of the preservation of the environment for a sustainable development. Pyrolysis is an ultimate promising process in the recycling and acquisition of precious chemicals from wastes. Here, the co-pyrolysis of hazelnut shell with ultra-high molecular weight polyethylene was carried out catalytically and noncatalytically at 500 and 650 ºC. Potassium dichromate was added in certain amounts to act as a catalyst. The liquid, solid and gas products quantities were determined by gravimetry. As a main result, remarkable increases in gasification were observed by using this catalyst for pure components and their blends especially at 650 ºC. The increase in gas product quantity was compensated mainly with the decreases in the solid products and additionally in some cases liquid products quantities. These observations may stem from mainly the activation of carbon-carbon bonds rather than carbon-hydrogen bonds via potassium dichromate. Also, the catalytic effect of potassium dichromate on HS: PEO and HS: UHMWPE co-pyrolysis was compared.
Abstract: The special and unique advantages of explosive
forming, has developed its use in different industries. Considering the
important influence of improving the current explosive forming
techniques on increasing the efficiency and control over the
explosive forming procedure, the effects of air and water as the
energy-conveying medium, and also their differences will be
illustrated in this paper. Hence, a large number of explosive forming
tests have been conducted on two sizes of thin walled cylindrical
shells by using air and water as the working medium. Comparative
diagrams of the maximum radial deflection of work-pieces of the
same size, as a function of the scaled distance, show that for the
points with the same values of scaled distance, the maximum radial
deformation caused by the under water explosive loading is 4 to 5
times more than the deflection of the shells under explosive forming,
while using air. Results of this experimental research have also been
compared with other studies which show that using water as the
energy conveying media increases the efficiency up to 4.8 times. The
effect of the media on failure modes of the shells, and the necking
mechanism of the walls of the specimens, while being explosively
loaded, are also discussed in this issue. Measuring the tested
specimens shows that, the increase in the internal volume has been
accompanied by necking of the walls, which finally results in the
radial rupture of the structure.
Abstract: Mapping between local and global coordinates is an
important issue in finite element method, as all calculations are
performed in local coordinates. The concern arises when subparametric
are used, in which the shape functions of the field variable
and the geometry of the element are not the same. This is particularly
the case for C* elements in which the extra degrees of freedoms
added to the nodes make the elements sub-parametric. In the present
work, transformation matrix for C1* (an 8-noded hexahedron
element with 12 degrees of freedom at each node) is obtained using
equivalent C0 elements (with the same number of degrees of
freedom). The convergence rate of 8-noded C1* element is nearly
equal to its equivalent C0 element, while it consumes less CPU time
with respect to the C0 element. The existence of derivative degrees
of freedom at the nodes of C1* element along with excellent
convergence makes it superior compared with it equivalent C0
element.
Abstract: The nature of adsorbed species on catalytic surface
over an industrial precipitated iron-based high temperature catalyst
during FTS was investigated by in-situ DRIFTS and chemical
trapping. The formulation of the mechanism of oxygenates formation
and key intermediates were also discussed. Numerous oxygenated
precursors and crucial intermediates were found by in-situ DRIFTS,
such as surface acetate, acetyl and methoxide. The results showed that
adsorbed molecules on surface such as methanol or acetaldehyde
could react with basic sites such as lattice oxygen or free surface
hydroxyls. Adsorbed molecules also had reactivity of oxidizing.
Moreover, acetyl as a key intermediate for oxygenates was observed
by investigation of CH3OH + CO and CH3I + CO + H2. Based on the
nature of surface properties, the mechanism of oxygenates formation
on precipitated iron-based high temperature catalyst was discussed.
Abstract: The desulfurization of coal using biological methods is an emerging technology. The biodesulfurization process uses the catalytic activity of chemolithotrophic acidpohiles in removing sulfur and pyrite from the coal. The present study was undertaken to examine the potential of Acidithiobacillus ferrooxidans in removing the pyritic sulfur and iron from high iron and sulfur containing US coal. The experiment was undertaken in 10 L batch stirred tank reactor having 10% pulp density of coal. The reactor was operated under mesophilic conditions and aerobic conditions were maintained by sparging the air into the reactor. After 35 days of experiment, about 64% of pyrite and 21% of pyritic sulfur was removed from the coal. The findings of the present study indicate that the biodesulfurization process does have potential in treating the high pyrite and sulfur containing coal. A good mass balance was also obtained with net loss of about 5% showing its feasibility for large scale application.
Abstract: Many applications require surface modification and
micro-structuring of polymers. For these purposes is mainly used
ultraviolet (UV) radiation from excimer lamps or excimer lasers.
