Abstract: Thermal insulation materials based on natural fibers
represent a very promising area of materials based on natural easy
renewable row sources. These materials may be in terms of the
properties of most competing synthetic insulations, but show
somewhat higher moisture sensitivity and thermal insulation
properties are strongly influenced by the density and orientation of
fibers. The paper described the problem of hygrothermal behavior of
thermal insulation materials based on natural plant and animal fibers.
This is especially the dependence of the thermal properties of these
materials on the type of fiber, bulk density, temperature, moisture and
the fiber orientation.
Abstract: In this study, the Mo-electrode thin films were deposited using two-stepped process and the high purity copper indium selenide-based powder (CuInSe2, CIS) was fabricated by using hydrothermal process by Nanowin Technology Co. Ltd. Because the CIS powder was aggregated into microscale particles, the CIS power was ground into nano-scale particles. 6 wt% CIS particles were mixed and dispersed into isopropyl alcohol (IPA). A new non-vacuum thin-film deposition process, spray coating method (SPM), was investigated to deposit the high-densified CIS absorber layers. 0.1 ml CIS solution was sprayed on the 20 mm×10 mm Mo/glass substrates and then the CuInSe2 thin films were annealed in a selenization furnace using N2 as atmosphere. The annealing temperature and time were set at 550oC and 5 min, and 0.0g~0.6g extra Se content was added in the furnace. The influences of extra Se content on the densification, crystallization, resistivity (ρ), hall mobility (μ), and carrier concentration of the CIS absorber layers were well investigated in this study.
Abstract: This work details the generation of thin films of
structured zeolite catalysts (ZSM–5 and Y) onto the surface of a
metal substrate (FeCrAlloy) using in-situ hydrothermal synthesis. In
addition, the zeolite Y is post-synthetically modified by acidified
ammonium ion exchange to generate US-Y. Finally the catalytic
activity of the structured ZSM-5 catalyst films (Si/Al = 11, thickness
146 0m) and structured US–Y catalyst film (Si/Al = 8, thickness
230m) were compared with the pelleted powder form of ZSM–5 and
USY catalysts of similar Si/Al ratios.
The structured catalyst films have been characterised using a range
of techniques, including X-ray diffraction (XRD), Electron
microscopy (SEM), Energy Dispersive X–ray analysis (EDX) and
Thermogravimetric Analysis (TGA). The transition from oxide-onalloy
wires to hydrothermally synthesised uniformly zeolite coated
surfaces was followed using SEM and XRD. In addition, the
robustness of the prepared coating was confirmed by subjecting these
to thermal cycling (ambient to 550oC).
The cracking of n–heptane over the pellets and structured catalysts
for both ZSM–5 and Y zeolite showed very similar product
selectivities for similar amounts of catalyst with an apparent
activation energy of around 60 kJ mol-1. This paper demonstrates that
structured catalysts can be manufactured with excellent zeolite
adherence and when suitably activated/modified give comparable
cracking results to the pelleted powder forms. These structured
catalysts will improve temperature distribution in highly exothermic
and endothermic catalysed processes.
Abstract: The Salman Farsi dam project is constructed on the Ghareh Agahaj River about 140km south of Shiraz city in the Zagros Mountains of southwestern Iran. This tectonic province of south-western Iran is characterized by a simple folded sedimentary sequence. The dam foundation rocks compose of the Asmari Formation of Oligo-miocene and generally comprise of a variety of karstified carbonate rocks varying from strong to weak rocks. Most of the rocks exposed at the dam site show a primary porosity due to incomplete diagenetic recrystallization and compaction. In addition to these primary dispositions to weathering, layering conditions (frequency and orientation of bedding) and the subvertical tectonic discontinuities channeled preferably the infiltrating by deep-sited hydrothermal solutions. Consequently the porosity results to be enlarged by dissolution and the rocks are expected to be karstified and to develop cavities in correspondence of bedding, major joint planes and fault zones. This kind of karsts is named hypogenic karsts which associated to the ascendant warm solutions. Field observations indicate strong karstification and vuggy intercalations especially in the middle part of the Asmari succession. The biggest karst in the dam axis which identified by speleological investigations is Golshany Cave with volume of about 150,000 m3. The tendency of the Asmari limestone for strong dissolution can alert about the seepage from the reservoir and area of the dam locality.
