Abstract: Co metal supported on SiO2 and Al2O3 catalysts with
a metal loading varied from 30 of 70 wt.% were evaluated for
decomposition of methane to COx free hydrogen and carbon
nanomaterials. The catalytic runs were carried out from 550-800oC
under atmospheric pressure using fixed bed vertical flow reactor. The
fresh and spent catalysts were characterized by BET surface area
analyzer, XRD, SEM, TEM and TG analysis. The data showed that
50% Co/Al2O3 catalyst exhibited remarkable higher activity at 800oC
with respect to H2 production compared to rest of the catalysts.
However, the catalytic activity and durability was greatly declined at
higher temperature. The main reason for the catalytic inhibition of Co
containing SiO2 catalysts is the higher reduction temperature of
Co2SiO4. TEM images illustrate that the carbon materials with
various morphologies, carbon nanofibers (CNFs), helical-shaped
CNFs and branched CNFs depending on the catalyst composition and
reaction temperature were obtained.
Abstract: Today, the pollution due to non-degradable material
such as plastics, has led to studies about the development of
environmental-friendly material. Because of biodegradability
obtained from natural sources, polylactid acid (PLA) and ijuk fiber
are interesting to modify into a composite. This material is also
expected to reduce the impact of environmental pollution. Surface
modification of ijuk fiber through alkalinization with 0.25 M NaOH
solution for 30 minutes was aimed to enhance its compatibility to
PLA, in order to improve properties of the composite such as the
mechanical properties. Alkalinization of the ijuk fibers annihilates
some surface components such as lignin, wax and hemicelloluse, so
the pore on the surface clearly appeared, decreasing of the density
and diameter of the ijuk fibers. The change of the ijuk fiber properties
leads to increase the mechanical properties of PLA composites
reinforced the ijuk fibers through strengthening of the mechanical
interlocking with the PLA matrix. An addition to enhance the
distribution of the fibers in the PLA matrix, the stirring during DCM
solvent evaporation from the mixture of the ijuk fibers and the
dissolved-PLA can reduce amount of the trapped-voids and fibers
pull-out phenomena, which can decrease the mechanical properties of
the composite.
Abstract: The composite pavement system considered in this
paper is composed of a functional surface layer, a fiber reinforced
asphalt middle layer and a fiber reinforced lean concrete base layer.
The mix design of the fiber reinforced lean concrete corresponds to the
mix composition of conventional lean concrete but reinforced by
fibers. The quasi-absence of research on the durability or long-term
performances (fatigue, creep, etc.) of such mix design stresses the
necessity to evaluate experimentally the long-term characteristics of
this layer composition. This study tests the creep characteristics as one
of the long-term characteristics of the fiber reinforced lean concrete
layer for composite pavement using a new creep device. The test
results reveal that the lean concrete mixed with fiber reinforcement
and fly ash develops smaller creep than the conventional lean
concrete. The results of the application of the CEB-FIP prediction
equation indicate that a modified creep prediction equation should be
developed to fit with the new mix design of the layer.
Abstract: In this paper 3D FEM analysis was carried out on
double lap bonded joint with composite adherents subjected to
dynamic shear. The adherents are made of Carbon/Epoxy while the
adhesive is epoxy Araldite 2031. The maximum average shear stress
and the stress homogeneity in the adhesive layer were examined.
Three fibers textures were considered: UD; 2.5D and 3D with same
volume fiber then a parametric study based on changing the thickness
and the type of fibers texture in 2.5D was accomplished. Moreover,
adherents’ dissimilarity was also investigated. It was found that the
main parameter influencing the behavior is the longitudinal stiffness
of the adherents. An increase in the adherents’ longitudinal stiffness
induces an increase in the maximum average shear stress in the
adhesive layer and an improvement in the shear stress homogeneity
within the joint. No remarkable improvement was observed for
dissimilar adherents.
Abstract: In recent years, the hair building fiber has become
popular, in other words, it is an effective method which helps people
who suffer hair loss or sparse hair since the hair building fiber is
capable to create a natural look of simulated hair rapidly. In the
markets, there are a lot of hair fiber brands that have been designed to
formulate an intense bond with hair strands and make the hair appear
more voluminous instantly. However, those products have their own
set of properties. Thus, in this report, some measurement techniques
are proposed to identify those products. Up to five different brands of
hair fiber are tested. The electrostatic and dielectric properties of the
hair fibers are macroscopically tested using design DC and high
frequency microwave techniques. Besides, the hair fibers are
microscopically analysis by magnifying the structures of the fiber
using scanning electron microscope (SEM). From the SEM photos,
the comparison of the uniformly shaped and broken rate of the hair
fibers in the different bulk samples can be observed respectively.
