Abstract: Zinc borates are used as a multi-functional flame
retardant additive for its high dehydration temperature. In this study,
the method of ultrasonic mixing was used in the synthesis of zinc
borates. The reactants of zinc oxide (ZnO) and boric acid (H3BO3)
were used at the constant reaction parameters of 90°C reaction
temperature and 55 min of reaction time. Several molar ratios of
ZnO:H3BO3 (1:1, 1:2, 1:3, 1:4 and 1:5) were conducted for the
determination of the optimum reaction ratio. Prior to synthesis the
characterization of the synthesized zinc borates were made by X-Ray
Diffraction (XRD) and Fourier Transform Infrared Spectroscopy
(FT-IR). From the results Zinc Oxide Borate Hydrate
[Zn3B6O12.3.5H2O], were synthesized optimum at the molar ratio of
1:3, with a reaction efficiency of 95.2%.
Abstract: Zinc borate is an important inorganic hydrate borate
material, which can be used as a flame retardant agent and corrosion
resistance material. This compound can loss its structural water
content at higher than 290°C. Due to thermal stability; Zinc Borate
can be used as flame retardant at high temperature process of plastic
and gum. In this study, the ultrasonic reaction of zinc borates were
studied using hydrozincite (Zn5(CO3)2·(OH)6) and boric acid
(H3BO3) raw materials. Before the synthesis raw materials were
characterized by X-Ray Diffraction (XRD) and Fourier Transform
Infrared Spectroscopy (FT-IR). Ultrasonic method is a new
application on the zinc borate synthesis. The synthesis parameters
were set to 90°C reaction temperature and 55 minutes of reaction
time, with 1:1, 1:2, 1:3, 1:4 and 1:5 molar ratio of starting materials
(Zn5(CO3)2·(OH)6 : H3BO3). After the zinc borate synthesis, the
products were analyzed by XRD and FT-IR. As a result, optimum
molar ratio of 1:5 is determined for the synthesis of zinc borates with
ultrasonic method.
Abstract: Potassium borates, which are widely used in welding
and metal refining industry, as a lubricating oil additive, cement
additive, fiberglass additive and insulation compound, are one of the
important groups of borate minerals. In this study the production of a
potassium borate mineral via hydrothermal method is aimed. The
potassium source of potassium nitrate (KNO3) was used along with a
sodium source of sodium hydroxide (NaOH) and boron source of
boric acid (H3BO3). The constant parameters of reaction temperature
and reaction time were determined as 80°C and 1 h, respectively. The
molar ratios of 1:1:3 (as KNO3:NaOH:H3BO3), 1:1:4, 1:1:5, 1:1:6
and 1:1:7 were used. Following the synthesis the identifications of
the produced products were conducted by X-Ray Diffraction (XRD),
Fourier Transform Infrared Spectroscopy (FT-IR) and Raman
Spectroscopy. The results of the experiments and analysis showed in
the ratio of 1:1:6, the Santite mineral with powder diffraction file
number (pdf no.) of 01-072-1688, which is known as potassium
pentaborate (KB5O8·4H2O) was synthesized as best.
Abstract: Activated carbon is an amorphous carbon chain which
has extremely extended surface area. High surface area of activated
carbon is due to the porous structure. Activated carbon, using a
variety of materials such as coal and cellulosic materials; can be
obtained by both physical and chemical methods. The prepared
activated carbon can be used for decolorize, deodorize and also can
be used for removal of organic and non-organic pollution. In this
study, pomegranate peel was subjected to 800W microwave power
for 1 to 4 minutes. Also fresh pomegranate peel was used for the
reference material. Then ZnCl2 was used for the chemical activation
purpose. After the activation process, activated pomegranate peels
were used for the adsorption of Zn metal (40 ppm) in the waste water.
As a result of the adsorption experiments, removal of heavy metals
ranged from 89% to 85%.