Delamination Fracture Toughness Benefits of Inter-Woven Plies in Composite Laminates Produced through Automated Fibre Placement

An automated fibre placement method has been
developed to build through-thickness reinforcement into carbon fibre
reinforced plastic laminates during their production, with the goal
of increasing delamination fracture toughness while circumventing
the additional costs and defects imposed by post-layup stitching
and z-pinning. Termed ‘inter-weaving’, the method uses custom
placement sequences of thermoset prepreg tows to distribute regular
fibre link regions in traditionally clean ply interfaces. Inter-weaving’s impact on mode I delamination fracture toughness
was evaluated experimentally through double cantilever beam tests
(ASTM standard D5528-13) on [±15°]9 laminates made from Park
Electrochemical Corp. E-752-LT 1/4” carbon fibre prepreg tape.
Unwoven and inter-woven automated fibre placement samples were
compared to those of traditional laminates produced from standard
uni-directional plies of the same material system. Unwoven automated fibre placement laminates were found to
suffer a mostly constant 3.5% decrease in mode I delamination
fracture toughness compared to flat uni-directional plies. Inter-weaving caused significant local fracture toughness increases
(up to 50%), though these were offset by a matching overall
reduction. These positive and negative behaviours of inter-woven
laminates were respectively found to be caused by fibre breakage
and matrix deformation at inter-weave sites, and the 3D layering
of inter-woven ply interfaces providing numerous paths of least
resistance for crack propagation.

Authors:

• Jayden Levy
• Garth M. K. Pearce

Keywords:

• AFP
• automated fibre placement
• delamination
• fracture toughness
• inter-weaving.

References:

[1] R. P. Taylor, Fibre composite aircraft - capability and safety. Australian
Transport Safety Bureau, 1 ed., 2008.
[2] Z. Aslan and F. Daricik, “Effects of multiple delaminations on the
compressive, tensile, flexural, and buckling behaviour of e-glass/epoxy
composites,” Composites Part B: Engineering, vol. 100, pp. 186–196,
Sep. 2016.
[3] H. Chai, “The characterization of mode i delamination failure
in non-woven, multidirectional laminates,” Composites, vol. 15,
pp. 277–290, Oct. 1984.
[4] M. B. M. Rehan, J. Rousseau, S. Fontaine, and X. Gong, “Experimental
study of the influence of ply orientation on DCB mode-i delamination
behavior by using multidirectional fully isotropic carbon/epoxy
laminates,” Composite Structures, vol. 161, pp. 1–7, Feb. 2017.
[5] J.-K. Kim and M.-L. Sham, “Impact and delamination failure of
woven-fabric composites,” Composites Science and Technology, vol. 60,
pp. 745–761, Apr. 2000.
[6] D. Nicholls and J. Gallagher, “Determination of GIC in angle ply
composites using a cantilever beam test method,” Journal of Reinforced
Plastics and Composites, vol. 2, pp. 2–17, Jan. 1983.
[7] I. Herszberg, M. K. Bannister, K. H. Leong, and P. J. Falzon, “Research
in textile composites at the cooperative research centre for advanced
composite structures,” Journal of the Textile Institute, vol. 88, pp. 52–73,
Jan. 1997.
[8] A. Mouritz, K. Leong, and I. Herszberg, “A review of the effect
of stitching on the in-plane mechanical properties of fibre-reinforced
polymer composites,” Composites Part A: Applied Science and
Manufacturing, vol. 28, pp. 979–991, Jan. 1997. [9] K. Dransfield, C. Baillie, and Y.-W. Mai, “Improving the delamination
resistance of CFRP by stitching—a review,” Composites Science and
Technology, vol. 50, pp. 305–317, Jan. 1994.
[10] G. Stegschuster, K. Pingkarawat, B. Wendland, and A. Mouritz,
“Experimental determination of the mode i delamination fracture and
fatigue properties of thin 3d woven composites,” Composites Part A:
Applied Science and Manufacturing, vol. 84, pp. 308–315, May. 2016.
[11] A. Mouritz, M. Bannister, P. Falzon, and K. Leong, “Review of
applications for advanced three-dimensional fibre textile composites,”
Composites Part A: Applied Science and Manufacturing, vol. 30,
pp. 1445–1461, Dec. 1999.
[12] A. Mouritz and B. Cox, “A mechanistic interpretation of the comparative
in-plane mechanical properties of 3d woven, stitched and pinned
composites,” Composites Part A: Applied Science and Manufacturing,
vol. 41, pp. 709–728, Jun. 2010.
[13] P. Robinson and D. Song, “A modified DCB specimen for mode i testing
of multidirectional laminates,” Journal of Composite Materials, vol. 26,
pp. 1554–1577, Nov. 1992.
[14] C. C. Poe, H. B. Dexter, and I. S. Raju, “Review of the NASA textile
composites research,” Journal of Aircraft, vol. 36, pp. 876–884, Sep.
1999.
[15] J. Levy, “Delamination resistance of inter-woven composite plies
produced through automated fibre placement,” tech. rep., UNSW
Sydney, Feb. 2017.
[16] Park Electrochemical Corp., “E-752-LT CFRP Prepreg Material
Datasheet,” Feb. 2015.
[17] “ASTM D5528-13 Test Method for Mode I Interlaminar Fracture
Toughness of Unidirectional Fiber-Reinforced Polymer Matrix
Composites,” standard, ASTM International, West Conshohocken, PA,
Nov. 2013.