Abstract: Active carbon can be obtained from agricultural sources. Due to the high surface area, the production of activated carbon from cheap resources is very important. Since the surface area of 1 g activated carbon is approximately between 300 and 2000 m2, it can be used to remove both organic and inorganic impurities. In this study, the adsorption of Zn metal was studied with the product of activated carbon, which is obtained from pomegranate peel by microwave and chemical activation methods. The microwave process of pomegranate peel was carried out under constant microwave power of 800 W and 1 to 4 minutes. After the microwave process, samples were treated with H2SO4 for 3 h. Then prepared product was used in synthetic waste water including 40 ppm Zn metal. As a result, removal of waste Zn in waste water ranged from 91% to 93%.
Abstract: Coffee is a widely consumed beverage with many components such as caffeine, flavonoids, phenolic compounds, and minerals. Coffee consumption continues to increase due to its physiological effects, its pleasant taste, and aroma. Robusta and Arabica are two basic types of coffee beans. The coffee bean used for Turkish coffee is Arabica. There are many elements in the structure of coffee and have various effect on human health such as Sodium (Na), Boron (B), Magnesium (Mg) and Iron (Fe). In this study, the amounts of Mg, Na, Fe, and B contents in Turkish coffee are determined and effect of sugar addition is investigated for conscious consumption. The analysis of the contents of coffees was determined by using inductively coupled plasma optical emission spectrometry (ICP-OES). From the results of the experiments the Mg, Na, Fe and B contents of Turkish coffee after sugar addition were found as 19.83, 1.04, 0.02, 0.21 ppm, while without using sugar these concentrations were found 21.46, 0.81, 0.008 and 0.16 ppm. In addition, element contents were calculated for 1, 3 and 5 cups of coffee in order to investigate the health effects.
Abstract: Flue gas desulfurization gypsum (FGD) is a waste
material arouse from coal power plants. Hydroxyapatite (HAP) is a
biomaterial with porous structure. In this study, FGD gypsum which
retrieved from coal power plant in Turkey was characterized and
HAP particles which can be used as an adsorbent in wastewater
treatment application were synthesized from the FGD gypsum. The
raw materials are characterized by using X Ray Diffraction (XRD)
and Fourier transform infrared spectroscopy (FT-IR) techniques and
produced HAP are characterized by using XRD. As a result, HAP
particles were synthesized at the molar ratio of 5:10, 5:15, 5:20, 5:24,
at room temperature, in alkaline medium (pH=11) and in 1 hour-reaction
time. Among these conditions, 5:20 had the best result.
Abstract: Zinc borates are used as a multi-functional flame
retardant additive for its high dehydration temperature. In this study,
the method of ultrasonic mixing was used in the synthesis of zinc
borates. The reactants of zinc oxide (ZnO) and boric acid (H3BO3)
were used at the constant reaction parameters of 90°C reaction
temperature and 55 min of reaction time. Several molar ratios of
ZnO:H3BO3 (1:1, 1:2, 1:3, 1:4 and 1:5) were conducted for the
determination of the optimum reaction ratio. Prior to synthesis the
characterization of the synthesized zinc borates were made by X-Ray
Diffraction (XRD) and Fourier Transform Infrared Spectroscopy
(FT-IR). From the results Zinc Oxide Borate Hydrate
[Zn3B6O12.3.5H2O], were synthesized optimum at the molar ratio of
1:3, with a reaction efficiency of 95.2%.
Abstract: Zinc borate is an important inorganic hydrate borate
material, which can be used as a flame retardant agent and corrosion
resistance material. This compound can loss its structural water
content at higher than 290°C. Due to thermal stability; Zinc Borate
can be used as flame retardant at high temperature process of plastic
and gum. In this study, the ultrasonic reaction of zinc borates were
studied using hydrozincite (Zn5(CO3)2·(OH)6) and boric acid
(H3BO3) raw materials. Before the synthesis raw materials were
characterized by X-Ray Diffraction (XRD) and Fourier Transform
Infrared Spectroscopy (FT-IR). Ultrasonic method is a new
application on the zinc borate synthesis. The synthesis parameters
were set to 90°C reaction temperature and 55 minutes of reaction
time, with 1:1, 1:2, 1:3, 1:4 and 1:5 molar ratio of starting materials
(Zn5(CO3)2·(OH)6 : H3BO3). After the zinc borate synthesis, the
products were analyzed by XRD and FT-IR. As a result, optimum
molar ratio of 1:5 is determined for the synthesis of zinc borates with
ultrasonic method.
