Abstract: It is well known that cemented sand is one of the best approaches for soil stabilization. In some cases, a blend of sand, cement and other pozzolan materials such as zeolite, nano-particles and fiber can be widely (commercially) available and be effectively used in soil stabilization, especially in road construction. In this research, we investigate the effects of CaO which is based on the geotechnical characteristics of zeolite composition with sandy silt soil. Zeolites have low amount of CaO in their structures, that is, varying from 3% to 10%, and by removing the cement paste, we want to investigate the effect of zeolite pozzolan without any activator on soil samples strength. In this research, experiments are concentrated on various weight percentages of zeolite in the soil to examine the effect of the zeolite on drainage shear strength and California Bearing Ratio (CBR) both with and without curing. The study also investigates their liquid limit and plastic limit behavior and makes a comparative result by using Feng's and Wroth-Wood's methods in fall cone (cone penetrometer) device; in the final the SEM images have been presented. The results show that by increasing the percentage of zeolite in without-curing samples, the fine zeolite particles increase some soil's strength, but in the curing-state we can see a relatively higher strength toward without-curing state, since the zeolites have no plastic behavior, the pozzolanic property of zeolites plays a much higher role than cementing properties. Indeed, it is better to combine zeolite particle with activator material such as cement or lime to gain better results.
Abstract: The fly ash of waste incineration processes is usually hazardous and the disposal or reuse of waste incineration fly ash is difficult. In this study, the waste incineration fly ash was converted to useful zeolites by the alkali fusion and hydrothermal synthesis method. The influence of different operating conditions (the ratio of Si/Al, the ratio of hydrolysis liquid to solid, and hydrothermal time) was investigated to seek the optimum operating conditions for the synthesis of zeolite from waste incineration fly ash. The results showed that concentrations of heavy metals in the leachate of Toxicity Characteristic Leaching Procedure (TCLP) were all lower than the regulatory limits except lead. The optimum operating conditions for the synthesis of zeolite from waste incineration fly ash by the alkali fusion and hydrothermal synthesis method were Si/Al=40, NaOH/ash=1.5, alkali fusion at 400 oC for 40 min, hydrolysis with Liquid to Solid ratio (L/S)= 200 at 105 oC for 24 h, and hydrothermal synthesis at 105 oC for 24 h. The specific surface area of fly ash could be significantly increased from 8.59 m2/g to 651.51 m2/g (synthesized zeolite). The influence of different operating conditions on the synthesis of zeolite from waste incineration fly ash followed the sequence of Si/Al ratio > hydrothermal time > hydrolysis L/S ratio. The synthesized zeolites can be reused as good adsorbents to control the air or wastewater pollutants. The purpose of fly ash detoxification, reduction and waste recycling/reuse is achieved successfully.
Abstract: This paper aims to contribute to the characterization and the understanding of fresh state, compressive strength and chloride penetration tendency of high strength self-compacting concretes (HSSCCs) where Portland cement type II is partially substituted by 10% and 15% of natural pumice and zeolite. First, five concrete mixtures with a control mixture without any pozzolan are prepared and tested in both fresh and hardened states. Then, resistance to chloride penetration for all formulation is investigated in non-steady state and steady state by measurement of chloride penetration and diffusion coefficient. In non-steady state, the correlation between initial current and chloride penetration with diffusion coefficient is studied. Moreover, the relationship between diffusion coefficient in non-steady state and electrical resistivity is determined. The concentration of free chloride ions is also measured in steady state. Finally, chloride penetration for all formulation is studied in immersion and tidal condition. The result shows that, the resistance to chloride penetration for HSSCC in immersion and tidal condition increases by incorporating pumice and zeolite. However, concrete with zeolite displays a better resistance. This paper shows that the HSSCC with 15% pumice and 10% zeolite is suitable in fresh, hardened, and durability characteristics.
Abstract: The heat island phenomenon becomes one of the environmental problems. As countermeasures in the field of road engineering, cool pavements such as water retaining pavements and solar radiation reflective pavements have been developed to reduce the surface temperature of asphalt pavements in the hot summer climate in Japan. The authors have studied on the water retaining pavements with cement–based grouting materials. The cement–based grouting materials consist of cement, ceramic waste powder, and natural zeolite. The ceramic waste powder is collected through the recycling process of electric porcelain insulators. In this study, mixing ratio between the ceramic waste powder and the natural zeolite and a type of cement for the cement–based grouting materials is investigated to measure the surface temperature of asphalt pavements in the outdoor. All of the developed cement–based grouting materials were confirmed to effectively reduce the surface temperature of the asphalt pavements. Especially, the cement–based grouting material using the ultra–rapid hardening cement with the mixing ratio of 0.7:0.3 between the ceramic waste powder and the natural zeolite reduced mostly the surface temperature by 20 °C and more.
