Substantial Fatigue Similarity of a New Small-Scale Test Rig to Actual Wheel-Rail System

The substantial similarity of fatigue mechanism in a
new test rig for rolling contact fatigue (RCF) has been investigated. A
new reduced-scale test rig is designed to perform controlled RCF
tests in wheel-rail materials. The fatigue mechanism of the rig is
evaluated in this study using a combined finite element-fatigue
prediction approach. The influences of loading conditions on fatigue
crack initiation have been studied. Furthermore, the effects of some
artificial defects (squat-shape) on fatigue lives are examined. To
simulate the vehicle-track interaction by means of the test rig, a threedimensional
finite element (FE) model is built up. The nonlinear
material behaviour of the rail steel is modelled in the contact
interface. The results of FE simulations are combined with the critical
plane concept to determine the material points with the greatest
possibility of fatigue failure. Based on the stress-strain responses, by
employing of previously postulated criteria for fatigue crack initiation
(plastic shakedown and ratchetting), fatigue life analysis is carried
out. The results are reported for various loading conditions and
different defect sizes. Afterward, the cyclic mechanism of the test rig
is evaluated from the operational viewpoint. The results of fatigue
life predictions are compared with the expected number of cycles of
the test rig by its cyclic nature. Finally, the estimative duration of the
experiments until fatigue crack initiation is roughly determined.





References:
[1] E.E. Magel, “Rolling Contact Fatigue: A Comprehensive Review”,
Report, DOT/FRA/ORD-11/24, Federal Railroad Administration, 2011.
[2] D.T. Eadie, D. Elvidge, K. Oldknow, R. Stock, P. Pointner, J. Kalousek,
P. Klauser, “The effects of top of rail friction modifier on wear and
rolling contact fatigue: Full-scale fail-wheel test rig evaluation, analysis
and modelling,” Wear, vol. 265 (2008) pp. 1222-1230.
[3] U. Olofsson, T. Telliskivi, “Wear, plastic deformation and friction of
two rail steels—a full-scale test and a laboratory study”, Wear, vol. 254
(2003) pp. 80-93.
[4] J.H. Beynon, J.E. Garnham, K.J. Sawley, “Rolling contact fatigue of
three pearlitic rail steels”, Wear, vol. 192 (1996) pp. 94-111.
[5] W.R. Tyfour, J.H. Beynon, A. Kapoor, “Deterioration of rolling contact
fatigue life of pearlitic rail steel due to dry-wet rolling-sliding line
contact”, Wear, vol. 197 (1996) pp. 255-265.
[6] R.I. Carroll, J.H. Beynon, “Decarburisation and rolling contact fatigue of
a rail steel”, Wear, vol. 260 (2006) pp. 523-537.
[7] G. Donzella, A. Mazzu, C. Petrogalli, “Competition between wear and
rolling contact fatigue at the wheel-rail interface: some experimental
evidence on rail steel”, IMech. Part F, J Rai, vol. 223 (2009) pp. 31-44.
[8] J. Seo, S. Kwon, H. Jun, D. Lee, Rolling contact fatigue of white etching
layer on pearlite steel rail, Key Eng Mat, vol. 417-418 (2010) 309-312.
[9] S. Pal, C. Valente, W. Daniel, M. Farjoo, “Metallurgical and physical
understanding of rail squat initiation and propagation”, Wear, vol. 284
(2012) pp. 30-42.
[10] D. Scott, J. Blackwell, “NEL rolling contact tests—accelerated service
simulation tests for lubricants and materials for rolling elements”, Wear,
vol. 17 (1971) pp. 323-333.
[11] O. Zwirlein, H. Schlicht, “Rolling contact fatigue mechanisms—
accelerated testing versus field performance, Rolling contact fatigue
testing of bearing steels”, vol. 771 (1982) pp. 358-379.
[12] J.J. Hoo, “Rolling Contact Fatigue Testing of Bearing Steels: A
Symposium”, ASTM International, 1982.
[13] S. Ito, N. Tsushima, H. Muro, “Accelerated rolling contact fatigue test
by a cylinder-to-ball rig”, Rolling Contact Fatigue Testing of Bearing
Steels, (1982) pp. 125-135.
[14] D. Glover, “A ball-rod rolling contact fatigue tester, Rolling Contact”
Fatigue Testing of Bearing Steels, ASTM STP, 771 (1982) pp. 107-125.
[15] J. Ciruna, H. Szieleit, “The effect of hydrogen on the rolling contact
fatigue life of AISI 52100 and 440C steel balls”, Wear, vol. 24 (1973)
107-118.
[16] E.A. Gallardo-Hernandez, R. Lewis, R.S. Dwyer-Joyce, Temperature in
a twin-disc wheel/rail contact simulation, Tribology International, vol.
39 (2006) pp. 1653-1663.
[17] E. Gallardo-Hernandez, R. Lewis, “Twin disc assessment of wheel/rail
adhesion”, Wear, vol. 265 (2008) pp. 1309-1316.
[18] M. Takikawa, Y. Iriya, “Laboratory simulations with twin-disc machine
on head check”, Wear, vol. 265 (2008) pp. 1300-1308.
[19] J.E. Garnham, C.L. Davis, “The role of deformed rail microstructure on
rolling contact fatigue initiation”, Wear, vol. 265 (2008) pp. 1363-1372.
[20] W.J. Wang, W. Zhong, J. Guo, Q.Y. Liu, “Investigation on rolling
contact fatigue and wear properties of railway rail”, Advanced
Tribology, (2009) pp. 327-328.