Abstract: In this research, copper borates are synthesized by the
reaction of copper sulfate pentahydrate (CuSO4.5H2O) and
tincalconite (Na2O4B7.10H2O). The experimental parameters are
selected as 80oC reaction temperature and 60 of reaction time. The
effect of mole ratio of CuSO4.5H2O to Na2O4B7.5H2O is studied. For
the identification analyses X-Ray Diffraction (XRD) and Fourier
Transform Infrared Spectroscopy (FT-IR) techniques are used. At the
end of the experiments, synthesized copper borate is matched with
the powder diffraction file of “00-001-0472” [Cu(BO2)2] and
characteristic vibrations between B and O atoms are seen. The proper
crystals are obtained at the mole ratio of 3:1. This study showed that
simplified synthesis process is suitable for the production of copper
borate minerals.
Abstract: The coal utilization in thermal power plants in Malaysia has increased significantly which produces an enormous amount of coal combustion by-product (CCBP) or coal ash and poses severe disposal problem. As each coal ash is distinct, this study presents the geochemistry of the coal ash, in particular fly ash, produced from the combustion of local coal from Kuching Sarawak, Malaysia. The geochemical composition of the ash showed a high amount of silica, alumina, iron oxides and alkalies which was found to be a convenient starting material for the hydrothermal synthesis of zeolites with the higher Na2O percentage being a positive factor for its alkaline activation; while the mineral phases are mainly quartz, mullite, calcium oxide, silica, and iron oxide hydrate. The geochemical changes upon alkali activation that can be predicted in a similar type of ash have been described in this paper. The result shows that this particular ash has a good potential for a high value industrial product like zeolites upon alkali activation.
Abstract: Magnesium borate(MB) istechnical ceramic for high heat-resisting, corrosion-resisting, super mechanical strength, superinsulation, light weight, high strength, and high coefficient of elasticity. Zinc borate (ZB) can be used as multi-functional synergistic additives with flame retardant additives in polymers. The most important properties are low solubility in water and high dehydration temperature. ZB dehydrates above 290°C and anhydrous ZB has thermal resistance about 400°C. In this study, the raw materials of ZnO, MgO and H3BO3 were used with mole ratio of 1:1:9. With the starting materials hydrothermal method was applied at a temperature of 100oC. The reaction time was determined as 30, 60, 90 and 120 minutes after some preliminary experiments. After the synthesis, the crystal structure and the morphology of the products were examined by X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR). As a result, the forms of Zinc Oxide Borate Hydrate [Zn3B6O12.3.5H2O], Admontite [MgO(B2O3)3.7(H2O)] and Mcallisterite [Mg2(B6O7(OH)6)2.9(H2O)] were synthesized.
Abstract: Pure phase gallosilicate nitrite sodalite has been synthesized in a single step by low temperature (373 oK) hydrothermal technique. The product obtained was characterized using a combination of techniques including X-ray powder diffraction, IR, Raman spectroscopy, SEM, MAS NMR spectroscopy as well as thermogravimetry. Sodalite with an ideal composition was obtained after synthesis at 3730K and seven days duration using alkaline medium. The structural features of the Na8[GaSiO4]6(NO2)2 sodalite were investigated by IR, MAS NMR spectroscopy of 29Si and 23Na nuclei and by Reitveld refinement of X-ray powder diffraction data. The crystal structure of this sodalite has been refined in the space group P 4 3n; with a cell parameter 8.98386Å, V= 726.9 Å, (Rwp= 0.077 and Rp=0.0537) and Si-O-Ga angle is found to be 132.920 . MAS NMR study confirms complete ordering of Si and Ga in the gallosilicate framework. The surface area of single entity with stoichiometry Na8[GaSiO4]6(NO2)2 was found to be 8.083 x10-15 cm2/g.
Abstract: Magnesium wastes are produced by many industrial activities. This waste problem is becoming a future problem for the world. Magnesium borates have many advantages such as; high corrosion resistance, heat resistance, high coefficient of elasticity and can also be used in the production of material against radiation. Addition, magnesium borates have great potential in sectors
including ceramic and detergents industry and superconducting materials.
In this study, using the starting materials of waste magnesium and H3BO3 the hydrothermal method was applied at a moderate
temperature of 70oC. Several mole ratios of waste magnesium to H3BO3 are selected as; 1:2, 1:4, 1:6, 1:8, 1:10. Reaction time was determined as 1 hour. After the synthesis, X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) techniques are applied to products. As a result the forms of mcallisterite “Mg2(B6O7(OH)6)2.9(H2O)”, admontite “MgO(B2O3)3.7(H2O)” and magnesium boron hydrate (MgO(B2O3)3.6(H2O)” are obtained.