However, these sources have a decided disadvantage - degrading the
polymer deep inside due to relatively big radiation penetration depth
which may exceed 100 μm. In contrast, extreme ultraviolet (EUV)
radiation is absorbed in a layer approximately 100 nm thick only. In
this work, the radiation from a discharge-plasma EUV source (with
wavelength 46.9 nm) based on a capillary discharge driver is focused
with a spherical Si/Sc multilayer mirror for surface modification of
PMMA sample or thin gold layer (thickness about 40 nm). It was
found that the focused EUV laser beam is capable by one shot to
ablate PMMA or layer of gold, even if the focus is significantly
influenced by astigmatism.
Abstract: This paper presents the experimental results of silicone rubber outdoor polymer insulators in salt fog ageing test based on IEC 61109. Specimens made ofHTV silicone rubber with ATH content having three different configurations, straight shedsalternated sheds, and incline and alternate sheds, were tested continuously 1000 hrs.in artificial salt fog chamber. Contamination level, reduction of hydrophobicity and hardness measurement were used as physical damaged inspection techniques to evaluate degree of surface deterioration. In addition, chemical changing of tested specimen surface was evaluated by ATR-FTIRto confirm physical damaged inspection. After 1000 hrs.of salt fog test, differences in degree of surface deterioration were observed on all tested specimens. Physical damaged inspection and chemical analysis results confirmed the experimental results as well.
Abstract: Gold coated silica core nanoparticles have an optical
response dictated by the plasmon resonance. The wavelength at
which the resonance occurs depends on the core and shell sizes,
allowing nanoshells to be tailored for particular applications. The
purposes of this study was to synthesize and use different
concentration of gold nanoshells as exogenous material for skin
tissue soldering and also to examine the effect of laser soldering
parameters on the properties of repaired skin. Two mixtures of
albumin solder and different concentration of gold nanoshells were
prepared. A full thickness incision of 2×20 mm2 was made on the
surface and after addition of mixtures it was irradiated by an 810nm
diode laser at different power densities. The changes of tensile
strength σt due to temperature rise, number of scan (Ns), and scan
velocity (Vs) were investigated. The results showed at constant laser
power density (I), σt of repaired incisions increases by increasing the
concentration of gold nanoshells, Ns and decreasing Vs. It is therefore
important to consider the trade off between the scan velocity and the
surface temperature for achieving an optimum operating condition. In
our case this corresponds to σt =1610 gr/cm2 at I~ 60 Wcm-2, T ~
65ºC, Ns =10 and Vs=0.2mms-1.
Abstract: Wetting characteristics of reactive (Sn–0.7Cu solder)
and non– reactive (castor oil) wetting of liquids on Cu and Ag plated
Al substrates have been investigated. Solder spreading exhibited
capillary, gravity and viscous regimes. Oils did not exhibit noticeable
spreading regimes. Solder alloy showed better wettability on Ag
coated Al substrate compared to Cu plating. In the case of castor oil,
Cu coated Al substrate exhibited good wettability as compared to Ag
coated Al substrates. The difference in wettability during reactive
wetting of solder and non–reactive wetting of oils is attributed to the
change in the surface energies of Al substrates brought about by the
formation of intermetallic compounds (IMCs).
Abstract: The nickel and gold nanoclusters as supported
catalysts were analyzed by XAS, XRD and XPS in order to
determine their local, global and electronic structure. The present
study has pointed out a strong deformation of the local structure of
the metal, due to its interaction with oxide supports. The average
particle size, the mean squares of the microstrain, the particle size
distribution and microstrain functions of the supported Ni and Au
catalysts were determined by XRD method using Generalized Fermi
Function for the X-ray line profiles approximation. Based on EXAFS
analysis we consider that the local structure of the investigated
systems is strongly distorted concerning the atomic number pairs.
Metal-support interaction is confirmed by the shape changes of the
probability densities of electron transitions: Ni K edge (1s →
continuum and 2p), Au LIII-edge (2p3/2 → continuum, 6s, 6d5/2 and
6d3/2). XPS investigations confirm the metal-support interaction at
their interface.
Abstract: This paper describes a steady state model of a multiple
effect evaporator system for simulation and control purposes. The
model includes overall as well as component mass balance equations,
energy balance equations and heat transfer rate equations for area
calculations for all the effects. Each effect in the process is
represented by a number of variables which are related by the energy
and material balance equations for the feed, product and vapor flow
for backward, mixed and split feed. For simulation 'fsolve' solver in
MATLAB source code is used. The optimality of three sequences i.e.
backward, mixed and splitting feed is studied by varying the various
input parameters.