Abstract: In this research the effects of adding silica and
alumina nanoparticles on flow ability and compressive strength of
cementitious composites based on Portland cement were investigated.
In the first stage, the rheological behavior of different samples
containing nanosilica, nanoalumina and polypropylene, polyvinyl
alcohol and polyethylene fibers were evaluated. With increasing of
nanoparticles in fresh samples, the slump flow diameter reduced.
Fibers reduced the flow ability of the samples and viscosity
increased. With increasing of the micro silica particles to cement
ratio from 2/1 to 2/2, the slump flow diameter increased. By adding
silica and alumina nanoparticles up to 3% and 2% respectively, the
compressive strength increased and after decreased. Samples
containing silica nanoparticles and fibers had the highest compressive
strength.
Abstract: Polysulfone (PSU) is a specialty engineering polymer
having various industrial applications. PSU is especially used in
waste water treatment membranes due to its good mechanical
properties, structural and chemical stability. But it is a hydrophobic
material and therefore its surface aim to pollute easily. In order to
resolve this problem and extend the properties of membrane, PSU
surface is rendered hydrophilic by addition of the sepiolite
nanofibers. Sepiolite is one of the natural clays, which is a hydrate
magnesium silicate fiber, also one of the well known layered clays of
the montmorillonites where has several unique channels and pores
within. It has also moisture durability, strength and low price.
Sepiolite channels give great capacity of absorption and good surface
properties. In this study, nanocomposites of commercial PSU and
Sepiolite were prepared by solvent mixing method. Different organic
solvents and their mixtures were used. Rheological characteristics of
PSU-Sepiolite solvent mixtures were analyzed, the solubility of
nanocomposite content in those mixtures were studied.
Abstract: The main objective of this paper is study the influence
of carbon nano-tubes fibers and nano silica fibers on the
characteristic compressive strength and flexural strength on concrete
and cement mortar. Twelve tested specimens were tested with square
section its dimensions (4040 160) mm, divided into four groups.
The first and second group studied the effect of carbon nano-tubes
(CNTs) fibers with different percentage equal to 0.0, 0.11%, 0.22%,
and 0.33% by weight of cement and effect of nano-silica (nS) fibers
with different percentages equal to 0.0, 1.0%, 2.0%, and 3.0% by
weight of cement on the cement mortar. The third and fourth groups
studied the effect of CNTs fiber with different percentage equal to
0.0%, 0.11%, and 0.22% by weight of cement, and effect of nS fibers
with different percentages were equal to 0.0%, 1.0%, and 2.0% by
weight of cement on the concrete. The compressive strength and
flexural strength at 7, 28, and 90 days is determined. From analysis of
tested results concluded that the nano-fibers is more effective when
used with cement mortar more than used with concrete because of
increasing the surface area, decreasing the pore and the collection of
nano-fibers. And also by adding nano-fibers the improvement of
flexural strength of concrete and cement mortar is more than
improvement of compressive strength.
Abstract: In this study, composites were fabricated from oil
palm empty fruit bunch fiber and poly(lactic) acid by extrusion
followed by injection moulding. Surface of the fiber was pre-treated
by ultrasound in an alkali medium and treatment efficiency was
investigated by scanning electron microscopy (SEM) analysis and
Fourier transforms infrared spectrometer (FTIR). Effect of fiber
treatment on composite was characterized by tensile strength (TS),
tensile modulus (TM) and impact strength (IS). Furthermore,
biostrong impact modifier was incorporated into the treated fiber
composite to improve its impact properties. Mechanical testing
showed an improvement of up to 23.5% and 33.6% respectively for
TS and TM of treated fiber composite above untreated fiber
composite. On the other hand incorporation of impact modifier led to
enhancement of about 20% above the initial IS of the treated fiber
composite.