Abstract: Structured catalysts formed from the growth of
zeolites on substrates is an area of increasing interest due to the
increased efficiency of the catalytic process, and the ability to
provide superior heat transfer and thermal conductivity for both
exothermic and endothermic processes.
However, the generation of structured catalysts represents a
significant challenge when balancing the relationship variables
between materials properties and catalytic performance, with the
Na2O, H2O and Al2O3 gel composition paying a significant role in
this dynamic, thereby affecting the both the type and range of
application.
The structured catalyst films generated as part of this
investigation have been characterised using a range of techniques,
including X-ray diffraction (XRD), Electron microscopy (SEM),
Energy Dispersive X-ray analysis (EDX) and Thermogravimetric
Analysis (TGA), with the transition from oxide-on-alloy wires to
hydrothermally synthesised uniformly zeolite coated surfaces being
demonstrated using both SEM and XRD. The robustness of the
coatings has been ascertained by subjecting these to thermal cycling
(ambient to 550oC), with the results indicating that the synthesis time
and gel compositions have a crucial effect on the quality of zeolite
growth on the FeCrAlloy wires.
Finally, the activity of the structured catalyst was verified by a
series of comparison experiments with standard zeolite Y catalysts in
powdered pelleted forms.
Abstract: The hydrothermal behavior of a bed consisting of
magnetic and shale oil particle admixtures under the effect of a
transverse magnetic field is investigated. The phase diagram, bed
void fraction are studied under wide range of the operating
conditions i.e., gas velocity, magnetic field intensity and fraction of
the magnetic particles. It is found that the range of the stabilized
regime is reduced as the magnetic fraction decreases. In addition, the
bed voidage at the onset of fluidization decreases as the magnetic
fraction decreases. On the other hand, Nusselt number and
consequently the heat transfer coefficient is found to increase as the
magnetic fraction decreases. An empirical equation is investigated to
relate the effect of the gas velocity, magnetic field intensity and
fraction of the magnetic particles on the heat transfer behavior in the
bed.
Abstract: Pyritisation halos are identified in weathering crusts and unconsolidated formations at five locations within large fault structure of the Urals’ eastern slope. Electron microscopy reveals the presence of inclusions and growths on pyrite faces – normally on cubic pyrite with striations, or combinations of cubes and other forms. Following neogenesis types are established: native elements and intermetallic compounds (including gold and silver), halogenides, sulphides, sulfosalts, tellurides, sulphotellurides,
selenides, tungstates, sulphates, phosphates, carbon-based substances. Direct relationship is noted between amount and diversity of such mineral phases, and proximity to and scale of ore-grade mineralization. Gold and silver, both in native form and within tellurides, presence of lead (galena, native lead), native tungsten, and, possibly, molybdenite and sulfosalts can indicate gold-bearing formations. First find of native tungsten in the Urals is for the first time – in crystallised and druse-like form. Link is suggested between unusual mineralization and “reducing” hydrothermal fluids from deep-seated faults at later stages of Urals’ reactivation.
Abstract: In this paper presents the mathematical model of
hydrothermal processes in thermal power plant with different wind
direction scenarios in the water reservoir, which is solved by the
Navier - Stokes and temperature equations for an incompressible
fluid in a stratified medium. Numerical algorithm based on the
method of splitting by physical parameters. Three dimensional
Poisson equation is solved with Fourier method by combination of
tridiagonal matrix method (Thomas algorithm).
Abstract: Waste problem is becoming a future problem all over the world. Magnesium wastes which can be used in recycling processes are produced by many industrial activities. Magnesium borates which have useful properties such as; high heat resistance, corrosion resistance, supermechanical strength, superinsulation, light weight, high coefficient of elasticity and so on. Addition, magnesium borates have great potential in the development of ceramic and detergents industry, whisker-reinforced composites, antiwear, and reducing friction additives.
In this study, using the starting materials of waste magnesium and H3BO3 the hydrothermal method was applied at a moderate temperature of 70oC with different reaction times. Several reaction times of waste magnesium to H3BO3 were selected as; 30, 60, 120, 240 minutes. After the synthesis, X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) techniques were applied to products. As a result, the forms of Admontite [MgO(B2O3)3.7(H2O)] and Mcallisterite [Mg2(B6O7(OH)6)2.9(H2O)] were synthesized.
