Abstract: Fly ash is an important waste, produced in thermal
power plants which causes very important environmental pollutions.
For this reason the usage and evaluation the fly ash in various areas
are very important. Nearly, 15 million tons/year of fly ash is
produced in Turkey. In this study, usage of fly ash with diatomite and
molasses for heavy metal (Cd) adsorption from wastewater is
investigated. The samples of Seyitomer region fly ash were analyzed
by X-ray fluorescence (XRF) and Scanning Electron Microscope
(SEM) then diatomite (0 and 1% in terms of fly ash, w/w) and
molasses (0-0.75 mL) were pelletized under 30 MPa of pressure for
the usage of cadmium (Cd) adsorption in wastewater. After the
adsorption process, samples of Seyitomer were analyzed using
Optical Emission Spectroscopy (ICP-OES). As a result, it is seen that
the usage of Seyitomer fly ash is proper for cadmium (Cd) adsorption
and an optimum adsorption yield with 52% is found at a compound
with Seyitomer fly ash (10 g), diatomite (0.5 g) and molasses (0.75
mL) at 2.5 h of reaction time, pH:4, 20ºC of reaction temperature and
300 rpm of stirring rate.
Abstract: Magnesium borate(MB) istechnical ceramic for high heat-resisting, corrosion-resisting, super mechanical strength, superinsulation, light weight, high strength, and high coefficient of elasticity. Zinc borate (ZB) can be used as multi-functional synergistic additives with flame retardant additives in polymers. The most important properties are low solubility in water and high dehydration temperature. ZB dehydrates above 290°C and anhydrous ZB has thermal resistance about 400°C. In this study, the raw materials of ZnO, MgO and H3BO3 were used with mole ratio of 1:1:9. With the starting materials hydrothermal method was applied at a temperature of 100oC. The reaction time was determined as 30, 60, 90 and 120 minutes after some preliminary experiments. After the synthesis, the crystal structure and the morphology of the products were examined by X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR). As a result, the forms of Zinc Oxide Borate Hydrate [Zn3B6O12.3.5H2O], Admontite [MgO(B2O3)3.7(H2O)] and Mcallisterite [Mg2(B6O7(OH)6)2.9(H2O)] were synthesized.
Abstract: Fly ash is a waste material of coal firing thermal
plants that is released from thermal power plants. It was defined as
very fine particles that are drifted upward which are taken up by the
flue gases. The emerging amount of fly ash in the world is
approximately 600 million tons per year. In our country, it is
expected that will be occurred 50 million tons of waste ash per year
until 2020. The fly ashes can be evaluated by using as adsorbent
material. The purpose of this study is to investigate the possibility of
use of various fly ashes (Tuncbilek, Catalagzi, Orhaneli) like lowcost
adsorbents for heavy metal adsorption. First of all, fly ashes
were characterized. For this purpose; analyses such as XRD, XRF,
SEM and FT-IR were performed.
Abstract: Fly ash is one of the residues generated in
combustion, and comprises the fine particles that rise with the flue
gases. Ash which does not rise is termed bottom ash [1]. In our
country, it is expected that will be occurred 50 million tons of waste
ash per year until 2020. Released waste from the thermal power
plants is caused very significant problems as known. The fly ashes
can be evaluated by using as adsorbent material.
The purpose of this study is to investigate the possibility of use of
Tuncbilek fly ash like low-cost adsorbents for heavy metal
adsorption. First of all, Tuncbilek fly ash was characterized. For this
purpose; analysis such as sieve analysis, XRD, XRF, SEM and FT-IR
were performed.
Abstract: Turkey has 72 % of total world boron reserves on the
basis of B2O3.Borates that is a refined form of boron minerals have a
wide range of applications. Zinc borates can be used as multifunctional
synergistic additives. The most important properties are
low solubility in water and high dehydration temperature. Zinc
borates dehydrate above 290°C and anhydrous zinc borate has
thermal resistance about 400°C. Zinc borates can be synthesized
using several methods such as hydrothermal and solid-state
processes. In this study, the solid-state method was applied between
500 and 800°C using the starting materials of ZnO and H3BO3 with
1:4 mole ratio. The reaction time was determined as 4 hours after
some preliminary experiments. After the synthesis, the crystal
structure and the morphology of the products were examined by XRay
Diffraction (XRD), Fourier Transform Infrared Spectroscopy
(FT-IR) and Raman Spectrometer. As a result the form of ZnB4O7
was synthesized with the highest crystal score at 800°C.
Abstract: Zinc borates can be used as multi-functional
synergistic additives with flame retardant additives in polymers. Zinc
borate is white, non-hygroscopic and powder type product. The most
important properties are low solubility in water and high dehydration
temperature. Zinc borates dehydrate above 290°C and anhydrous zinc
borate has thermal resistance about 400°C. Zinc borates can be
synthesized using several methods such as hydrothermal and solidstate
processes. In this study, the solid-state method was applied at
low temperatures of 600oC and 700oC using the starting materials of
ZnO and H3BO3 with several mole ratios. The reaction time was
determined as 4 hours after some preliminary experiments. After the
synthesis, the crystal structure and the morphology of the products
were examined by X-Ray Diffraction (XRD) and Fourier Transform
Infrared Spectroscopy (FT-IR). As a result the forms of ZnB4O7,
Zn3(BO3)2, ZnB2O4 were synthesized and obtained along with the
unreacted ZnO.