Abstract: In this paper, the electromagnetic shielding
characteristics of an up-to-date typical carbon filler material, carbon
fiber used with a metal mesh were investigated. Carbon fiber
12k-prepregs, where carbon fibers were impregnated with epoxy, were
laminated with wire meshes, vacuum bag-molded and hardened to
manufacture hybrid-type specimens, with which an electromagnetic
shield test was performed in accordance with ASTM D4935-10,
through which was known as the most excellent reproducibility is
obtainable among electromagnetic shield tests. In addition, glass fiber
prepregs whose electromagnetic shielding effect were known as
insignificant were laminated and formed with wire meshes to verify
the validity of the electromagnetic shield effect of wire meshes in
order to confirm the electromagnetic shielding effect of metal meshes
corresponding existing carbon fiber 12k-prepregs. By grafting carbon
fibers, on which studies are being actively underway in the
environmental aspects and electromagnetic shielding effect, with
hybrid-type wire meshes that were analysed through the tests, in this
study, the applicability and possibility are proposed.
Abstract: Photonic Crystal Fibers (PCFs) can be used in optical
communications as transmission lines. For this reason, the PCFs with
low confinement loss, low chromatic dispersion, and low nonlinear
effects are highly suitable transmission media. In this paper, we
introduce a new design of index-guiding nanostructured photonic
crystal fiber (IG-NPCF) with ultra-low chromatic dispersion, low
nonlinearity effects, and low confinement loss. Relatively low
dispersion is achieved in the wavelength range of 1200 to 1600nm
using the proposed design. According to the new structure of
nanostructured PCF presented in this study, the chromatic dispersion
slope is -30(ps/km.nm) and the confinement loss reaches below 10-7
dB/km. While in the wavelength range mentioned above at the same
time an effective area of more than 50.2μm2 is obtained.
Abstract: In this research, waterglass based aerogel powder was
prepared by sol–gel process and ambient pressure drying. Inspired by
limited dust releasing, aerogel powder was introduced to the PET
electrospinning solution in an attempt to create required bulk and
surface structure for the nanofibers to improve their hydrophobic and
insulation properties. The samples evaluation was carried out by
measuring density, porosity, contact angle, heat transfer, FTIR, BET,
and SEM. According to the results, porous silica aerogel powder was
fabricated with mean pore diameter of 24 nm and contact angle of
145.9º. The results indicated the usefulness of the aerogel powder
confined into nanofibers to control surface roughness for
manipulating superhydrophobic nanowebs with water contact angle
of 147º. It can be due to a multi-scale surface roughness which was
created by nanowebs structure itself and nanofibers surface
irregularity in presence of the aerogels while a layer of fluorocarbon
created low surface energy. The wettability of a solid substrate is an
important property that is controlled by both the chemical
composition and geometry of the surface. Also, a decreasing trend in
the heat transfer was observed from 22% for the nanofibers without
any aerogel powder to 8% for the nanofibers with 4% aerogel
powder. The development of thermal insulating materials has become
increasingly more important than ever in view of the fossil energy
depletion and global warming that call for more demanding energysaving
practices.
Abstract: Two types of glass fibers having different lengths
(1/16" and 1/32") were added into rigid PVC foams to enhance the
dimensional stability of extruded rigid Polyvinyl Chloride (PVC)
foam at different concentrations (0-20 phr) using a single screw
profile extruder. PVC foam-glass fiber composites (PVC-GF) were
characterized for their dimensional stability, structural, thermal, and
mechanical properties. Experimental results show that the
dimensional stability, heat resistance, and storage modulus were
enhanced without compromising the tensile and flexural strengths of
the composites. Overall, foam composites which were prepared with
longer glass fibers exhibit better mechanical and thermal properties
than those prepared with shorter glass fibers due to higher
interlocking between the fibers and the foam cells, which result in
better load distribution in the matrix.
Abstract: The main purpose of this work was verify the
influence of the accelerated carbonation in the physical and
mechanical properties of the hybrid composites, reinforced with
micro and nanofibers and composites with microfibers. The
composites were produced by the slurry vacuum dewatering method,
followed by pressing. It was produced using two formulations: 8% of
eucalyptus pulp + 1% of the nanofibrillated cellulose and 9% of
eucalyptus pulp, both were subjected to accelerated carbonation. The
results showed that the accelerated carbonation contributed to
improve the physical and mechanical properties of the hybrid
composites and of the composites reinforced with microfibers
(eucalyptus pulp).
