Abstract: In rapid industrial development, the demand for
high-strength and lightweight materials have been increased. Thus,
various CFRP (Carbon Fiber Reinforced Plastics) with composite
materials are being used. The design variables of CFRP are its
lamination direction, order and thickness. Thus, the hardness and
strength of CFRP depends much on their design variables. In this
paper, the lamination direction of CFRP was used to produce a
symmetrical ply [0°/0°, -15°/+15°, -30°/+30°, -45°/+45°, -60°/+60°,
-75°/+75° and 90°/90°] and an asymmetrical ply [0°/15°, 0°/30°,
0°/45°, 0°/60° 0°/75° and 0°/90°]. The bending flexure stress of the
CFRP specimen was evaluated through a bending test. Its thermal
property was measured using an infrared camera. The symmetrical
specimen and the asymmetrical specimen were analyzed. The results
showed that the asymmetrical specimen increased the bending loads
according to the increase in the orientation angle; and from 0°, the
symmetrical specimen showed a tendency opposite the asymmetrical
tendency because the tensile force of fiber differs at the vertical
direction of its load. Also, the infrared camera showed that the thermal
property had a trend similar to that of the mechanical properties.
Abstract: The prepreg process among the CFRP (Carbon Fiber
Reinforced Plastic) forming methods is the short term of
‘Pre-impregnation’, which is widely used for aerospace composites
that require a high quality property such as a fiber-reinforced woven
fabric, in which an epoxy hardening resin is impregnated the reality.
However, that this process requires continuous researches and
developments for its commercialization because the delamination
characteristically develops between the layers when a great weight is
loaded from outside to supplement such demerit, three lamination
methods among the prepreg lamination methods of CFRP were
designed to minimize the delamination between the layers due to
external impacts. Further, the newly designed methods and the
existing lamination methods were analyzed through a mechanical
characteristic test, Interlaminar Shear Strength test. The Interlaminar
Shear Strength test result confirmed that the newly proposed three
lamination methods, i.e. the Roll, Half and Zigzag laminations,
presented more excellent strengths compared to the conventional Ply
lamination. The interlaminar shear strength in the roll method with
relatively dense fiber distribution was approximately 1.75% higher
than that in the existing ply lamination method, and in the half method,
it was approximately 0.78% higher.
Abstract: In this paper, the electromagnetic shielding
characteristics of an up-to-date typical carbon filler material, carbon
fiber used with a metal mesh were investigated. Carbon fiber
12k-prepregs, where carbon fibers were impregnated with epoxy, were
laminated with wire meshes, vacuum bag-molded and hardened to
manufacture hybrid-type specimens, with which an electromagnetic
shield test was performed in accordance with ASTM D4935-10,
through which was known as the most excellent reproducibility is
obtainable among electromagnetic shield tests. In addition, glass fiber
prepregs whose electromagnetic shielding effect were known as
insignificant were laminated and formed with wire meshes to verify
the validity of the electromagnetic shield effect of wire meshes in
order to confirm the electromagnetic shielding effect of metal meshes
corresponding existing carbon fiber 12k-prepregs. By grafting carbon
fibers, on which studies are being actively underway in the
environmental aspects and electromagnetic shielding effect, with
hybrid-type wire meshes that were analysed through the tests, in this
study, the applicability and possibility are proposed.