Abstract: The rheological response of blends obtained from
quaternized polysulfone and polyvinyl alcohol in N-methyl-2-
pyrrolidone as against structural peculiarity of polymers from the
blend, composition of polymer mixtures, as well as the types of
interactions were investigated. Results show that the variation of
polyvinyl alcohol composition in the studied system determines
changes of the rheological properties, suggesting that the PVA acts as
a plasticizer. Consequently, rheological behavior of complex system,
described by the nonlinear flow curve, indicates the impact of
polyvinil alcohol content to polysulfone solution, in order to facilitate
the subsequently preparation of bioactive membranes.
Abstract: Polysulfone (PSU) is a specialty engineering polymer
having various industrial applications. PSU is especially used in
waste water treatment membranes due to its good mechanical
properties, structural and chemical stability. But it is a hydrophobic
material and therefore its surface aim to pollute easily. In order to
resolve this problem and extend the properties of membrane, PSU
surface is rendered hydrophilic by addition of the sepiolite
nanofibers. Sepiolite is one of the natural clays, which is a hydrate
magnesium silicate fiber, also one of the well known layered clays of
the montmorillonites where has several unique channels and pores
within. It has also moisture durability, strength and low price.
Sepiolite channels give great capacity of absorption and good surface
properties. In this study, nanocomposites of commercial PSU and
Sepiolite were prepared by solvent mixing method. Different organic
solvents and their mixtures were used. Rheological characteristics of
PSU-Sepiolite solvent mixtures were analyzed, the solubility of
nanocomposite content in those mixtures were studied.
Abstract: The separation of dissolved gas including dissolved oxygen can be used in breathing for a human under water. When one is suddenly wrecked or meets a tsunami, one is instantly drowned and cannot breathe under water. To avoid this crisis, when we meet waves, the dissolved gas separated from water by wave is used, while air can be used to breathe when we are about to escape from water. In this thesis, we investigated the separation characteristics of dissolved gas using the pipe type of hollow fiber membrane with polypropylene and the nude type of one with polysulfone. The hollow fiber membranes with good characteristics under water are used to separate the dissolved gas. The hollow fiber membranes with good characteristics in an air are used to transfer air. The combination of membranes with good separation characteristics under water and good transferring one in an air is used to breathe instantly under water to be alive at crisis. These results showed that polypropylene represented better performance than polysulfone under both of air and water conditions.
Abstract: This paper present some preliminary work on the
preparation and physicochemical caracterization of nanocomposite
MFI-alumina structures based on alumina hollow fibres. The fibers
are manufactured by a wet spinning process. α-alumina particles were
dispersed in a solution of polysulfone in NMP. The resulting slurry is
pressed through the annular gap of a spinneret into a precipitation
bath. The resulting green fibres are sintered. The mechanical strength
of the alumina hollow fibres is determined by a three-point-bending
test while the pore size is characterized by bubble-point testing. The
bending strength is in the range of 110 MPa while the average pore
size is 450 nm for an internal diameter of 1 mm and external diameter
of 1.7 mm. To characterize the MFI membranes various techniques
were used for physicochemical characterization of MFI–ceramic
hollow fibres membranes: The nitrogen adsorption, X-ray
diffractometry, scanning electron microscopy combined with X
emission microanalysis. Scanning Electron Microscopy (SEM) and
Energy Dispersive Microanalysis by the X-ray were used to observe
the morphology of the hollow fibre membranes (thickness,
infiltration into the carrier, defects, homogeneity). No surface film,
has been obtained, as observed by SEM and EDX analysis and
confirmed by high temperature variation of N2 and CO2 gas
permeances before cation exchange. Local analysis and characterise
(SEM and EDX) and overall (by ICP elemental analysis) were
conducted on two samples exchanged to determine the quantity and
distribution of the cation of cesium on the cross section fibre of the
zeolite between the cavities.