The Influence of Reaction Parameters on Magnetic Properties of Synthesized Strontium Ferrite
The conventional ceramic route was utilized to
prepare a hard magnetic powder (M-type strontium ferrite,
SrFe12O19). The stoichiometric mixture of iron oxide and strontium
carbonate were calcined at 1000oC and then fired at various
temperatures. The influence of various reaction parameters such as
mixing ratio, calcination temperature, firing temperature and firing
time on the magnetic behaviors of the synthesized magnetic powder
were investigated. The magnetic properties including Coercivity
(Hc), Magnetic saturation (Ms), and Magnetic remnance (Mr) were
measured by vibrating sample magnetometer. Morphologically the
produced magnetic powder has a dense hexagonal grain shape
structure.
[1] Global Industry Analysts, Inc. Report
http://www.prnewswire.com/news-releases/global-market-for-magneticmaterials-
to-reach-33-billion-by-2018-developing-countries-to-drivehigh-
performance-alloys-metal-finishing-chemicals-to-reach-85-bn-
177729081.html.
[2] Global Industry Analysts, Inc. Report.
http://www.prweb.com/releases/magnetic/materials/prweb4688474.htm
[3] Oliver Gutfl eisch, Matthew A. Willard , Ekkes Brück, Christina H.
Chen, S. G. Sankar, and J. Ping Liu, Adv. Mater., vol. 23 (2011) 821–
842.
[4] US Magnetic Materials Association,
http://www.usmagnetmaterials.com/documents/usmma-presentationgeneral-
5-08.ppt, (accessed September 2010).
[5] Yang Luo , Proc. 20 th Int. Workshop on Rare Earth Permanent Magnets
And Their Applications, (Ed: D. Niarchos), 2008, 27.
[6] R. Valenzuela, Magnetic Ceramics, Cambridge University Press, New
York, 1994.
[7] K.H.J. Buschow, F.R. De Boer, Physics of Magnetism and Magnetic
Materials, Kluwer Academic, Plenum Publishers, London, 2003.
[8] A. Rafferty, T. Prescott, D. Brabazon, Sintering behaviour of cobalt
ferrite ceramic, Ceramics International 34 (2008) 15–21.
[9] Sukhleen Bindra Narang and I. S. Hudiara, Journal of Ceramic
Processing Research, vol. 7, No. 2, (2006) 113-116.
[10] J.F. Wang, C.B. Ponton, I.R. Harris, J. Magn. Magn. Mater. 298 (2006)
122.
[11] A. Collomb, B. Lambert Andron, J.X. Boucherle, D. Samaras, Phys.
Stat. sol. (A) 96 (1986) 385.
[12] A. Ataie and S. Heshmati Manesh, J. Eur. Ceram. Soc., vol. 21 (2001)
1951.
[13] D. H. Chen and Y. Y. Chen, Mater. Res. Bull., vol. 37 (2002) 801.
[14] Z.F. Zi a,b,c, Y.P. Sun a,b,_, X.B. Zhu a,b, Z.R. Yang a,b, J.M. dai a,b,
W.H. Song, Journal of Magnetism and Magnetic Materials 320 (2008)
2746– 2751.
[15] J.M.D. Coey, J. Alloys Compd. 326 (2001) 2.
[16] P.E. Kazin, L.A. Trusov, D.D. Zaitsev, Yu.D. Tretyakov, M. Jansen, J.
Magn. Magn. Mater. 320 (2008) 1068.
[17] A. Morisako, T. Naka, K. Ito, A. Takizawa, M. Matsumoto, K.Y. Hong,
J. Magn. Magn. Mater. 242 (2002) 304.
[18] Muhammad Javed Iqbal, Muhammad Naeem Ashiq, Pablo Hernandez-
Gomez, Jose Maria Munoz, J. Magn. Magn. Mater. 320 (2008) 881
[19] Y. Wu, Z.W. Li, L. Chen, S.J. Wang, C.K. Ong, J. Appl. Phys. 95 (2004)
8.
[20] P.C.A. Brito, R.F. Gomes, J.G.S. Duqueb, M.A. Mace do, Physica B 384
(2006) 91.
[21] Ali Ghasemi, Akimitsu Morisako, J. Magn. Magn. Mater. 320 (2008)
1167.
[22] H. How, X. Zuo, C.V. Wave, IEEE Trans. Magn. 41 (2005) 2349.
[23] Z.B. Guo, W.P. Ding, W. Zhong, J.R. Zang, Y.W. Do, J. Magn. Magn.
Mater. 175 (1997) 333.
[24] W.A. Kaczmarek, B. Idzikowski, K.H. Muller, J. Magn. Magn. Mater.
177 (1998) 921.
[25] S.V. Ketov, Yu.D. Yagodkin, A.L. Lebed, Yu.V. Chernopyatova, K.
Khlopkov, J. Magn. Magn. Mater. 300 (2006) e479.
[26] L. Qiao, L.H. You, J.W. Zheng, L.Q. Jiang, J.W. Sheng, J. Magn. Magn.
Mater. 318 (2007) 74.
[27] V.V. Pankov,M. Pernet, P. Germi, P. Mollard, J.Magn.Magn.Mater. 120
(1993) 69.
[28] Wandee Onreabroy a,*, Komane Papato a, Gobwute Rujijanagul b,
Kamonpan Pengpat b, Tawee Tunkasiri b, Ceramics International 38S
(2012) S415–S419.
[1] Global Industry Analysts, Inc. Report
http://www.prnewswire.com/news-releases/global-market-for-magneticmaterials-
to-reach-33-billion-by-2018-developing-countries-to-drivehigh-
performance-alloys-metal-finishing-chemicals-to-reach-85-bn-
177729081.html.