Abstract: Potassium borates, which are widely used in welding
and metal refining industry, as a lubricating oil additive, cement
additive, fiberglass additive and insulation compound, are one of the
important groups of borate minerals. In this study the production of a
potassium borate mineral via hydrothermal method is aimed. The
potassium source of potassium nitrate (KNO3) was used along with a
sodium source of sodium hydroxide (NaOH) and boron source of
boric acid (H3BO3). The constant parameters of reaction temperature
and reaction time were determined as 80°C and 1 h, respectively. The
molar ratios of 1:1:3 (as KNO3:NaOH:H3BO3), 1:1:4, 1:1:5, 1:1:6
and 1:1:7 were used. Following the synthesis the identifications of
the produced products were conducted by X-Ray Diffraction (XRD),
Fourier Transform Infrared Spectroscopy (FT-IR) and Raman
Spectroscopy. The results of the experiments and analysis showed in
the ratio of 1:1:6, the Santite mineral with powder diffraction file
number (pdf no.) of 01-072-1688, which is known as potassium
pentaborate (KB5O8·4H2O) was synthesized as best.
Abstract: Fruit juices play important roles in human health as
being a key part of nutrition. Juice and nectar are two categories of
drinks with so many variations for consumers, regardless of age,
lifestyle and taste preferences, which they can find their favorites.
Juices contain 100% pulp when pulp content of ‘nectar’ changes
between 25%-50%. In this study, potassium (K), magnesium (Mg),
and phosphorus (P) contents in orange juice and nectar is determined
for conscious consumption. For this purpose inductively coupled
plasma optical emission spectrometry (ICP-OES) is used to find out
potassium (K), magnesium (Mg), and phosphorus (P) contents in
orange juices and nectar. Furthermore, the daily intake of elements
from orange juice and nectar that affects human health is also
investigated. From the results of experiments K, Mg and P contents
are found in orange juice as 1351; 73,25; 89,27 ppm and in orange
nectar as 986; 33,76; 51,30 respectively.
Abstract: Activated carbon is an amorphous carbon chain which
has extremely extended surface area. High surface area of activated
carbon is due to the porous structure. Activated carbon, using a
variety of materials such as coal and cellulosic materials; can be
obtained by both physical and chemical methods. The prepared
activated carbon can be used for decolorize, deodorize and also can
be used for removal of organic and non-organic pollution. In this
study, pomegranate peel was subjected to 800W microwave power
for 1 to 4 minutes. Also fresh pomegranate peel was used for the
reference material. Then ZnCl2 was used for the chemical activation
purpose. After the activation process, activated pomegranate peels
were used for the adsorption of Zn metal (40 ppm) in the waste water.
As a result of the adsorption experiments, removal of heavy metals
ranged from 89% to 85%.
Abstract: Boron-gypsum is a waste which occurs in the boric
acid production process. In this study, the boron content of this waste
is evaluated for the use in synthesis of magnesium borates and such
evaluation of this kind of waste is useful more than storage or
disposal. Magnesium borates, which are a sub-class of boron
minerals, are useful additive materials for the industries due to their
remarkable thermal and mechanical properties. Magnesium borates
were obtained hydrothermally at different temperatures. Novelty of
this study is the search of the solution density effects to magnesium
borate synthesis process for the increasing the possibility of borongypsum
usage as a raw material. After the synthesis process, products
are subjected to XRD and FT-IR to identify and characterize their
crystal structure, respectively.
Abstract: Fly ash is an important waste, produced in thermal
power plants which causes very important environmental pollutions.
For this reason the usage and evaluation the fly ash in various areas
are very important. Nearly, 15 million tons/year of fly ash is
produced in Turkey. In this study, usage of fly ash with diatomite and
molasses for heavy metal (Cd) adsorption from wastewater is
investigated. The samples of Seyitomer region fly ash were analyzed
by X-ray fluorescence (XRF) and Scanning Electron Microscope
(SEM) then diatomite (0 and 1% in terms of fly ash, w/w) and
molasses (0-0.75 mL) were pelletized under 30 MPa of pressure for
the usage of cadmium (Cd) adsorption in wastewater. After the
adsorption process, samples of Seyitomer were analyzed using
Optical Emission Spectroscopy (ICP-OES). As a result, it is seen that
the usage of Seyitomer fly ash is proper for cadmium (Cd) adsorption
and an optimum adsorption yield with 52% is found at a compound
with Seyitomer fly ash (10 g), diatomite (0.5 g) and molasses (0.75
mL) at 2.5 h of reaction time, pH:4, 20ºC of reaction temperature and
300 rpm of stirring rate.