[21] W. Zhong, J.J. Hu, P. Shen, C.Y. Wang, Q.Y. Lius, “Experimental
investigation between rolling contact fatigue and wear of high-speed and
heavy-haul railway and selection of rail material”, Wear, vol. 271 (2011)
pp. 2485-2493.
[22] E. Kabo, A. Ekberg, P. Torstensson, T. Vernersson, “Rolling contact
fatigue prediction for rails and comparisons with test rig results”, Proc.
IMech., Part F: J Rail and Rapid Transit, vol. 224 (2010) pp. 303-317.
[23] J.W. Ringsberg, “Life prediction of rolling contact fatigue crack
initiation”, International J fatigue, vol. 23 (2001) pp. 575-586.
[24] K. Johnson, “The strength of surfaces in rolling contact”, Proc. IMech.,
Part C: J Mechanical Engineering Science, vol. 203 (1989) pp. 151-163.
[25] J. Ringsberg, M. Loo-Morrey, B. Josefson, A. Kapoor, J.H. Beynon,
“Prediction of fatigue crack initiation for rolling contact fatigue”,
International J Fatigue, vol. 22 (2000) pp. 205-215.
[26] U. Zerbst, R. Lundén, K.O. Edel, R.A. Smith, “Introduction to the
damage tolerance behaviour of railway rails – a review”, Engineering
Fracture Mechanics, vol. 76 (2009) pp. 2563-2601.
[27] B.R. You, S.B. Lee, A critical review on multiaxial fatigue assessments
of metals, International J Fatigue, vol. 18 (1996) pp. 235-244.
[28] J. Das, S. Sivakumar, “An evaluation of multiaxial fatigue life
assessment methods for engineering components”, International J
Pressure Vessels and Piping, vol. 76 (1999) pp. 741-746.
[29] J. Ringsberg, B. Josefson, “Finite element analyses of rolling contact
fatigue crack initiation in railheads”, Proc. IMech., Part F: J Rail and
Rapid Transit, vol. 215 (2001) pp. 243-259.
[30] A. Ekberg, E. Kabo, “Fatigue of railway wheels and rails under rolling
contact and thermal loading—an overview”, Wear, vol. 258 (2005) pp.
1288-1300.
[31] Y. Jiang, H. Sehitoglu, “A model for rolling contact failure”, Wear, vol.
224 (1999) pp. 38-49.
[32] Y. Jiang, “A fatigue criterion for general multiaxial loading, Fatigue and
fracture of engineering materials and structures”, 23 (2000) pp. 19-32.
[33] A. Kapoor, “A re-evaluation of the life to rupture of ductile metals by
cyclic plastic strain”, Fatigue & fracture of engineering materials &
structures, vol. 17 (1994) pp. 201-219.
[34] J. Bannantine, “Fundamentals of metal fatigue analysis”, Prentice Hall,
1990, (1990) 273.
[35] K. Smith, T. Topper, P. Watson, “A stress-strain function for the fatigue
of metals (Stress-strain function for metal fatigue including mean stress
effect)”, J materials, vol. 5 (1970) pp. 767-778.
[36] D. Socie, “Multiaxial fatigue damage models”, J Engineering Materials
and Technology, vol. 109 (1987) pp. 293-298.
[37] J. Ringsberg, “Rolling contact fatigue of railway rails with emphasis on
crack initiation”, Chalmers University of Technology, 2000.
[38] A. Jaschinski, H. Chollet, S. Iwnicki, A. Wickens, J. Würzen, “The
application of roller rigs to railway vehicle dynamics”, Vehicle System
Dynamics, vol. 31 (1999) pp. 345-392.
[39] T. Armstrong, D. Thompson, “Use of a reduced scale model for the
study of wheel/rail interaction”, Proc. IMech., Part F: J Rail and Rapid
Transit, vol. 220 (2006) pp. 235-246.
[40] X. Zhao, Z. Li, “The solution of frictional wheel–rail rolling contact
with a 3D transient finite element model: Validation and error analysis”,
Wear, vol. 271 (2011) pp. 444-452.
[41] J. Hallquist, “LS-DYNA Theoretical Manual”, in, Livermore Software
Technology Corporation: Livermore, California, 1998.
[42] J.-L. Chaboche, “Constitutive equations for cyclic plasticity and cyclic
viscoplasticity”, International J Plasticity, vol. 5 (1989) pp. 247-302.
[43] J. Lemaitre, J.-L. Chaboche, Mechanics of solid materials, Cambridge
University Press, 1990.
[44] J.W. Ringsberg, “Cyclic ratchetting and failure of a pearlitic rail steel”,
Fatigue & Fracture of Engineering Materials & Structures, vol. 23
(2000) 747-758.
[45] M. Akama, H. Matsuda, H. Doi, M. Tsujie, “Fatigue crack initiation life
prediction of rails using theory of critical distance and critical plane
approach”, J Comp. Science and Technology, vol. 6 (2012) pp. 54-69.
[46] X. Zhao, Z. Li, J. Liu, “Wheel–rail impact and the dynamic forces at
discrete supports of rails in the presence of singular rail surface defects”,
Proc. IMech., Part F: J Rail and Rapid Transit, 226 (2012) pp. 124-139.
[47] Z. Li, X. Zhao, C. Esveld, R. Dollevoet, M. Molodova, “An
investigation into the causes of squats—correlation analysis and
numerical modeling”, Wear, vol. 265 (2008) pp. 1349-1355.
[48] Z. Li, R. Dollevoet, M. Molodova, X. Zhao, “Squat growth—Some
observations and the validation of numerical predictions”, Wear, vol.
271 (2011) pp. 148-157.