Abstract: ZnO nanostructures including nanowires, nanorods,
and nanoneedles were successfully deposited on GaAs substrates,
respectively, by simple two-step chemical method for the first time. A
ZnO seed layer was firstly pre-coated on the O2-plasma treated
substrate by sol-gel process, followed by the nucleation of ZnO
nanostructures through hydrothermal synthesis. Nanostructures with
different average diameter (15-250 nm), length (0.9-1.8 μm), density
(0.9-16×109 cm-2) were obtained via adjusting the growth time and
concentration of precursors. From the reflectivity spectra, we
concluded ordered and taper nanostructures were preferential for
photovoltaic applications. ZnO nanoneedles with an average diameter
of 106 nm, a moderate length of 2.4 μm, and the density of 7.2×109
cm-2 could be synthesized in the concentration of 0.04 M for 18 h.
Integrated with the nanoneedle array, the power conversion efficiency
of single junction solar cell was increased from 7.3 to 12.2%,
corresponding to a 67% improvement.
Abstract: This paper presents an efficient emission constrained
economic dispatch algorithm that deals with nonlinear cost function
and constraints. It is then incorporated into the dynamic
programming based hydrothermal coordination program. The
program has been tested on a practical utility system having 32
thermal and 12 hydro generating units. Test results show that a slight
increase in production cost causes a substantial reduction in
emission.
Abstract: A study concerning the photocatalytic decolourization
of Congo red (CR) dye, over artificial UV irradiation is presented.
Photocatalysts based on a commercial titanium dioxide (TiO2)
modified with transition metals (Ni, Cu and Zn) were used. The
dopage method used was wet impregnation. A TiO2 sample without
salt was subjected to the same hydrothermal treatment to be used as
reference. Congo red solutions to several pH conditions (natural and
basic) were used to evaluate photocatalytic performance of each
doped catalysts. Photodecolourization percentage was measured
spectrofotrometically after 3 h of treatment to 499 nm as response
variable. Kinetics investigations of photodegradation indicated that
reactions obey to Langmuir-Hinshelwood model and pseudo–first
order law. The rate constant studies of photocatalytic decolourization
reactions for Zn–TiO2 and Cu–TiO2 photocatalysts indicated that in
all cases the rate constant of the reaction was higher than that of TiO2
undoped. These results show that nature of the metal modifying the
TiO2 influence on the efficiency of the photocatalyst evaluated in
process. Ni does not present an additional effect compared with TiO2,
while Zn enhances the photoactivity due to its electronic properties.
Abstract: Cassava bagasse is one of major biomass wastes in Thailand from starch processing industry, which contains high starch content of about 60%. The object of this study was to investigate the optimal condition for hydrothermally pretreating cassava baggasses with or without acid addition. The pretreated samples were measured reducing sugar yield directly or after enzymatic hydrolysis (alpha-amylase). In enzymatic hydrolysis, the highest reducing sugar content was obtained under hydrothermal conditions for at 125oC for 30 min. The result shows that pretreating cassava baggasses increased the efficiency of enzymatic hydrolysis. For acid hydrolysis, pretreating cassava baggasses with sulfuric acid at 120oC for 60 min gave a maximum reducing sugar yield. In this study, sulfuric acid had a greater capacity for hydrolyzing cassava baggasses than phosphoric acid. In comparison, dilute acid hydrolysis to provide a higher yield of reducing sugar than the enzymatic hydrolysis combined hydrothermal pretreatment. However, enzymatic hydrolysis in a combination with hydrothermal pretreatment was an alternative to enhance efficiency reducing sugar production from cassava bagasse.
Abstract: This paper deals with the tuning of parameters for Automatic Generation Control (AGC). A two area interconnected hydrothermal system with PI controller is considered. Genetic Algorithm (GA) and Particle Swarm optimization (PSO) algorithms have been applied to optimize the controller parameters. Two objective functions namely Integral Square Error (ISE) and Integral of Time-multiplied Absolute value of the Error (ITAE) are considered for optimization. The effectiveness of an objective function is considered based on the variation in tie line power and change in frequency in both the areas. MATLAB/SIMULINK was used as a simulation tool. Simulation results reveal that ITAE is a better objective function than ISE. Performances of optimization algorithms are also compared and it was found that genetic algorithm gives better results than particle swarm optimization algorithm for the problems of AGC.