Abstract: In this research, it is aimed not only microwave synthesis of magnesium borates but also evaluation of magnesium wastes. Synthesis process can be described with the reaction of Mg wastes and boric acid using microwave energy. X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) were applied to synthesized minerals. According to XRD results, magnesium borate hydrate mixtures were obtained as mcallisterite (pdf# = 01-070-1902, Mg2(B6O7(OH)6)2.9(H2O)) at higher crystallinity properties was achieved at the mole ratio raw material 1:1. Also, other kinds of magnesium borate hydrates were obtained at lower crystallinity such as admontite (pdf # = 01-076-0540, MgO(B2O3)3.7(H2O)), inderite (pdf # = 01-072-2308, 2MgO.3B2O3.15(H2O)) and magnesium borate hydrates (pdf # = 01-076-0539, MgO(B2O3)3.6(H2O)). FT-IR spectrums indicated that minor changes were seen at the band values of characteristic stretching in each experiment. At the end of experiments it is seen that using microwave energy may contribute positive effects to design of synthesis process such as reducing reaction time and products at higher crystallinity.
Abstract: Zinc borate is an important boron compound that can be used as multi-functional flame retardant additive due to its high dehydration temperature property. In this study, theraw materials of ZnSO4.7H2O, NaOH and H3BO3werecharacterized by X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) and used in the synthesis of zinc borates.The synthesis parameters were set to 100°C reaction temperature and 120 minutes of reaction time, with different molar ratio of starting materials (ZnSO4.7H2O:NaOH:H3BO3). After the zinc borate synthesis, the identifications of the products were conducted by XRD and FT-IR. As a result,Zinc Oxide Borate Hydrate [Zn3B6O12.3.5H2O], were synthesized at the molar ratios of 1:1:3, 1:1:4, 1:2:5 and 1:2:6. Among these ratios 1:2:6 had the best results.
Abstract: Tea is one of the most consumed beverages all over the world. Especially, black and green teas are preferred to consume. In Turkey, some local tea houses use sodium bicarbonate (SB) to obtain more infusion by using less than the amount of tea. Therefore, the addition of SB to black and green teas affects element concentrations of these teas. In this study, determination of magnesium (Mg) and phosphorus (P) contents in black and green teas aimed for conscious consumption, after the addition of SB. Inductively coupled plasma optical emission spectrometry (ICP-OES) was used for these analysis. The results of this study showed that the concentrations of Mg and P decreased by adding SB from 11.020, 21.915 to 10.009, 17.520 in black tea and from 12.605, 14.550 to 8.118, 9.425 in green tea, respectively. The addition of SB on analyzed teas is not recommended to cause reducing intake percentages of Mg and P from the essential elements.
Abstract: Due to their strong mechanical and thermal properties magnesium borates have a wide usage area such as ceramic industry, detergent production, friction reducing additive and grease production. In this study, microwave synthesis of magnesium borates from MgCl2.6H2O (Magnesium chloride hexahydrate), MgO (Magnesium oxide) and H3BO3 (Boric acid) for different reaction times is researched. X-ray Diffraction (XRD) and Fourier Transform Infrared (FT-IR) Spectroscopy are used to find out how the reaction time sways on the products. The superficial properties are investigated with Scanning Electron Microscopy (SEM). According to XRD analysis, the synthesized compounds are 00-041-1407 pdf coded Shabinite (Mg5(BO3)4Cl2(OH)5.4(H2O)) and 01-073-2158 pdf coded Karlite (Mg7(BO3)3(OH,Cl)5).
Abstract: In this research, copper borates are synthesized by the
reaction of copper sulfate pentahydrate (CuSO4.5H2O) and
tincalconite (Na2O4B7.10H2O). The experimental parameters are
selected as 80oC reaction temperature and 60 of reaction time. The
effect of mole ratio of CuSO4.5H2O to Na2O4B7.5H2O is studied. For
the identification analyses X-Ray Diffraction (XRD) and Fourier
Transform Infrared Spectroscopy (FT-IR) techniques are used. At the
end of the experiments, synthesized copper borate is matched with
the powder diffraction file of “00-001-0472” [Cu(BO2)2] and
characteristic vibrations between B and O atoms are seen. The proper
crystals are obtained at the mole ratio of 3:1. This study showed that
simplified synthesis process is suitable for the production of copper
borate minerals.
