Abstract: Heteropoly acid nanoparticles anchored on graphene oxide based on UiO-66 were synthesized via in-situ growth hydrothermal method and tested for photodegradation of a tetracycline as critical pollutant. Results showed that presence of graphene oxide and UiO-66 with high specific surface area, great electron mobility and various functional groups make an excellent support for heteropoly acid and improve photocatalytic efficiency up to 95% for tetracycline. Furthermore, total organic carbon (TOC) analysis verified 79% mineralization of this pollutant under optimum condition.
Abstract: The fly ash of waste incineration processes is usually hazardous and the disposal or reuse of waste incineration fly ash is difficult. In this study, the waste incineration fly ash was converted to useful zeolites by the alkali fusion and hydrothermal synthesis method. The influence of different operating conditions (the ratio of Si/Al, the ratio of hydrolysis liquid to solid, and hydrothermal time) was investigated to seek the optimum operating conditions for the synthesis of zeolite from waste incineration fly ash. The results showed that concentrations of heavy metals in the leachate of Toxicity Characteristic Leaching Procedure (TCLP) were all lower than the regulatory limits except lead. The optimum operating conditions for the synthesis of zeolite from waste incineration fly ash by the alkali fusion and hydrothermal synthesis method were Si/Al=40, NaOH/ash=1.5, alkali fusion at 400 oC for 40 min, hydrolysis with Liquid to Solid ratio (L/S)= 200 at 105 oC for 24 h, and hydrothermal synthesis at 105 oC for 24 h. The specific surface area of fly ash could be significantly increased from 8.59 m2/g to 651.51 m2/g (synthesized zeolite). The influence of different operating conditions on the synthesis of zeolite from waste incineration fly ash followed the sequence of Si/Al ratio > hydrothermal time > hydrolysis L/S ratio. The synthesized zeolites can be reused as good adsorbents to control the air or wastewater pollutants. The purpose of fly ash detoxification, reduction and waste recycling/reuse is achieved successfully.
Abstract: Biosensors are playing vital role in industrial, clinical, and chemical analysis applications. Among other techniques, ZnO based biosensor is an easy approach due to its exceptional chemical and electrical properties. ZnO nanorods have positively charged isoelectric point which helps immobilize the negative charge glucose oxides (GOx). Here, we report ZnO nanorods based biosensors for the immobilization of GOx. The ZnO nanorods were grown by hydrothermal method on indium tin oxide substrate (ITO). The fabrication of biosensors was carried through batch processing using conventional photolithography. The buffer solutions of GOx were prepared in phosphate with a pH value of around 7.3. The biosensors effectively immobilized the GOx and result was analyzed by calculation of voltage and current on nanostructures.
Abstract: A novel chromium-free protective coating films based
on a zeolite coating was growing onto a FeCrAlloy metal using in –
situ hydrothermal method. The zeolite film was obtained using in-situ
crystallization process that is capable of coating large surfaces with
complex shape and in confined spaces has been developed. The
zeolite coating offers an advantage of a high mechanical stability and
thermal stability. The physicochemical properties were investigated
using X-ray diffraction (XRD), Electron Microscopy (SEM), Energy
Dispersive X–ray Analysis (EDX) and Thermogravimetric Analysis
(TGA). The transition from oxide-on-alloy wires to hydrothermally
synthesised uniformly zeolite coated surfaces was followed using
SEM and XRD. In addition, the robustness of the prepared coating
was confirmed by subjecting these to thermal cycling (ambient to
550oC).
Abstract: Potassium borates, which are widely used in welding
and metal refining industry, as a lubricating oil additive, cement
additive, fiberglass additive and insulation compound, are one of the
important groups of borate minerals. In this study the production of a
potassium borate mineral via hydrothermal method is aimed. The
potassium source of potassium nitrate (KNO3) was used along with a
sodium source of sodium hydroxide (NaOH) and boron source of
boric acid (H3BO3). The constant parameters of reaction temperature
and reaction time were determined as 80°C and 1 h, respectively. The
molar ratios of 1:1:3 (as KNO3:NaOH:H3BO3), 1:1:4, 1:1:5, 1:1:6
and 1:1:7 were used. Following the synthesis the identifications of
the produced products were conducted by X-Ray Diffraction (XRD),
Fourier Transform Infrared Spectroscopy (FT-IR) and Raman
Spectroscopy. The results of the experiments and analysis showed in
the ratio of 1:1:6, the Santite mineral with powder diffraction file
number (pdf no.) of 01-072-1688, which is known as potassium
pentaborate (KB5O8·4H2O) was synthesized as best.