Abstract: Constructed Wetland (CW) is a reasonable method to
treat wastewater. Current study was carried out to co-treat landfill
leachate and domestic wastewater using a CW system. Typha
domingensis was transplanted to CW, which encloses two substrate
layers of adsorbents named ZELIAC and zeolite. Response surface
methodology and central composite design were employed to
evaluate experimental data. Contact time (h) and leachate-towastewater
mixing ratio (%; v/v) were selected as independent
factors. Phenols and manganese removal were selected as dependent
responses. At optimum contact time (48.7 h) and leachate-towastewater
mixing ratio (20.0%), removal efficiencies of phenols and
manganese removal efficiencies were 90.5%, and 89.4%,
respectively.
Abstract: There are several possibilities of reducing the required
amount of cement in concrete production. Natural zeolite is one of
the raw materials which can partly substitute Portland cement. The
effort to reduce the amount of Portland cement used in concrete
production is brings both economical as well as ecological benefits.
The paper presents the properties of concrete containing natural
zeolite as an active admixture in the concrete which partly substitutes
Portland cement. The properties discussed here bring information
about the basic mechanical properties and frost resistance of concrete
containing zeolite. The properties of concretes with the admixture of
zeolite are compared with a reference concrete with no content of
zeolite. The properties of the individual concretes are observed for
360 days.
Abstract: Global temperature had increased by about 0.5oC over
the past century, increasing temperature leads to a loss or a decrease
of soil organic matter (SOM). Whereas soil organic matter in many
tropical soils is less stable than that of temperate soils, and it will be
easily affected by climate change. Therefore, conservation of soil
organic matter is urgent issue nowadays. This paper presents the
effect of different doses (5%, 15%) of Ca-type zeolite in conjunction
with organic manure, applied to soil samples from Philippines,
Paraguay and Japan, on the decomposition resistance of soil organic
matter under high temperature. Results showed that a remain or
slightly increase the C/N ratio of soil. There are an increase in
percent of humic acid (PQ) that extracted with Na4P2O7. A decrease
of percent of free humus (fH) after incubation was determined. A
larger the relative color intensity (RF) value and a lower the color
coefficient (6logK) value following increasing zeolite rates leading
to a higher degrees of humification. The increase in the aromatic
condensation of humic acid (HA) after incubation, as indicates by the
decrease of H/C and O/C ratios of HA. This finding indicates that the
use of zeolite could be beneficial with respect to SOM conservation
under global warming condition.
Abstract: A new SUZ-4 zeolite membrane with
tetraethlyammonium hydroxide as the template was fabricated on
mullite tube via hydrothermal sol-gel synthesis in a rotating
autoclave reactor. The suitable synthesis condition was SiO2:Al2O3
ratio of 21.2 for 4 days at 155 °C crystallization under autogenous
pressure. The obtained SUZ-4 possessed a high BET surface area of
396.4 m2/g, total pore volume at 2.611 cm3/g, and narrow pore size
distribution with 97 nm mean diameter and 760 nm long of needle
crystal shape. The SUZ-4 layer obtained from seeding crystallization
was thicker than that of without seeds or in situ crystallization.
Abstract: The ionizing radiation of livestock wastewater for the
removal of nitrogen and phosphorus was studied in the presence of a
natural zeolite. The feasibility of a combined process of zeolite ion
exchange and electron beam irradiation of livestock wastewater was
also investigated. The removal efficiencies of NH4
+-N, T-N and T-P
were significantly enhanced by electron beam irradiation after zeolite
ion exchange as a pre-treatment. The presence of silica zeolite
accelerated the decomposition rate of livestock wastewater in the
electron beam irradiation process. These results indicate that the
combined process of zeolite ion exchange and electron beam
irradiation has the potential for the treatment of livestock wastewater
Abstract: Low silica type X (LSX) Zeolite is one of useful
material in many manufacturing due to the advantage properties
including high surface area, stability, microporous crystalline
aluminosilicates and positive ion in an extra–framework. The LSX
was used rice husk silica source which obtained by leaching with
hydrochloric acid and calcination at 500 C. To improve the
synthesis method, the LSX was crystallizated in Teflon–lined
autoclave will expedite deceasing of the amorphous particles. The
mixed gel with composition of 5.5 Na2O : 1.65 K2O : Al2O3 : 2.2
SiO2 : 122 H2O was crystallized in different container
(Polypropylene bottom and Teflon–lined autoclave). The obtained
powder was characterized by X–ray diffraction (XRD), X–ray
fluorescence spectrometry, N2 adsorption-desorption analysis BET
surface area Scanning electron microscopy (SEM) and Fourier
transform infrared spectroscopy to justify the quality of zeolite. The
results showed the crystallized zeolite in Teflon lined autoclave has
102.8 nm of crystal size, 286 m2/g of surface area and fewer amounts
of round amorphous particles when compared with the crystallized
zeolite in Polypropylene.