Abstract: Magnesium borate(MB) istechnical ceramic for high heat-resisting, corrosion-resisting, super mechanical strength, superinsulation, light weight, high strength, and high coefficient of elasticity. Zinc borate (ZB) can be used as multi-functional synergistic additives with flame retardant additives in polymers. The most important properties are low solubility in water and high dehydration temperature. ZB dehydrates above 290°C and anhydrous ZB has thermal resistance about 400°C. In this study, the raw materials of ZnO, MgO and H3BO3 were used with mole ratio of 1:1:9. With the starting materials hydrothermal method was applied at a temperature of 100oC. The reaction time was determined as 30, 60, 90 and 120 minutes after some preliminary experiments. After the synthesis, the crystal structure and the morphology of the products were examined by X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR). As a result, the forms of Zinc Oxide Borate Hydrate [Zn3B6O12.3.5H2O], Admontite [MgO(B2O3)3.7(H2O)] and Mcallisterite [Mg2(B6O7(OH)6)2.9(H2O)] were synthesized.
Abstract: Fly ash is a waste material of coal firing thermal
plants that is released from thermal power plants. It was defined as
very fine particles that are drifted upward which are taken up by the
flue gases. The emerging amount of fly ash in the world is
approximately 600 million tons per year. In our country, it is
expected that will be occurred 50 million tons of waste ash per year
until 2020. The fly ashes can be evaluated by using as adsorbent
material. The purpose of this study is to investigate the possibility of
use of various fly ashes (Tuncbilek, Catalagzi, Orhaneli) like lowcost
adsorbents for heavy metal adsorption. First of all, fly ashes
were characterized. For this purpose; analyses such as XRD, XRF,
SEM and FT-IR were performed.
Abstract: Dehydration behavior gives a hint about thermal properties of materials. It is important for the usage areas and transportation of minerals. Magnesium borates can be used as additive materials in areas such as in the production of superconducting materials, in the composition of detergents, due to the content of boron in the friction-reducing additives in oils and insulating coating compositions due to their good mechanic and thermal properties.
In this study, thermal dehydration behavior of admontite (MgO(B2O3)3.7(H2O)), which is a kind of magnesium borate mineral, is experimented by microwave energy at 360W. Structure of admontite is suitable for the investigation of dehydration behavior by microwave because of its seven moles of crystal water. It is seen that admontite lost its 28.7% of weight at the end of the 120 minutes heating in microwave furnace.
Abstract: Magnesium wastes are produced by many industrial activities. This waste problem is becoming a future problem for the world. Magnesium borates have many advantages such as; high corrosion resistance, heat resistance, high coefficient of elasticity and can also be used in the production of material against radiation. Addition, magnesium borates have great potential in sectors
including ceramic and detergents industry and superconducting materials.
In this study, using the starting materials of waste magnesium and H3BO3 the hydrothermal method was applied at a moderate
temperature of 70oC. Several mole ratios of waste magnesium to H3BO3 are selected as; 1:2, 1:4, 1:6, 1:8, 1:10. Reaction time was determined as 1 hour. After the synthesis, X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) techniques are applied to products. As a result the forms of mcallisterite “Mg2(B6O7(OH)6)2.9(H2O)”, admontite “MgO(B2O3)3.7(H2O)” and magnesium boron hydrate (MgO(B2O3)3.6(H2O)” are obtained.
Abstract: Waste problem is becoming a future problem all over the world. Magnesium wastes which can be used in recycling processes are produced by many industrial activities. Magnesium borates which have useful properties such as; high heat resistance, corrosion resistance, supermechanical strength, superinsulation, light weight, high coefficient of elasticity and so on. Addition, magnesium borates have great potential in the development of ceramic and detergents industry, whisker-reinforced composites, antiwear, and reducing friction additives.
In this study, using the starting materials of waste magnesium and H3BO3 the hydrothermal method was applied at a moderate temperature of 70oC with different reaction times. Several reaction times of waste magnesium to H3BO3 were selected as; 30, 60, 120, 240 minutes. After the synthesis, X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) techniques were applied to products. As a result, the forms of Admontite [MgO(B2O3)3.7(H2O)] and Mcallisterite [Mg2(B6O7(OH)6)2.9(H2O)] were synthesized.