Abstract: Magnesium borate(MB) istechnical ceramic for high heat-resisting, corrosion-resisting, super mechanical strength, superinsulation, light weight, high strength, and high coefficient of elasticity. Zinc borate (ZB) can be used as multi-functional synergistic additives with flame retardant additives in polymers. The most important properties are low solubility in water and high dehydration temperature. ZB dehydrates above 290°C and anhydrous ZB has thermal resistance about 400°C. In this study, the raw materials of ZnO, MgO and H3BO3 were used with mole ratio of 1:1:9. With the starting materials hydrothermal method was applied at a temperature of 100oC. The reaction time was determined as 30, 60, 90 and 120 minutes after some preliminary experiments. After the synthesis, the crystal structure and the morphology of the products were examined by X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR). As a result, the forms of Zinc Oxide Borate Hydrate [Zn3B6O12.3.5H2O], Admontite [MgO(B2O3)3.7(H2O)] and Mcallisterite [Mg2(B6O7(OH)6)2.9(H2O)] were synthesized.
Abstract: Magnesium wastes are produced by many industrial activities. This waste problem is becoming a future problem for the world. Magnesium borates have many advantages such as; high corrosion resistance, heat resistance, high coefficient of elasticity and can also be used in the production of material against radiation. Addition, magnesium borates have great potential in sectors
including ceramic and detergents industry and superconducting materials.
In this study, using the starting materials of waste magnesium and H3BO3 the hydrothermal method was applied at a moderate
temperature of 70oC. Several mole ratios of waste magnesium to H3BO3 are selected as; 1:2, 1:4, 1:6, 1:8, 1:10. Reaction time was determined as 1 hour. After the synthesis, X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) techniques are applied to products. As a result the forms of mcallisterite “Mg2(B6O7(OH)6)2.9(H2O)”, admontite “MgO(B2O3)3.7(H2O)” and magnesium boron hydrate (MgO(B2O3)3.6(H2O)” are obtained.
Abstract: Waste problem is becoming a future problem all over the world. Magnesium wastes which can be used in recycling processes are produced by many industrial activities. Magnesium borates which have useful properties such as; high heat resistance, corrosion resistance, supermechanical strength, superinsulation, light weight, high coefficient of elasticity and so on. Addition, magnesium borates have great potential in the development of ceramic and detergents industry, whisker-reinforced composites, antiwear, and reducing friction additives.
In this study, using the starting materials of waste magnesium and H3BO3 the hydrothermal method was applied at a moderate temperature of 70oC with different reaction times. Several reaction times of waste magnesium to H3BO3 were selected as; 30, 60, 120, 240 minutes. After the synthesis, X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) techniques were applied to products. As a result, the forms of Admontite [MgO(B2O3)3.7(H2O)] and Mcallisterite [Mg2(B6O7(OH)6)2.9(H2O)] were synthesized.
Abstract: TiO2 nanoparticles were synthesized by hydrothermal
method at 180°C from TiOSO4 aqueous solution with1m/l
concentration. The obtained products were coated with silica by
means of a seeded polymerization technique for a coating time of
1440 minutes to obtain well defined TiO2@SiO2 core-shell structure.
The uncoated and coated nanoparticles were characterized by using
X-Ray diffraction technique (XRD), Fourier Transform Infrared
Spectroscopy (FT-IR) to study their physico-chemical properties.
Evidence from XRD and FTIR results show that SiO2 is
homogenously coated on the surface of titania particles. FTIR spectra
show that there exists an interaction between TiO2 and SiO2 and
results in the formation of Ti-O-Si chemical bonds at the interface of
TiO2 particles and SiO2 coating layer. The non linear optical limiting
properties of TiO2 and TiO2@SiO2 nanoparticles dispersed in
ethylene glycol were studied at 532nm using 5ns Nd:YAG laser
pulses. Three-photon absorption is responsible for optical limiting
characteristics in these nanoparticles and it is seen that the optical
nonlinearity is enhanced in core-shell structures when compared with
single counterparts. This effective three-photon type absorption at
this wavelength, is of potential application in fabricating optical
limiting devices.
Abstract: Borate minerals have attracted considerable attention in the past years due to their structural chemistry and mechanical properties in several industries. Recently, increasing attention has been paid to the use of; synthetically produced magnesium borates as catalysts reinforcing material for plastics, the conversion of hydrocarbons, electro-conductive treating agent, anti-wear and anti-corrosion materials. Magnesium borates can be synthesized by several methods such as; hydrothermal and solid-state (thermal) processes. In this study the hydrothermal production method was applied at the modest temperature of 80C along with convenient crystal growth. Using MgCl2.6H2O, H3BO3, and NaOH as starting materials, 30, 60, 120, 240 minutes of reaction times were studied. After all, the crystal structure and the morphology of the products were examined by X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR). As a result the forms of Admontite and Mcallisterite minerals were synthesized.
Abstract: The paper reports the preparation and photocatalytic
activity of ZnO/SnO2 and SnO2 nanoparticles. These nanoparticles
were synthesized by hydrothermal method. The products were
characterized by X-ray diffraction (XRD) and scanning electron
microscopy (SEM). Their grain sizes are about 50-100 nm. The
photocatalytic activities of these materials were investigated for
congo red removal from aqueous solution under UV light irradiation.
It was shown that the use of ZnO/SnO2 as photocatalyst have better
photocatalytic activity for degradation of congo red than SnO2 or
TiO2 (anatase, particle size: 30nm) alone.