Abstract: PAN nanofibers reinforced with amine functionalized
carbon nanotubes. The effect of amine functionalization and the
effect of concentration of CNT on the conductivity and mechanical
and morphological properties of composite nanofibers were
examined. 1%CNT-NH2 loaded PAN/CNT nanofiber showed the best
mechanical properties. Conductivity increased with the incorporation
of carbon nanotubes. While an increase of concentration of CNT
increases the diameter of nanofiber, the use of functionalized CNT
results to decrease of diameter of nanofiber.
Abstract: Polymer composite nano-fibers including (1, 3 wt %)
silver nano-particles have been produced by electrospinning method.
Polyacrylonitrile/N,N-dimethylformamide (PAN/DMF) solution have
been prepared and the amount of silver nitrate have been adjusted to
PAN weight. Silver nano-particles were obtained from reduction of
silver ions into silver nano-particles by chemical reduction by
hydrazine hydroxide (N2H5OH). The different amount of silver salt
was loaded into polymer matrix to obtain polyacrylonitrile composite
nano-fiber containing silver nano-particles. The effect of the amount
of silver nano-particles on the properties of composite nano-fiber web
was investigated. Electrical conductivity, mechanical properties,
thermal properties were examined by Microtest LCR Meter 6370
(0.01 mΩ-100 MΩ), Tensile tester, Differential scanning calorimeter
DSC (Q10) and SEM respectively. Also antimicrobial efficiency test
(ASTM E2149-10) was done against to Staphylococcus aureus
bacteria. It has been seen that breaking strength, conductivity,
antimicrobial effect, enthalpy during cyclization increase by use of
silver nano-particles while the diameter of nano-fiber decreases.