Abstract: Crystallization has been used for the separation of
chloronitrobenzene or CNBs, which are isomeric substances (o-, mand
p-CNB) and important intermediates in chemical productions. Effects of feed composition on the crystallization of m- and p-CNB was first studied. The results conform to the binary phase diagram of
m- and p-CNB. After that, effects of FAU zeolites (NaX, CaX, BaX, NaY and CaY) above the eutectic composition (63.5 and 65.0 wt% m-CNB in the feed) was also investigated. The results showed that
the FAU zeolites significantly affected the precipitates, the
composition of which was shifted from being rich in m-CNB to rich
in p-CNB. Effects of the number of FAU zeolites on the precipitate composition was then studied. The results revealed that the
precipitates from the lower number of the zeolites had higher p-CNB purity than those from the higher number of zeolite.
Abstract: Sulphur dioxide is a harmful gaseous product that
needs to be minimized in the atmosphere. This research work
investigates the use of zeolite as a possible additive that can improve
the sulphur dioxide capture in wet flue gas desulphurisation
dissolution process. This work determines the effect of temperature,
solid to liquid ratio, acid concentration and stirring speed on the
leaching of zeolite using a pH stat apparatus. The atomic absorption
spectrometer was used to measure the calcium ions from the solution.
It was found that the dissolution rate of zeolite decreased with
increase in solid to liquid ratio and increases with increase in
temperature, stirring speed and acid concentration. The activation
energy for the dissolution rate of zeolite in hydrochloric acid was
found to be 9.29kJ/mol. and therefore the product layer diffusion was
the rate limiting step.
Abstract: This study deals with evaluation of influence of salinity (NaCl) onto equilibrium of Cu and Ni removal from aqueous solutions by natural sorbent – zeolite. Equilibrium data were obtained by batch experiments. The salinity of the aqueous solution was influenced by dissolving NaCl in distilled water. It was studied in the range of NaCl concentrations from 1 g.l-1 to 100g.l-1. For Cu sorption there is a significant influence of salinity. The maximum capacity of zeolite for Cu was decreasing with growing concentration of NaCl. For Ni sorption there is not so significant influence of salinity as for Cu. The maximum capacity of zeolite for Ni was slightly decreasing with growing concentration of NaCl.
Abstract: Pharmaceutical industries and effluents of sewage treatment plants are the main sources of residual pharmaceuticals in water resources. These emergent pollutants may adversely impact the biophysical environment. Pharmaceutical industries often generate wastewater that changes in characteristics and quantity depending on the used manufacturing processes. Carbamazepine (CBZ), {5Hdibenzo [b,f]azepine-5-carboxamide, (C15H12N2O)}, is a significant non-biodegradable pharmaceutical contaminant in the Jordanian pharmaceutical wastewater, which is not removed by the activated sludge processes in treatment plants. Activated carbon may potentially remove that pollutant from effluents, but the high cost involved suggests that more attention should be given to the potential use of low-cost materials in order to reduce cost and environmental contamination. Powders of Jordanian non-metallic raw materials namely, Azraq Bentonite (AB), Kaolinite (K), and Zeolite (Zeo) were activated (acid and thermal treatment) and evaluated by removing CBZ. The results of batch and column techniques experiments showed around 46% and 67% removal of CBZ respectively.
Abstract: For more than 120 years, gold mining formed the
backbone the South Africa-s economy. The consequence of mine
closure was observed in large-scale land degradation and widespread
pollution of surface water and groundwater. This paper investigates
the feasibility of using natural zeolite in removing heavy metals
contaminating the Wonderfonteinspruit Catchment Area (WCA), a
water stream with high levels of heavy metals and radionuclide
pollution. Batch experiments were conducted to study the adsorption
behavior of natural zeolite with respect to Fe2+, Mn2+, Ni2+, and Zn2+.
The data was analysed using the Langmuir and Freudlich isotherms.
Langmuir was found to correlate the adsorption of Fe2+, Mn2+, Ni2+,
and Zn2+ better, with the adsorption capacity of 11.9 mg/g, 1.2 mg/g,
1.3 mg/g, and 14.7 mg/g, respectively. Two kinetic models namely,
pseudo-first order and pseudo second order were also tested to fit the
data. Pseudo-second order equation was found to be the best fit for
the adsorption of heavy metals by natural zeolite. Zeolite
functionalization with humic acid increased its uptake ability.