Abstract: Titanium and its alloys have become more significant implant materials due to their mechanical properties, excellent biocompatibility and high corrosion resistance. Biomaterials can be produce by using the powder metallurgy (PM) methods and required properties can tailored by varying the processing parameters, such as ball milling time, space holder particles, and sintering temperature. The desired properties such as, structural and mechanical properties can be obtained by powder metallurgy method. In the present study, deals with fabrication of solid and porous Ti-20Nb-5Ag alloy using high energy ball milling for different times (5 and 20 h). The resultant powder particles were used to fabricate solid and porous Ti-20Nb-5Ag alloy by adding space holder particles (NH4HCO3). The resultant powder particles, fabricated solid and porous samples were characterized by scanning electron microscopy (SEM). The compressive strength, elastic modulus and microhardness properties were investigated. Solid and porous Ti-20Nb-5Ag alloy samples showed good mechanical properties for 20 h ball milling time as compare to 5 h ball milling.
Abstract: Intermetallic materials are among advanced
technology materials that have outstanding mechanical and physical
properties for high temperature applications. Especially creep
resistance, low density and high hardness properties stand out in such
intermetallics. The microstructure, mechanical properties of %88Ni-
%10Cr and %2Mn powders were investigated using specimens
produced by tube furnace sintering at 900-1300°C temperature. A
composite consisting of ternary additions, a metallic phase, Fe, Cr
and Mn have been prepared under Ar shroud and then tube furnace
sintered. XRD, SEM (Scanning Electron Microscope), were
investigated to characterize the properties of the specimens.
Experimental results carried out for composition %88Ni-%10Cr and
%2Mn at 1300°C suggest that the best properties as 138,80HV and
6,269/cm3 density were obtained at 1300°C.
Abstract: Sustainability and eco-friendly requirement of
engineering materials are sort for in recent times, thus giving rise to
the development of bio-composites. However, the natural fibres to
matrix interface interactions remain a key issue in getting the desired
mechanical properties from such composites. Treatment of natural
fibres is essential in improving matrix to filler adhesion, hence
improving its mechanical properties. In this study, investigations
were carried out to determine the effect of sodium hydroxide
treatment on the tensile, flexural, impact and hardness properties of
crushed and uncrushed Luffa cylindrica fibre reinforced recycled low
density polyethylene composites. The LC (Luffa cylindrica) fibres
were treated with 0%, 2%, 4%, 6%, 8% and 10% wt. sodium
hydroxide (NaOH) concentrations for a period of 24 hours under
room temperature conditions. A formulation ratio of 80/20 g (matrix
to reinforcement) was maintained for all developed samples. Analysis
of the results showed that the uncrushed luffa fibre samples gave
better mechanical properties compared with the crushed luffa fibre
samples. The uncrushed luffa fibre composites had a maximum
tensile and flexural strength of 7.65 MPa and 17.08 Mpa respectively
corresponding to a young modulus and flexural modulus of 21.08
MPa and 232.22 MPa for the 8% and 4% wt. NaOH concentration
respectively. Results obtained in the research showed that NaOH
treatment with the 8% NaOH concentration improved the mechanical
properties of the LC fibre reinforced composites when compared with
other NaOH treatment concentration values.
Abstract: Aluminum alloy has an extensive range of industrial application due to its consistent mechanical properties and structural integrity. The heat treatment by precipitation technique affected the Magnesium, Silicon Manganese and copper crystals dissolved in the Aluminum alloy. The crystals dislocated to precipitate on the crystal’s boundaries of the Aluminum alloy when given a thermal energy increased its hardness. In this project various times and temperature were varied to find out the best combination of these variables to increase the precipitation of the metals on the Aluminum crystal’s boundaries which will lead to get the highest hardness. These specimens are then tested for their hardness and tensile strength. It is noticed that when the temperature increases, the precipitation increases and consequently the hardness increases. A threshold temperature value (264C0) of Aluminum alloy should not be reached due to the occurrence of recrystalization which causes the crystal to grow. This recrystalization process affected the ductility of the alloy and decrease hardness. In addition, and while increasing the temperature the alloy’s mechanical properties will decrease. The mechanical properties, namely tensile and hardness properties are investigated according to standard procedures. In this research, different temperature and time have been applied to increase hardening.The highest hardness at 100°c in 6 hours equals to 207.31 HBR, while at the same temperature and time the lowest elongation equals to 146.5.