[2] Global Industry Analysts, Inc. Report.
http://www.prweb.com/releases/magnetic/materials/prweb4688474.htm
[3] Oliver Gutfl eisch, Matthew A. Willard , Ekkes Brück, Christina H.
Chen, S. G. Sankar, and J. Ping Liu, Adv. Mater., vol. 23 (2011) 821–
842.
[4] US Magnetic Materials Association,
http://www.usmagnetmaterials.com/documents/usmma-presentationgeneral-
5-08.ppt, (accessed September 2010).
[5] Yang Luo , Proc. 20 th Int. Workshop on Rare Earth Permanent Magnets
And Their Applications, (Ed: D. Niarchos), 2008, 27.
[6] R. Valenzuela, Magnetic Ceramics, Cambridge University Press, New
York, 1994.
[7] K.H.J. Buschow, F.R. De Boer, Physics of Magnetism and Magnetic
Materials, Kluwer Academic, Plenum Publishers, London, 2003.
[8] A. Rafferty, T. Prescott, D. Brabazon, Sintering behaviour of cobalt
ferrite ceramic, Ceramics International 34 (2008) 15–21.
[9] Sukhleen Bindra Narang and I. S. Hudiara, Journal of Ceramic
Processing Research, vol. 7, No. 2, (2006) 113-116.
[10] J.F. Wang, C.B. Ponton, I.R. Harris, J. Magn. Magn. Mater. 298 (2006)
122.
[11] A. Collomb, B. Lambert Andron, J.X. Boucherle, D. Samaras, Phys.
Stat. sol. (A) 96 (1986) 385.
[12] A. Ataie and S. Heshmati Manesh, J. Eur. Ceram. Soc., vol. 21 (2001)
1951.
[13] D. H. Chen and Y. Y. Chen, Mater. Res. Bull., vol. 37 (2002) 801.
[14] Z.F. Zi a,b,c, Y.P. Sun a,b,_, X.B. Zhu a,b, Z.R. Yang a,b, J.M. dai a,b,
W.H. Song, Journal of Magnetism and Magnetic Materials 320 (2008)
2746– 2751.
[15] J.M.D. Coey, J. Alloys Compd. 326 (2001) 2.
[16] P.E. Kazin, L.A. Trusov, D.D. Zaitsev, Yu.D. Tretyakov, M. Jansen, J.
Magn. Magn. Mater. 320 (2008) 1068.
[17] A. Morisako, T. Naka, K. Ito, A. Takizawa, M. Matsumoto, K.Y. Hong,
J. Magn. Magn. Mater. 242 (2002) 304.
[18] Muhammad Javed Iqbal, Muhammad Naeem Ashiq, Pablo Hernandez-
Gomez, Jose Maria Munoz, J. Magn. Magn. Mater. 320 (2008) 881
[19] Y. Wu, Z.W. Li, L. Chen, S.J. Wang, C.K. Ong, J. Appl. Phys. 95 (2004)
8.
[20] P.C.A. Brito, R.F. Gomes, J.G.S. Duqueb, M.A. Mace do, Physica B 384
(2006) 91.
[21] Ali Ghasemi, Akimitsu Morisako, J. Magn. Magn. Mater. 320 (2008)
1167.
[22] H. How, X. Zuo, C.V. Wave, IEEE Trans. Magn. 41 (2005) 2349.
[23] Z.B. Guo, W.P. Ding, W. Zhong, J.R. Zang, Y.W. Do, J. Magn. Magn.
Mater. 175 (1997) 333.
[24] W.A. Kaczmarek, B. Idzikowski, K.H. Muller, J. Magn. Magn. Mater.
177 (1998) 921.
[25] S.V. Ketov, Yu.D. Yagodkin, A.L. Lebed, Yu.V. Chernopyatova, K.
Khlopkov, J. Magn. Magn. Mater. 300 (2006) e479.
[26] L. Qiao, L.H. You, J.W. Zheng, L.Q. Jiang, J.W. Sheng, J. Magn. Magn.
Mater. 318 (2007) 74.
[27] V.V. Pankov,M. Pernet, P. Germi, P. Mollard, J.Magn.Magn.Mater. 120
(1993) 69.
[28] Wandee Onreabroy a,*, Komane Papato a, Gobwute Rujijanagul b,
Kamonpan Pengpat b, Tawee Tunkasiri b, Ceramics International 38S
(2012) S415–S419.
@article{"International Journal of Chemical, Materials and Biomolecular Sciences:70997", author = "M. Bahgat and F. M. Awan and H. A. Hanafy", title = "The Influence of Reaction Parameters on Magnetic Properties of Synthesized Strontium Ferrite", abstract = "The conventional ceramic route was utilized to
prepare a hard magnetic powder (M-type strontium ferrite,
SrFe12O19). The stoichiometric mixture of iron oxide and strontium
carbonate were calcined at 1000oC and then fired at various
temperatures. The influence of various reaction parameters such as
mixing ratio, calcination temperature, firing temperature and firing
time on the magnetic behaviors of the synthesized magnetic powder
were investigated. The magnetic properties including Coercivity
(Hc), Magnetic saturation (Ms), and Magnetic remnance (Mr) were
measured by vibrating sample magnetometer. Morphologically the
produced magnetic powder has a dense hexagonal grain shape
structure.", keywords = "Hard magnetic materials, ceramic route, strontium
ferrite, magnetic properties.", volume = "9", number = "8", pages = "1043-5", }