Abstract: There are many kinds of metal borates found not only
in nature but also synthesized in the laboratory such as magnesium
borates. Due to its excellent properties, as remarkable ceramic
materials, they have also application areas in anti-wear and friction
reducing additives as well as electro-conductive treating agents. The
synthesis of magnesium borate powders can be fulfilled simply with
two different methods, hydrothermal and thermal synthesis.
Microwave assisted method, also another way of producing
magnesium borate, can be classified into thermal synthesis because of
using the principles of solid state synthesis. It also contributes
producing particles with small size and high purity in nano-size
material synthesize. In this study the production of magnesium
borates, are aimed using MgCl2.6H2O and H3BO3. The identification
of both starting materials and products were made by the equipments
of, X-Ray Diffraction (XRD) and Fourier Transform Infrared
Spectroscopy (FT-IR). After several synthesis steps magnesium
borates were synthesized and characterized by XRD and FT-IR, as
well.
Abstract: Turkey has 72 % of total world boron reserves on the
basis of B2O3.Borates that is a refined form of boron minerals have a
wide range of applications. Zinc borates can be used as multifunctional
synergistic additives. The most important properties are
low solubility in water and high dehydration temperature. Zinc
borates dehydrate above 290°C and anhydrous zinc borate has
thermal resistance about 400°C. Zinc borates can be synthesized
using several methods such as hydrothermal and solid-state
processes. In this study, the solid-state method was applied between
500 and 800°C using the starting materials of ZnO and H3BO3 with
1:4 mole ratio. The reaction time was determined as 4 hours after
some preliminary experiments. After the synthesis, the crystal
structure and the morphology of the products were examined by XRay
Diffraction (XRD), Fourier Transform Infrared Spectroscopy
(FT-IR) and Raman Spectrometer. As a result the form of ZnB4O7
was synthesized with the highest crystal score at 800°C.
Abstract: Hydrothermally synthesized high silica borosilicates
with the MFI structure was subjected to several characterization
techniques. The effect of boron on the structure and acidity of
HZSM-5 catalyst were studied by XRD, SEM, N2 adsorption, solid
state NMR, NH3-TPD. It was confirmed that boron had entered the
framework in the boron samples. The results also revealed that strong
acidity was weakened and weak acidity was strengthened by the
boron added zeolite framework compared with parent catalyst. The
catalytic performance was carried out in a fixed bed at 460°C for
methanol to propylene (MTP) reaction. The results of MTP reaction
showed a great increment of the propylene selectivity and excellent
stability for the B-HZSM-5. The catalyst exhibited about 81%
selectivity to C2
= - C4
= olefins with 40% selectivity of propylene as
major component at near 100% methanol conversion, and the stable
performance in the studied period was 100h.
Abstract: Borate minerals have attracted considerable attention in the past years due to their structural chemistry and mechanical properties in several industries. Recently, increasing attention has been paid to the use of; synthetically produced magnesium borates as catalysts reinforcing material for plastics, the conversion of hydrocarbons, electro-conductive treating agent, anti-wear and anti-corrosion materials. Magnesium borates can be synthesized by several methods such as; hydrothermal and solid-state (thermal) processes. In this study the hydrothermal production method was applied at the modest temperature of 80C along with convenient crystal growth. Using MgCl2.6H2O, H3BO3, and NaOH as starting materials, 30, 60, 120, 240 minutes of reaction times were studied. After all, the crystal structure and the morphology of the products were examined by X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR). As a result the forms of Admontite and Mcallisterite minerals were synthesized.