Abstract: Platinum oxide nanoparticles were prepared by a
simple hydrothermal route and chemical reduction using
carbohydrates (Fructose and sucrose) as the reducing and
stabilizing agents. The crystallite size of these nanoparticles was
evaluated from X-ray diffraction (XRD), atomic force microscopy
(AFM) and transmission electron microscopy (TEM) and was
found to be 10 nm as shown in figure 1, which is the
demonstration of EM bright field and transmission electron
microscopy. The effect of carbohydrates on the morphology of the
nanoparticles was studied using TEM (Figure 1). The
nanoparticles (100 μg/ml) were administered to the Pseudomonas
Stutzeri and Lactobacillus cultures and the incubation was done at
35 oC for 24 hours. The nanocomposites exhibited interesting
inhibitory as well as bactericidal activity against P. Stutzeri and
and Lactobacillus species. Incorporation of nanoparticles also
increased the thermal stability of the carbohydrates.
Abstract: Titanium oxide films with different morphologies have for the first time been fabricated through hydrothermal reactions between a titanium substrate and iodine powder in water or ethanol. SEM revealed that iodine supported titanium (Ti-I2) surface shows different morphologies with variable treatment conditions. The mean surface roughness (Ra) was increased in the different groups. Use of surfactant has a role to increase the roughness of the film. The surface roughness was in the range of 0.15 μm-0.42 μm. Furthermore, the electrochemical examinations showed that the Ti-I2 surface fabricated in alcoholic medium has high corrosion resistance than in aqueous medium.
Abstract: TiO2 nanoparticles were synthesized by hydrothermal
method at 180°C from TiOSO4 aqueous solution with1m/l
concentration. The obtained products were coated with silica by
means of a seeded polymerization technique for a coating time of
1440 minutes to obtain well defined TiO2@SiO2 core-shell structure.
The uncoated and coated nanoparticles were characterized by using
X-Ray diffraction technique (XRD), Fourier Transform Infrared
Spectroscopy (FT-IR) to study their physico-chemical properties.
Evidence from XRD and FTIR results show that SiO2 is
homogenously coated on the surface of titania particles. FTIR spectra
show that there exists an interaction between TiO2 and SiO2 and
results in the formation of Ti-O-Si chemical bonds at the interface of
TiO2 particles and SiO2 coating layer. The non linear optical limiting
properties of TiO2 and TiO2@SiO2 nanoparticles dispersed in
ethylene glycol were studied at 532nm using 5ns Nd:YAG laser
pulses. Three-photon absorption is responsible for optical limiting
characteristics in these nanoparticles and it is seen that the optical
nonlinearity is enhanced in core-shell structures when compared with
single counterparts. This effective three-photon type absorption at
this wavelength, is of potential application in fabricating optical
limiting devices.
Abstract: This paper presents an efficient emission constrained
hydrothermal scheduling algorithm that deals with nonlinear
functions such as the water discharge characteristics, thermal cost,
and transmission loss. It is then incorporated into the hydrothermal
coordination program. The program has been tested on a practical
utility system having 32 thermal and 12 hydro generating units. Test
results show that a slight increase in production cost causes a
substantial reduction in emission.
Abstract: The Mahin area is a part of Tarom- Hashtjin zone that
located in west of Qazvin province in northwest of Iran. Many copper
and base metals ore deposits are hosted by this zone. High potential
localities identification in this area is very necessary. The objective of
this research, is finding hydrothermal alteration zones by remote
sensing methods and best processing technique of Advanced
Spaceborne Thermal Emission and Reflection Radiometer (ASTER)
data. Different methods such as band ratio, Principal Component
Analysis (PCA), Minimum Noise Fraction (MNF) and Least Square
Fit (LS-Fit) were used for mapping hydrothermal alteration zones.
Abstract: A new SUZ-4 zeolite membrane with
tetraethlyammonium hydroxide as the template was fabricated on
mullite tube via hydrothermal sol-gel synthesis in a rotating
autoclave reactor. The suitable synthesis condition was SiO2:Al2O3
ratio of 21.2 for 4 days at 155 °C crystallization under autogenous
pressure. The obtained SUZ-4 possessed a high BET surface area of
396.4 m2/g, total pore volume at 2.611 cm3/g, and narrow pore size
distribution with 97 nm mean diameter and 760 nm long of needle
crystal shape. The SUZ-4 layer obtained from seeding crystallization
was thicker than that of without seeds or in situ crystallization.