Abstract: Two different superhydrophobic surfaces were
elaborated and their oil repellency behavior was evaluated using
several liquid with different surface tension. A silicone rubber/SiO2
nanocomposite coated (A) on aluminum substrate by “spin-coating"
and the sample B was an anodized aluminum surface covered by
Teflon-like coating. A high static contact angle about ∼162° was
measured for two prepared surfaces on which the water droplet rolloff.
Scanning electron microscopy (SEM) showed the presence of
micro/nanostructures for both sample A and B similar to that of lotus
leaf.
However the sample A presented significantly different behaviour
of wettability against the low surface tension liquid. Sample A has
been wetted totally by oil (dodecan) droplet while sample B showed
oleophobic behaviour. Oleophobic property of Teflon like coating
can be contributed to the presence of CF2 and CF3 functional group
which was shown by XPS analysis.
Abstract: ZnO-SnO2 i.e. Zinc-Tin-Oxide (ZTO) thin films were
deposited on glass substrate with varying concentrations (ZnO:SnO2
- 100:0, 90:10, 70:30 and 50:50 wt.%) at room temperature by flash
evaporation technique. These deposited ZTO film were annealed at
450 0C in vacuum. These films were characterized to study the effect
of annealing on the structural, electrical, and optical properties.
Atomic force microscopy (AFM) and Scanning electron microscopy
(SEM) images manifest the surface morphology of these ZTO thin
films. The apparent growth of surface features revealed the formation
of nanostructure ZTO thin films. The small value of surface
roughness (root mean square RRMS) ensures the usefulness in
optical coatings. The sheet resistance was also found to be decreased
for both types of films with increasing concentration of SnO2. The
optical transmittance found to be decreased however blue shift has
been observed after annealing.
Abstract: This study describes the preparation of a novel proton
conducting membranes based on bacterial cellulose (BC) modified by
grafting of 2-acrylamido-2-methyl-1 -propanesulfonic acid (AMPS)
through UV-induced graft polymerization. These AMPS-g-BC
membranes have been characterized by various techniques including
FTIR, SEM and TGA, to find their successful grafting of AMPS on
BC, surface morphology and thermal stability, respectively. Physical
properties of AMPS-g-BC membranes have been assessed in terms of
Lamda value( λ ), ion exchange capacity(IEC) and proton
conductivity. The relationship between degree of grafting and AMPS
concentration used for grafting has been determined by weight gain
method. An optimum proton conductivity equal to 2.89x10-2 S cm-1
and IEC value equal to 1.79 mmol g-1 have been obtained when 20
wt% AMPS concentration is used for grafting (i.e. the corresponding
membrane is notated as AMPS20-g-BC).
Abstract: Aluminum alloy has an extensive range of industrial application due to its consistent mechanical properties and structural integrity. The heat treatment by precipitation technique affected the Magnesium, Silicon Manganese and copper crystals dissolved in the Aluminum alloy. The crystals dislocated to precipitate on the crystal’s boundaries of the Aluminum alloy when given a thermal energy increased its hardness. In this project various times and temperature were varied to find out the best combination of these variables to increase the precipitation of the metals on the Aluminum crystal’s boundaries which will lead to get the highest hardness. These specimens are then tested for their hardness and tensile strength. It is noticed that when the temperature increases, the precipitation increases and consequently the hardness increases. A threshold temperature value (264C0) of Aluminum alloy should not be reached due to the occurrence of recrystalization which causes the crystal to grow. This recrystalization process affected the ductility of the alloy and decrease hardness. In addition, and while increasing the temperature the alloy’s mechanical properties will decrease. The mechanical properties, namely tensile and hardness properties are investigated according to standard procedures. In this research, different temperature and time have been applied to increase hardening.The highest hardness at 100°c in 6 hours equals to 207.31 HBR, while at the same temperature and time the lowest elongation equals to 146.5.
Abstract: Renewable natural fibres such as oil palm, flax, and
pineapple leaf can be utilized to obtain new high performance
polymer materials. The reuse of waste natural fibres as reinforcement
for polymer is a sustainable option to the environment. However, due
to its high hydroxyl content of cellulose, natural fibres are
susceptible to absorb water that affects the composite mechanical
properties adversely. Research found that Nano materials such as
Nano Silica Carbide (n-SiC) and Nano Clay can be added into the
polymer composite to overcome this problem by enhancing its
mechanical properties in wet condition. The addition of Nano
material improves the tensile and wear properties, flexural stressstrain
behaviour, fracture toughness, and fracture strength of polymer
natural composites in wet and dry conditions.