Abstract: Zinc borates can be used as multi-functional
synergistic additives with flame retardant additives in polymers. Zinc
borate is white, non-hygroscopic and powder type product. The most
important properties are low solubility in water and high dehydration
temperature. Zinc borates dehydrate above 290°C and anhydrous zinc
borate has thermal resistance about 400°C. Zinc borates can be
synthesized using several methods such as hydrothermal and solidstate
processes. In this study, the solid-state method was applied at
low temperatures of 600oC and 700oC using the starting materials of
ZnO and H3BO3 with several mole ratios. The reaction time was
determined as 4 hours after some preliminary experiments. After the
synthesis, the crystal structure and the morphology of the products
were examined by X-Ray Diffraction (XRD) and Fourier Transform
Infrared Spectroscopy (FT-IR). As a result the forms of ZnB4O7,
Zn3(BO3)2, ZnB2O4 were synthesized and obtained along with the
unreacted ZnO.
Abstract: In this work Artificial Intelligence (AI) techniques like Fuzzy logic, Genetic Algorithms and Particle Swarm Optimization have been used to improve the performance of the Automatic Generation Control (AGC) system. Instead of applying Genetic Algorithms and Particle swarm optimization independently for optimizing the parameters of the conventional AGC with PI controller, an intelligent tuned Fuzzy logic controller (acting as the secondary controller in the AGC system) has been designed. The controller gives an improved dynamic performance for both hydrothermal and thermal-thermal power systems under a variety of operating conditions.
Abstract: Magnesium wastes and scraps, one of the metal wastes, are produced by many industrial activities, all over the world. Their growing size is becoming a future problem for the world. In this study, the use of magnesium wastes as a raw material in the production of the magnesium borate hydrates are aimed. The method used in the experiments is hydrothermal synthesis. The conditions are set to, waste magnesium to B2O3, 1:3 as a molar ratio. Four different reaction times are studied which are 30, 60, 120 and 240 minutes. For the identification analyses X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FT-IR) and Raman spectroscopy techniques are used. As a result at all the reaction times magnesium borate hydrates are synthesized and the most crystalline forms are obtained at a reaction time of 120 minutes. The overall yields of the production are found between the values of 65-80 %.
Abstract: Composite of Celatom-ZeoliteY (Cel-ZY) was used to
remove cobalt ion from an aqueous solution using batch mode.
ZeoliteY has successfully superimposed on Celatom FW-14 surface
using hydrothermal treatment .The product was synthesized as a
novel of hierarchical porous material. It was observed from the
results that Cel-ZY has higher ability to remove cobalt ions than the
pure ZeoliteY powder (PZY) synthesized under the same conditions.
Several parameters were studied in this project to investigate the
effect of removal cobalt ion such as pH and initial cobalt
concentration. It was clearly observed that the uptake of cobalt ions
was affected with increase these parameters. The results proved that
the product can be used effectively to remove Co2+ ions from
wastewater as an environmentally friendly alternative.
Abstract: The paper reports the preparation and photocatalytic
activity of ZnO/SnO2 and SnO2 nanoparticles. These nanoparticles
were synthesized by hydrothermal method. The products were
characterized by X-ray diffraction (XRD) and scanning electron
microscopy (SEM). Their grain sizes are about 50-100 nm. The
photocatalytic activities of these materials were investigated for
congo red removal from aqueous solution under UV light irradiation.
It was shown that the use of ZnO/SnO2 as photocatalyst have better
photocatalytic activity for degradation of congo red than SnO2 or
TiO2 (anatase, particle size: 30nm) alone.
Abstract: Several optimization algorithms specifically applied to
the problem of Operation Planning of Hydrothermal Power Systems
have been developed and are used. Although providing solutions to
various problems encountered, these algorithms have some
weaknesses, difficulties in convergence, simplification of the original
formulation of the problem, or owing to the complexity of the
objective function. Thus, this paper presents the development of a
computational tool for solving optimization problem identified and to
provide the User an easy handling. Adopted as intelligent
optimization technique, Genetic Algorithms and programming
language Java. First made the modeling of the chromosomes, then
implemented the function assessment of the problem and the
operators involved, and finally the drafting of the graphical interfaces
for access to the User. The program has managed to relate a coherent
performance in problem resolution without the need for
simplification of the calculations together with the ease of
manipulating the parameters of simulation and visualization of output
results.