Abstract: We model and simulate the combined effect of fiber
dispersion and frequency chirp of a directly modulated high-speed
laser diode on the figures of merit of a non-amplified 40-Gbps optical
fiber link. We consider both the return to zero (RZ) and non-return to
zero (NRZ) patterns of the pseudorandom modulation bits. The
performance of the fiber communication system is assessed by the
fiber-length limitation due to the fiber dispersion. We study the
influence of replacing standard single-mode fibers by non-zero
dispersion-shifted fibers on the maximum fiber length and evaluate
the associated power penalty. We introduce new dispersion
tolerances for 1-dB power penalty of the RZ and NRZ 40-Gbps
optical fiber links.
Abstract: Thermal insulation materials based on natural fibers
represent a very promising area of materials based on natural easy
renewable row sources. These materials may be in terms of the
properties of most competing synthetic insulations, but show
somewhat higher moisture sensitivity and thermal insulation
properties are strongly influenced by the density and orientation of
fibers. The paper described the problem of hygrothermal behavior of
thermal insulation materials based on natural plant and animal fibers.
This is especially the dependence of the thermal properties of these
materials on the type of fiber, bulk density, temperature, moisture and
the fiber orientation.
Abstract: PAN nanofibers reinforced with amine functionalized
carbon nanotubes. The effect of amine functionalization and the
effect of concentration of CNT on the conductivity and mechanical
and morphological properties of composite nanofibers were
examined. 1%CNT-NH2 loaded PAN/CNT nanofiber showed the best
mechanical properties. Conductivity increased with the incorporation
of carbon nanotubes. While an increase of concentration of CNT
increases the diameter of nanofiber, the use of functionalized CNT
results to decrease of diameter of nanofiber.
Abstract: Polymer composite nano-fibers including (1, 3 wt %)
silver nano-particles have been produced by electrospinning method.
Polyacrylonitrile/N,N-dimethylformamide (PAN/DMF) solution have
been prepared and the amount of silver nitrate have been adjusted to
PAN weight. Silver nano-particles were obtained from reduction of
silver ions into silver nano-particles by chemical reduction by
hydrazine hydroxide (N2H5OH). The different amount of silver salt
was loaded into polymer matrix to obtain polyacrylonitrile composite
nano-fiber containing silver nano-particles. The effect of the amount
of silver nano-particles on the properties of composite nano-fiber web
was investigated. Electrical conductivity, mechanical properties,
thermal properties were examined by Microtest LCR Meter 6370
(0.01 mΩ-100 MΩ), Tensile tester, Differential scanning calorimeter
DSC (Q10) and SEM respectively. Also antimicrobial efficiency test
(ASTM E2149-10) was done against to Staphylococcus aureus
bacteria. It has been seen that breaking strength, conductivity,
antimicrobial effect, enthalpy during cyclization increase by use of
silver nano-particles while the diameter of nano-fiber decreases.
Abstract: High temperature is one of the most detrimental
effects that cause important changes in concrete’s mechanical,
physical, and thermo-physical properties. As a result of these
changes, especially high strength concrete (HSC), may exhibit
damages such as cracks and spallings. To overcome this problem,
incorporating polymer fibers such as polypropylene (PP) in concrete
is a very well-known method. In this study, using RRH, as a
sustainable material, instead of PP fiber in HSC to prevent spallings
and improve physical and thermo-physical properties were
investigated. Therefore, seven HSC mixtures with 0.25 water to
binder ratio were prepared incorporating silica fume and blast furnace
slag. PP and RRH were used at 0.2-0.5% and 0.5-3% by weight of
cement, respectively. All specimens were subjected to high
temperatures (20 (control), 300, 600 and 900˚C) with a heating rate
of 2.5˚C/min and after cooling, residual physical and thermo-physical
properties were determined.
Abstract: A polypropylene hollow fiber membrane module is used for separating dissolved gases which contain dissolved oxygen from water. These dissolved gases can be used for underwater breathing. To be used for a human, the minimum amount of oxygen is essential. To increase separation of dissolved gases, much water and high surface area of hollow fibers are requested. For efficient separation system, performance of single membrane module with high surface area needs to be investigated.
In this study, we set up experimental devices for analyzing separation characteristics of dissolved gases including oxygen from water using a polypropylene hollow fiber membrane module. Separation of dissolved gases from water is investigated with variations of water flow rates. Composition of dissolved gases is also measured using GC. These results expect to be used in developing the portable separation system.